Acta Metallurgica Sinica (English Letters) >
Plasma enhanced diamond deposition on steel and Si substrates
Received date: 2008-12-05
Revised date: 2009-03-02
Online published: 2009-10-15
Diamond growth on Fe-Cr-Al-Si steel and Si substrates was comparatively investigated in microwave plasma enhanced chemical vapor deposition (MPCVD) reactor with different deposition parameters. Adherent nanocrystalline diamond films were directly deposited on this steel substrate under a typical deposition condition, whereas microcrystalline diamond films were produced on Si wafer. With increasing CH4 concentration, reaction pressure, or the total gas flow rate, the quality of nanocrystalline diamond films formed on Fe-Cr-Al-Si substrates is gradually deteriorated in terms of density and adhesion. This impaired diamond quality on steels is primarily associated with a combined effect by the substrate composition and the specific process conditions that favor excessive nucleation of diamond.
Key words： Plasma CVD; Diamond film; Steel; Si
Y.S. Li , Y. Tang , W.Chen , Q. Yang , C. Xiao , A.Hirose . Plasma enhanced diamond deposition on steel and Si substrates[J]. Acta Metallurgica Sinica (English Letters), 2009 , 22(5) : 321 -329 . DOI: 10.1016/S1006-7191(08)60105-2
[1] X.G. Jian, L.D. Shi, M. Chen and F.H. Sun, Diamond Relat Mater 15(2-3) (2006) 313.
[2] R. Polini, Thin Solid Films 515(1) (2006) 4.
[3] A. Kromka, B. Rezek and Z. Remes, Chem Vap Deposition 14(7-8) (2008) 187.
[4] X.M. Meng, W.Z. Tang, L.F. Hei, C.M. Li, S.J. Askari, G.C. Chen and F.X. Lu, Int J Refract Met Hard Mater 26(5) (2008) 485.
[5] W. Chen, X. Lu, Q. Yang, C. Xiao, R. Sammynaiken, J.Maley and A. Hirose, Thin Solid Films 515(4) (2006)1970.
[6] J. Ahn, F.H. Tan and H.S. Tan, Diamond Relat Mater 2(2-4) (1993) 353.
[7] R. Haubner and B. Lux, Int J Refract Met Hard Mater 24(5) (2006) 380.
[8] J. Spinnewyn, M. Nesladek and C. Asinari, Diamond Relat Mater 2(2-4) (1993) 361.
[9] H. Chen, M.L. Nielsen, C.J. Gold and R.O. Dillon, Thin Solid Films 212(1-2) (1992) 169.
[10] T.P. Ong and R. Chang, Appl Phys Lett 58(4) (1991) 358.
[11] Y.S. Li and A. Hirose, Chem Phys Lett 433(1-3) (2006) 150.
[12] Y.S. Li and A. Hirose, Surf Coat Technol 202(2) (2007) 280.
[13] Y.S. Li, Q. Yang, C. Xiao and A. Hirose, Thin Solid Films 516(10) (2008) 3089.
[14] F.X. Lu, W.Z. Tang and Y.M. Tong, Diamond Relat Mater 15(11-12) (2006) 2039.
[15] R. Polini, G. Mattei and R. Valle, Thin Solid Films 515(3) (2006) 1011.
[16] F.J.G. Silva, A.J.S. Fernandes, F.M. Costa, A.P.M.Baptista and E. Pereira, Surf Coat Technol 191(1) (2005)102.
[17] V. Mortet, A. Kromka, R. Kravets, J. Rosa, V. Vorlicek, J.Zemek and M. Vanecek, Diamond Relat Mater 13(4-8) (2004)604.
[18] L.C. Chen, T.Y. Wang and J.R. Yang, Diamond Relat Mater 9(3-6) (2000) 877.
[19] H. Yoshikawa, C. Morel and Y. Koga, Diamond Relat Mater 10(9-10) (2001) 1588.
[20] M. Amaral, A. Fernandes and M. Vila, Diamond Relat Mater 15(11-12) (2006) 1822.
[21] Q. Yang, S. Yang, Y.S. Li, X. Lu and A. Hirose, Diamond Relat Mater 16(4-7) (2007) 730.
[22] S.A. Catledge and Y.K. Vohra, J Appl Phys 84(11) (1998) 6469.
[23] Y.S. Li, C. Xiao, A. Hirose, Q. Yang and S. Shimada, J Amer Ceram Soc 90(5) (2007) 1427.
[24] K. Subramanian, W.P. Kang, J.L. Davidson and W.H.Hofmeister, Diamond Relat Mater 14(3-7) (2005) 404.
[25] W. Kulisch, C. Popov, V. Vorlicek, P.N. Gibson and G.Favaro, Thin Solid Films 515(3) (2006) 1005.
/
| 〈 |
|
〉 |
WeChat