ON DISCONTINUOUS REINFORCED NiAl-BASED COMPOSITES

Abstract

Abstract: Mechanically alloyed NiAl-TiB_2-Y_2O_3 composite (volume percentage of dispersoids about 15v%) was prepared by hot pressing. The compressive properties of the composite from 300 K to 1360 K were tested and the microstructures were studied mainly by TEM. The yield strengths of the composite at room temperature and high temperatures are considerably higher than that of monolithic NiAl and also is higher than similar NiAl-based composites which contained higher content of dispersoids but showed coarser microstructure. The possible strengthening mechanisms working in the composite are discussed.

Key words: NiAl, composite, strength

CHENG Tianyi (Metal Materials Section, Beijing Institute of Technology, P.O.Box 327, China,International Centre for Materials Physics, Academia Sinica, Shenyang 110015), China. ON DISCONTINUOUS REINFORCED NiAl-BASED COMPOSITES[J]. Acta Metallurgica Sinica (English Letters), 1995, 8(z1): 589-595.

[1]	Xinqi Ji, Yue Zhang, Wenhan Jin, Xin Qi. A strategy on the consistency of tensile strength of friction stir lap welding joint based on the same peak temperature [J]. Metals Advances, 2026, 40(2): 78-87.
[2]	Xuhui Liu, Zijin Xiao, Yang Yuan, Qihong Huang, Kaiwei Tang, Yilong Dai, Dechuang Zhang, Jia She, Feng Peng, Fugang Qi, Xiaoping Ouyang. Corrosion-resistant and bioactive FeMn-CaP-Col@CS coating on magnesium alloy for orthopedic implants: Fabrication and characterization [J]. Metals Advances, 2026, 39(1): 1-12.
[3]	X.L. Wang, J.Y. Li, Q.S. Mei. Recent progress in Zn matrix composites for biomedical applications [J]. Metals Advances, 2026, 39(1): 26-37.
[4]	Xinhao Li, Jieli Ma, Yiren Wang, Yong Jiang. A Novel Nano-Structured Die Steel with High Strength and High Thermal Stability [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(9): 1591-1603.
[5]	Yutao Wang, Liming Fu, Shuo Ma, Wei Wang, Aidang Shan. A 2.6 GPa Ultra-Strong Steel with Ultrafine Lamellar Structure Produced by Heavy Warm Rolling [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(9): 1613-1627.
[6]	Xu Liu, Lan-Yun Yang, Li-Ting Zeng, Yun Peng, Chen-Xi Xu, Lei Li, Jia-Le Sun, Yang-Yang Chen, Liang Chen, Zhao-Hui Hou. A Self-Sacrifice Template Method to Produce FeS Encapsulated into N, S Co-Doped Carbon for Improved Lithium Storage Performance [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(9): 1637-1644.
[7]	Zihao Qiu, Chenwei Shao, Shuaijie Han, Yang Lu, Zhiqin Wang, Hanzhong Liu, Zhenjun Zhang, Zhefeng Zhang. Breaking Strength-Ductility Trade-off Relation in Ti-38644 Alloy with Heterogeneous Bi-Grain Bi-Lamella Structure [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(8): 1312-1316.
[8]	Yi-Fan Zhang, Liang-Yu Chen, Zi-Han Ge, Chenglong Teng, Yong Liu, Lai-Chang Zhang. In Vitro Gradual Decrease in Strength of Ti Scaffolds in Hank’s Solution upon Long-Term Immersion: Challenges and Prospective Solutions [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(8): 1331-1339.
[9]	Sen Ge, Ben Niu, Zhen-Hua Wang, Qian-Fu Pan, Chao-Hong Liu, Qing Wang. Recrystallization Behavior and Mechanical Property of a Medium-Si 12%Cr Reduced Activation Ferritic/Martensitic Steel Cladding Tube During the Manufacture [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(8): 1385-1396.
[10]	Haoyu Cheng, Chenyang Hou, Jianlei Zhang, Xiaodong Mao, Yuanxiang Zhang, Yanyun Zhao, Chulun Shen, Changjiang Song. An Innovative Large-Scale Preparation Method for ODS Steel: Zone Melting with Built-In Precursor Powder [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(8): 1397-1409.
[11]	Yuxuan Li, Xi Zhao, Shuchang Li, Yihan Gao, Rui Guo. Precipitation Behavior and Strengthening and Toughening Mechanisms of Pre-fabricated Strong Basal Texture AZ80 + 0.4%Ce Alloy Under Room-Temperature Pre-deformation Coupled with Dual-Stage Aging Conditions [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(7): 1127-1144.
[12]	Fei Yang, Canhui Wu, Ruifeng Li, Wenyi Huo, Liming Dong, Feng Fang. Strain-Induced Balancing of Strength and Electrical Conductivity in Cu-20 wt% Fe Alloy Wires: Effect of Drawing Strain [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(7): 1246-1260.
[13]	Yunhu Ding, Yingpeng Li, Hongfang Liu, Wenhao Wang, Yijun Wei, Haitao Duan, Wen Zhan. Corrosion Evolution Behavior of Ti/Zr/Oligomeric Epoxy Silane Composite Chemical Conversion Coatings on Multi-metals [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(6): 889-903.
[14]	Chenzhi Xing, Ming-Hsien Lee, Gongwang Cao, Yuwei Liu, Quanzhong Guo, Zhenyao Wang, Chuan Wang. Discoloration Process of Minted Copper-Nickel Alloys in Chloride Ion-Containing Environments: Experimental and DFT Research [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(6): 925-945.
[15]	Cuicui Shu, Pengcheng Zhai, Xiege Huang, Sergey I. Morozov, Guodong Li, Zhiyuan Pan. First Principles Study of CoSb₃/Ni Interface Structure and Mechanical Properties [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(5): 793-802.

ON DISCONTINUOUS REINFORCED NiAl-BASED COMPOSITES

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments