FATIGUE BEHAVIOR OF CARBURIZED STEEL BEFORE CRACK INITIATION

Abstract

Abstract: The fatigue behavior of quenched plus tempered carburized steel before crack initiation has been observed in tension-tension fatigue tests.It was found that fatigue softening and fatigue hardening coexist in this steel.A transition region near the ease depth of the steel divides the cross section of a round speeimen into two parts:the softened part outwards and the hardened part inwards.The degree of fatigue softening in the case and fatigue hardening in the core is increased with the maximum applied cyclic stress and the number of cycles.

Key words: carburized steel, fatigue, microhardness

CHEN Tiequn Wuhan Institute of Technology,Wuhan,ChinaVERPOEST I DER UYTTERE A Katholieke Universiteit,Leuven,Belgium. FATIGUE BEHAVIOR OF CARBURIZED STEEL BEFORE CRACK INITIATION[J]. Acta Metallurgica Sinica (English Letters), 1992, 5(1): 58-61.

[1]	Wangjian Yu, Rui Hu, Guoqiang Shang, Xian Luo, Hong Wang. Correlation Mechanism Between Microstructure and Fatigue Crack Propagation Behavior of Ti-Mo-Cr-V-Nb-Al Titanium Alloys [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(6): 981-1002.
[2]	Shaolong Zhang, Wen Zhou, Feng Hu, Kaiming Wu, Serhii Yershov. Effect of Intercritical Annealing Prior to Quenching and Partitioning on Impact Abrasive Wear Properties of Medium-Manganese Steel [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(6): 1041-1056.
[3]	Yiyun Guo, Lei Wu, Yibo Shang, Chengqi Sun. Effects of Defect, Mean Stress and Lower Loading on High Cycle and Very High Cycle Fatigue Behavior of Ti-6Al-4V Alloy [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(3): 435-448.
[4]	Xue Han, Dan Zhang, Song Zhang, Mohammed R. I. Abueida, Lili Tan, Xiaopeng Lu, Qiang Wang, Huanye Liu. Fatigue and Corrosion Fatigue Properties of Mg-Zn-Zr-Nd Alloys in Glucose-Containing Simulated Body Fluids [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(9): 1533-1550.
[5]	Qiao-Sheng Xia, Dong-Peng Hua, Qing Zhou, Ye-Ran Shi, Xiang-Tao Deng, Kai-Ju Lu, Hai-Feng Wang, Xiu-Bing Liang, Zhao-Dong Wang. Atomic-Scale Insights into Damage Mechanisms of GGr15 Bearing Steel Under Cyclic Shear Fatigue [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(7): 1265-1278.
[6]	Fanchao Meng, Rui Zhang, Shuai Wang, Fengbo Sun, Run Chen, Lujun Huang, Lin Geng. Fatigue Crack Initiation and Propagation Dominated by Crystallographic Factors in TiB/near α-Ti Composite [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(5): 763-776.
[7]	Dongqiqiong Wang, Qiang Wang, Xiaowu Li, Zhefeng Zhang. Improving Fatigue Properties of 316L Stainless Steel Welded Joints by Surface Spinning Strengthening [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(5): 840-854.
[8]	Xiaoguang Li, Jiatao Liu, Qing Liu, Chunbo Zhang, Hang Liang, Lei Cui, Yongchang Liu. High-Temperature Fatigue Behavior of Inertia Friction Welded Joints of GH4065A Ni-Based Superalloy [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(11): 1935-1946.
[9]	Xiaoyuan Teng, Jianchao Pang, Feng Liu, Chenglu Zou, Xin Bai, Shouxin Li, Zhefeng Zhang. Fatigue Life Prediction of Gray Cast Iron for Cylinder Head Based on Microstructure and Machine Learning [J]. Acta Metallurgica Sinica (English Letters), 2023, 36(9): 1536-1548.
[10]	Liqi Yang, Weihai Xue, Siyang Gao, Yanfei Cao, Hongwei Liu, Deli Duan, Dianzhong Li, Shu Li. Effects of Primary Carbide Size and Type on the Sliding Wear and Rolling Contact Fatigue Properties of M50 Bearing Steel [J]. Acta Metallurgica Sinica (English Letters), 2023, 36(8): 1336-1352.
[11]	Zhenlin Wang, Beibei Wang, Zhen Zhang, Peng Xue, Yunfei Hao, Yanhua Zhao, Dingrui Ni, Guoqing Wang, Zongyi Ma. Enhanced Fatigue Properties of 2219 Al Alloy Joints via Bobbin Tool Friction Stir Welding [J]. Acta Metallurgica Sinica (English Letters), 2023, 36(4): 586-596.
[12]	Tiezhuang Han, Jing Wang, Bo Li, Shuang Li, Kaisheng Ming, Fucheng Wang, Bin Miao, Shijian Zheng. Intermediate Temperature Fatigue Induced Precipitation and Associated Corrosion in CrMnFeCoNi High Entropy Alloy [J]. Acta Metallurgica Sinica (English Letters), 2023, 36(11): 1857-1869.
[13]	Yutian Fan, Liwei Lu, Hongliang Zhao, Zhiqiang Wu, Yong Xue, Wen Wang. Effect of Deformation Temperatures on Microstructure of AQ80 Magnesium Alloy under Repeated Upsetting-Extrusion [J]. Acta Metallurgica Sinica (English Letters), 2023, 36(10): 1649-1664.
[14]	Wen-Ke Yang, Zhu-Man Song, Xue-Mei Luo, Guang-Ping Zhang. Evaluation of Tensile and Fatigue Properties of Metals Using Small Specimens [J]. Acta Metallurgica Sinica (English Letters), 2023, 36(1): 147-157.
[15]	Peng Peng, Shengyuan Li, Weiqi Chen, Yuanli Xu, Xudong Zhang, Zhikun Ma, Jiatai Wang. Phase Selection and Microhardness of Directionally Solidified AlCoCrFeNi_2.1 Eutectic High-Entropy Alloy [J]. Acta Metallurgica Sinica (English Letters), 2022, 35(8): 1281-1290.

FATIGUE BEHAVIOR OF CARBURIZED STEEL BEFORE CRACK INITIATION

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments