Ratcheting Behavior of SA508-3 Steel at Elevated Temperature:Experimental Observation and Simulation

doi:10.1007/s40195-017-0588-1

Abstract

Abstract:

A series of monotonic uniaxial tensile tests, strain-controlled and stress-controlled cyclic tests of SA508-3 steel were conducted from 25 to 350 °C. Results showed that the steel exhibited temperature-dependent cyclic softening characteristic and obvious ratcheting behavior, and dynamic strain aging was observed in the range of 250-350 °C. Based on experimental observations, a temperature-dependent cyclic plastic constitutive model was proposed by introducing the nonlinear cyclic softening and kinematic hardening rules, and the dynamic strain aging was also considered into the constitutive model. Comparisons between experiments and simulations were carried out to validate the proposed model at elevated temperature.

Key words: Ratcheting, Constitutive model, Dynamic strain aging, Cyclic loading, Elevated temperature

Cite this article

Jun Tian, Yu Yang, Zhang Li Ping, Shao Xue Jiao, Juan Du, Kan Qian Hua. Ratcheting Behavior of SA508-3 Steel at Elevated Temperature:Experimental Observation and Simulation[J]. Acta Metallurgica Sinica (English Letters), 2017, 30(9): 822-828.

share this article

/ Recommend

Add to citation manager EndNote|Ris|BibTeX

URL: https://www.met-adv.cn/EN/10.1007/s40195-017-0588-1

https://www.met-adv.cn/EN/Y2017/V30/I9/822

Figures/Tables 7

Fig. 1 Monotonic tensile stress-strain curves at different temperatures: a experiments, b simulations by the proposed model, c simulations by the Chaboche model

Fig. 2 Experimental stress-strain curves of SA508-3 for uniaxial strain cycling under strain amplitude of 0.6% at a 25 °C; b 350 °C; c experimental and simulated stress amplitudes versus number of cycles by the proposed model

Table 1 Loading cases of stress cyclic tests at different temperatures for SA508-3 steel

Case	Temperature (°C)	First step (MPa)	Second step (MPa)
1	25	50 ± 450	50 ± 475
2	25	50 ± 450	75 ± 450
3	100	50 ± 450	50 ± 475
4	100	50 ± 450	75 ± 450
5	200	50 ± 425	50 ± 450
6	200	50 ± 425	75 ± 425
7	250	50 ± 425	50 ± 450
8	250	50 ± 425	75 ± 425
9	300	50 ± 425	50 ± 450
10	300	50 ± 425	75 ± 425
11	350	50 ± 425	50 ± 450
12	350	50 ± 425	75 ± 425

Table 1 Loading cases of stress cyclic tests at different temperatures for SA508-3 steel

Case	Temperature (°C)	First step (MPa)	Second step (MPa)
1	25	50 ± 450	50 ± 475
2	25	50 ± 450	75 ± 450
3	100	50 ± 450	50 ± 475
4	100	50 ± 450	75 ± 450
5	200	50 ± 425	50 ± 450
6	200	50 ± 425	75 ± 425
7	250	50 ± 425	50 ± 450
8	250	50 ± 425	75 ± 425
9	300	50 ± 425	50 ± 450
10	300	50 ± 425	75 ± 425
11	350	50 ± 425	50 ± 450
12	350	50 ± 425	75 ± 425

Fig. 3 Experimental and simulated curves of ratcheting strain versus number of cycles at a 25 °C; b 100 °C; c 200 °C; d 250 °C; e 300 °C; f 350 °C

Fig. 4 Experimental and simulated curves of ratcheting strain versus number of cycles by the proposed model a at 25 °C; b at different temperatures

Fig. 5 Exponential relationship between the plastic hardening moduli C and accumulated plastic strain at a 200 °C; b 300 °C

Table 2 Material parameters for SA508-3 steel in the Chaboche model

Temperature (°C)	Material parameters
25	C₁ = 7 × 10³ MPa, C₂ = 2.8 × 10³ MPa, C₃ = 800 MPa, r₁ = 100, r₂ = 25, r₃ = 30
100	C₁ = 9 × 10³ MPa, C₂ = 1.5 × 10³ MPa, C₃ = 770 MPa, r₁ = 100, r₂ = 25, r₃ = 30
200	C₁ = 1 × 10⁴ MPa, C₂ = 2.2 × 10³ MPa, C₃ = 474 MPa, r₁ = 100, r₂ = 25, r₃ = 30
250	C₁ = 1.5 × 10⁴ MPa, C₂ = 4 × 10³ MPa, C₃ = 600 MPa, r₁ = 250, r₂ = 25, r₃ = 30
300	C₁ = 1.6 × 10⁴ MPa, C₂ = 3.2 × 10³ MPa, C₃ = 820 MPa, r₁ = 250, r₂ = 25, r₃ = 30
350	C₁ = 3.3 × 10³ MPa, C₂ = 5.8 × 10³ MPa, C₃ = 100 MPa, r₁ = 250, r₂ = 25, r₃ = 30

Table 2 Material parameters for SA508-3 steel in the Chaboche model

Temperature (°C)	Material parameters
25	C₁ = 7 × 10³ MPa, C₂ = 2.8 × 10³ MPa, C₃ = 800 MPa, r₁ = 100, r₂ = 25, r₃ = 30
100	C₁ = 9 × 10³ MPa, C₂ = 1.5 × 10³ MPa, C₃ = 770 MPa, r₁ = 100, r₂ = 25, r₃ = 30
200	C₁ = 1 × 10⁴ MPa, C₂ = 2.2 × 10³ MPa, C₃ = 474 MPa, r₁ = 100, r₂ = 25, r₃ = 30
250	C₁ = 1.5 × 10⁴ MPa, C₂ = 4 × 10³ MPa, C₃ = 600 MPa, r₁ = 250, r₂ = 25, r₃ = 30
300	C₁ = 1.6 × 10⁴ MPa, C₂ = 3.2 × 10³ MPa, C₃ = 820 MPa, r₁ = 250, r₂ = 25, r₃ = 30
350	C₁ = 3.3 × 10³ MPa, C₂ = 5.8 × 10³ MPa, C₃ = 100 MPa, r₁ = 250, r₂ = 25, r₃ = 30

References

[1]	G. Kang, Int. J. Fatigue 30, 1448 (2008)
[2]	K. Sai, Int. J. Plast27, 250(2011)
[3]	X. Chen, X. Chen, D. Yu, B. Gao, 113 (2013
[4]	A. Mishra, P. Chellapandi, R.S. Kumar, G. Sasikala, Trans. Indian Inst. Met. 68, 161(2015)
[5]	Y.C. Lin, Z.H. Liu, X.M. Chen, J. Chen, Mater. Sci. Eng. A 573, 234 (2013)
[6]	Y.C. Lin, X.M. Chen, Z.H. Liu, J. Chen, Int. J. Fatigue 48, 122 (2013)
[7]	C.L. Pun, Q. Kan, P.J. Mutton, G. Kang, W. Yan, Int. J. Fatigue 66, 138 (2014)
[8]	G. Kang, Q. Gao, Key Eng. Mater. 247, 275-276 (2004)
[9]	C.O. Frederick, P. Armstrong, Mater. High Temp. 24, 1(2007)
[10]	J. Chaboche, D. Nouailhas, J. Eng. Mater. Tech. 111, 409(1989)
[11]	N. Ohno, J.D. Wang, Int. J. Plast9, 375(1993)
[12]	M. Abdel-Karim, N. Ohno, Int. J. Plast16, 225(2000)
[13]	G. Kang, Q. Kan, Mech. Mater. 39, 488(2007)
[14]	Y.C. Lin, Z.H. Liu, X.M. Chen, Z.L. Long, J. Mater. Eng. Perform. 24, 1820(2015)
[15]	D. Dong, F. Chen, Z. Cui, A 634, 103 (2015)
[16]	M. Sun, L. Hao, S. Li, D. Li, Y. Li, J. Nucl. Mater. 418, 269(2011)
[17]	J. Liu, L. Wang, Y. Liu, X. Song, J. Luo, D. Yuan, Int. J. Miner. Metall. Mater. 21, 1187(2014)
[18]	M. Yaguchi, Int. J. Plast21, 43(2005)
[19]	S. Xu, X.Q. Wu, E.H. Han, W. Ke, J. Mater. Sci. 44, 2882(2009)
[20]	J.L. Chaboche, Int. J. Plast5, 247(1989)
[21]	J. Ahlstr?m, E. Kabo, A. Ekberg, Wear 366-367, 378(2016)

Related Articles 15

[1]	Fei-Yang Chen, Peng-Cheng Guo, Zi-Han Jiang, Xiao Liu, Tie-Jun Song, Chao Xie. Abnormal Twinning Behavior and Constitutive Modeling of a Fine-Grained Extruded Mg-8.0Al-0.1Mn-2.0Ca Alloy under High-Speed Impact along Various Directions [J]. Acta Metallurgica Sinica (English Letters), 2023, 36(2): 281-294.
[2]	Hongbin Zhang, Kang Chen, Zhongwei Wang, Haiping Zhou, Chengcheng Shi, Shengxue Qin, Jie Liu, Tingjun Lv, Jian Xu. Thermal Deformation Behavior and Processing Map of a Novel CrFeNiSi_0.15 Medium Entropy Alloy [J]. Acta Metallurgica Sinica (English Letters), 2023, 36(11): 1870-1882.
[3]	Xin-Tong Lian, Jin-Lan An, Lei Wang, Han Dong. A New Strategy for Restraining Dynamic Strain Aging in GH4169 Alloy During Tensile Deformation at High Temperature [J]. Acta Metallurgica Sinica (English Letters), 2022, 35(11): 1895-1902.
[4]	Yixing Wan, Jinyong Mo, Xin Wang, Zhibin Zhang, Baolong Shen, Xiubing Liang. Mechanical Properties and Phase Stability of WTaMoNbTi Refractory High-Entropy Alloy at Elevated Temperatures [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(11): 1585-1590.
[5]	Yan-Sen Hao, Wan-Chun Liu, Zhen-Yu Liu. Microstructure Evolution and Strain-Dependent Constitutive Modeling to Predict the Flow Behavior of 20Cr-24Ni-6Mo Super-Austenitic Stainless Steel During Hot Deformation [J]. Acta Metallurgica Sinica (English Letters), 2018, 31(4): 401-414.
[6]	Rui Wang, Hai-Juan Mei, Ren-Suo Li, Quan Zhang, Teng-Fei Zhang, Qi-Min Wang. Friction and Wear Behavior of AlTiN-Coated Carbide Balls Against SKD11 Hardened Steel at Elevated Temperatures [J]. Acta Metallurgica Sinica (English Letters), 2018, 31(10): 1073-1083.
[7]	Bao-Sheng Xie,Qing-Wu Cai,Wei Yu,Li-Xiong Xu,Zhen Ning. Prediction for Flow Stress of 95CrMo Hollow Steel During Hot Compression [J]. Acta Metallurgica Sinica (English Letters), 2017, 30(3): 250-260.
[8]	Qing-Feng Zhu, Gao-Song Wang, En-Ge Zhang, Fan-Zheng Liu, Zhi-Qiang Zhang, Jian-Zhong Cui. Dynamic and Static Aging Precipitation of β-Mg₁₇Al₁₂ in the AZ80 Magnesium Alloy During Multi-directional Forging and Subsequent Aging [J]. Acta Metallurgica Sinica (English Letters), 2017, 30(10): 941-948.
[9]	Guo-Ming Han, Cheng-Gang Tian, Chuan-Yong Cui, Zhuang-Qi Hu, Xiao-Feng Sun. Portevin-Le Chatelier Effect in Nimonic 263 Superalloy [J]. Acta Metallurgica Sinica (English Letters), 2015, 28(5): 542-549.
[10]	Shi-Hong Zhang, Shuai-Feng Chen, Yan Ma, Hong-Wu Song, Ming Cheng. Developments of New Sheet Metal Forming Technology and Theory in China [J]. Acta Metallurgica Sinica (English Letters), 2015, 28(12): 1452-1470.
[11]	Lingyan Zhao, Dingyi Zhu, Longlong Liu, Zhenming Hu, Mingjie Wang. Strain Hardening Associated with Dislocation, Deformation Twinning, and Dynamic Strain Aging in Fe–20Mn–1.3C–(3Cu) TWIP Steels [J]. Acta Metallurgica Sinica (English Letters), 2014, 27(4): 601-608.
[12]	Leyang DAI. Behavior of Fe Powder During High-Energy Ball Milling Cooperated with Dielectric Barrier Discharge Plasma [J]. Acta Metallurgica Sinica (English Letters), 2013, 26(1): 63-68.
[13]	Yujie LIU, Qing GAO and Guozheng KANG. A damage-coupled multi-axial time-dependent low cycle fatigue failure model for SS304 stainless steel at high temperature [J]. Acta Metallurgica Sinica (English Letters), 2011, 24(2): 169-174.
[14]	Xiaohua ZHANG,Daoxin LIU. Effects of temperature, slip amplitude, contact pressure on fretting fatigue behavior of Ti811 alloys at elevated temperatures [J]. Acta Metallurgica Sinica (English Letters), 2009, 22(2): 131-137.
[15]	Z.M. Zhang, C.J. Xu, X.F. Guo, S.Z. Jia. Reciprocating Extrusion Of In Situ Mg 2 Si Reinforced Mg-Al Based Composite [J]. Acta Metallurgica Sinica (English Letters), 2008, 21(3): 169-177 .

Metrics

Viewed

Full text

Abstract

Comments

Abstract
Figures/Tables
References
Related Articles
Recommended Articles
Metrics
Comments

TOP