Tensile behavior of Sn-0.7Cu with Zn addition at various deformation temperatures

doi:10.11890/1006-7191-112-155

Abstract

Abstract: The tensile behavior of Sn-0.7Cu and Sn-0.7Cu-1Zn was compared at various deformation temperatures. Refined microstructure and γ-CuZn particles were discovered with Zn addition. The strengths of Zn-containing solder were higher than that of Sn-0.7Cu at room and subzero temperatures. With the elevation of deformation temperature, they both decreased and they were nearly the same at 80℃. The works of fracture exhibited the similar evolution law. For Sn-0.7Cu solder, the elongation after fracture was smaller and the reduction of area was bigger than those of Sn-0.7Cu-1Zn. This shows that Zn addition improved the deformation stability, which is attributed to the modification of the microstructure. Dimples in fracture surface became smaller and shallower with the decreasing temperature. Ductile fracture was discovered in all the samples.

Key words: Sn-0.7Cu, Zn, Tensile, Temperature, Strength, Ductility, Fracture

Zhongbing LUO, Jie ZHAO, Junshan ZHANG,Lai WANG. Tensile behavior of Sn-0.7Cu with Zn addition at various deformation temperatures[J]. Acta Metallurgica Sinica (English Letters), 2011, 24(2): 155-160.

[1]	Xinqi Ji, Yue Zhang, Wenhan Jin, Xin Qi. A strategy on the consistency of tensile strength of friction stir lap welding joint based on the same peak temperature [J]. Metals Advances, 2026, 40(2): 78-87.
[2]	X.L. Wang, J.Y. Li, Q.S. Mei. Recent progress in Zn matrix composites for biomedical applications [J]. Metals Advances, 2026, 39(1): 26-37.
[3]	Huihui Wang, Qianying Guo, Chong Li, Lei Cui, Yiming Huang, Yongchang Liu. Effect of Ti₂AlC Addition on the Microstructure and Mechanical Property of Additive Manufactured Inconel 718 Alloys via Laser Powder Bed Fusion [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(9): 1481-1498.
[4]	B. M. Shi, Y. T. Pang, B. H. Shan, B. B. Wang, Y. Liu, P. Xue, J. F. Zhang, Y. N. Zan, Q. Z. Wang, B. L. Xiao, Z. Y. Ma. Microstructure Evolution and Fracture Behavior of (B₄C+Al₂O₃)/Al Friction Stir Welded Joints [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(9): 1513-1526.
[5]	Qinyuan Zheng, Yi Lu, Chengwu Zheng, Peng Liu, Tian Liang, Yikun Luan, Dianzhong Li. Improving Ductility of a 3Mn Medium-Mn Steel by Manipulating the Austenite Reversion Path [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(9): 1583-1590.
[6]	Xinhao Li, Jieli Ma, Yiren Wang, Yong Jiang. A Novel Nano-Structured Die Steel with High Strength and High Thermal Stability [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(9): 1591-1603.
[7]	Hongliang Liu, Jingpei Nie, Liwei Bai, Yujing Fu, Xiaoguang Yang, Zhen Chang, Xue Zhang, Ying Li. Preparation and Anti-Oxidation Mechanism of an Inventive Preprocessing Method for Press-Hardened Steels [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(9): 1604-1612.
[8]	Yutao Wang, Liming Fu, Shuo Ma, Wei Wang, Aidang Shan. A 2.6 GPa Ultra-Strong Steel with Ultrafine Lamellar Structure Produced by Heavy Warm Rolling [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(9): 1613-1627.
[9]	Jiayu Wang, Ke Liu, Zhao Lei, Xing Li, Li Liu, Sujun Wu. Machine-Learning-Assisted Phase Prediction in High-Entropy Alloys Using Two-Step Feature Selection Strategy [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(8): 1261-1274.
[10]	Zihao Qiu, Chenwei Shao, Shuaijie Han, Yang Lu, Zhiqin Wang, Hanzhong Liu, Zhenjun Zhang, Zhefeng Zhang. Breaking Strength-Ductility Trade-off Relation in Ti-38644 Alloy with Heterogeneous Bi-Grain Bi-Lamella Structure [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(8): 1312-1316.
[11]	Yi-Fan Zhang, Liang-Yu Chen, Zi-Han Ge, Chenglong Teng, Yong Liu, Lai-Chang Zhang. In Vitro Gradual Decrease in Strength of Ti Scaffolds in Hank’s Solution upon Long-Term Immersion: Challenges and Prospective Solutions [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(8): 1331-1339.
[12]	Sen Ge, Ben Niu, Zhen-Hua Wang, Qian-Fu Pan, Chao-Hong Liu, Qing Wang. Recrystallization Behavior and Mechanical Property of a Medium-Si 12%Cr Reduced Activation Ferritic/Martensitic Steel Cladding Tube During the Manufacture [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(8): 1385-1396.
[13]	Haoyu Cheng, Chenyang Hou, Jianlei Zhang, Xiaodong Mao, Yuanxiang Zhang, Yanyun Zhao, Chulun Shen, Changjiang Song. An Innovative Large-Scale Preparation Method for ODS Steel: Zone Melting with Built-In Precursor Powder [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(8): 1397-1409.
[14]	Haoran Pang, Liwei Lu, Gongji Yang, Xiaojun Wang, Wen Wang, Hua Zhang, Yujuan Wu. Amelioration of Mechanical Properties of Rolled Mg-4.5Al-2.5Zn Alloy by Cryogenic Cycling Treatment [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(8): 1436-1452.
[15]	Qi Zhou, Yufeng Xia, Yu Duan, Baihao Zhang, Yuqiu Ye, Peitao Guo, Lu Li. Microstructure and Mechanical Properties of Yb-Containing AZ80 Cast Alloys [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(7): 1095-1108.

Tensile behavior of Sn-0.7Cu with Zn addition at various deformation temperatures

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments