(001)-oriented FePt/Ag composite films for perpendicular recording
Received date: 2008-11-03
Revised date: 2009-05-05
Online published: 2009-10-15
FePt/Ag thin films were deposited by magnetron sputtering onto 7059 glass substrates, then were annealed at 550 ℃ for 30~min. Nanostructured FePt/Ag films were successfully obtained with the magnetic easy axis of L10 FePt perpendicular to the film plane. It was found that the development of (001) texture depended strongly on the thicknesses of FePt magnetic layer and Ag underlayer. The L10 ordered FePt(15 nm)/Ag(50 nm) with (001) orientation can be obtained. And the perpendicular coercivity of FePt(15 nm)/Ag(50 nm) film reached to 7.21×105 A/m, whereas the longitudinal one was only 3.2×104 A/m. The non-magnetic Ag underlayer can not only induce (001) orientation and ordering of FePt grains, but also reduce the intergrain interactions.
Wenfeng LIU , Fang WANG , Xiaohong XU . (001)-oriented FePt/Ag composite films for perpendicular recording[J]. Acta Metallurgica Sinica (English Letters), 2009 , 22(5) : 392 -396 . DOI: 10.1016/S1006-7191(08)60113-1
[1]} A.C. Sun, J.H. Hsu, P.C. Kuo, H.L. Huang,H.C. Lu and S.F. Wang, J Magn Magn Mater 310 (2007)2650.
[2]} S. Suzuki, IEEE Trans Magn 20 (1984) 675.
[3]} C.P. Luo and D.J. Sellmyer, IEEE Trans Magn 31 (1995) 2764.
[4]} K.R. Coffey, M.A. Parker and J.K. Howard, IEEE Trans Magn 31 (1995) 2737.
[5]} N. Li and B.M. Lairson, IEEE Trans Magn 35 (1999) 1077.
[6]} S.H. Whang, Q. Feng and Y.Q. Gao, Acta Mater 46 (1998) 6485.
[7]} M. Daniil, P.A. Farber, H. Okumura, G.C. Hadjipanayis and D. Weller, J Magn Magn Mater 246 (2002) 297.
[8]} X.H. Xu, H.S. Wu, F. Wang and X.L. Li, Thin Solid Films 472 (2005) 222.
[9]} K. Kang, T. Yang and T. Suzuki, IEEE Trans Magn 38 (2002) 2039.
[10]} K. Kang, Z.G. Zhang, C. Papusoi and T. Suzuki, Appl Phys Lett 82 (2003) 3284.
[11]} Y.N. Hsu, S. Jeong, D.N. Lambeth and D.E. Laughlin, IEEE Trans Magn 36 (2000) 2945.
[12]} Y.F. Ding, J.S. Chen and E. Liu, Thin Solid Films 474 (2005) 141.
[13]} J.J. Delaunay, T. Hayashi, M. Tomita and S. Hirono, IEEE Trans Magn 34 (1998) 1627.
[14]} E.P. Wolfforth, J Appl Phys 29 (1958) 595.
[15]} V. Basso and G. Bertotti, IEEE Trans Magn 30 (1994) 64.
[16]} Z.L. Zhao, J.S. Chen, J. Ding, K. Inaba and J.P. Wang, J Magn Magn Mater 282 (2004) 105.
/
| 〈 |
|
〉 |
WeChat