Rapid air film continuous casting of aluminum alloy using static magnetic field
Received date: 2008-09-12
Revised date: 2008-10-09
Online published: 2009-10-15
The influences of the cooling style and static magnetic field on the air film casting process were investigated. Ingots of 6063 aluminum alloy were produced by AIRSOL VEIL casting with double-layer cooling water and static magnetic field. Surface segregation, hot crack and variation of solute content along the radius direction of ingot were examined. The results showed that double-layer cooling water can improve the surface quality and avoid of hot crack, which created conditions to increase the casting speed. The electromagnetic casting process can effectively improve the surface quality in high speed casting process, and static magnetic field has a great influence on solute distribution along the radius direction of ingot.
Key words： Air film casting; Static magnetic field; Surface quality; Casting speed
Fu QU , Huixue JIANG , Gaosong WANG , Qingfeng ZHU , Xiangjie WANG , Jianzhong CUI . Rapid air film continuous casting of aluminum alloy using static magnetic field[J]. Acta Metallurgica Sinica (English Letters), 2009 , 22(5) : 339 -344 . DOI: 10.1016/S1006-7191(08)60107-6
[1] J.M. Ekenes and F.E. Wagstaff, Light Metals: Proceedings of Sessions, AIME Annual Meeting (Pennsylvania, Warrendale, 1985) p.1311.
[2] W. Schneider and G.U. Grun, 4thAustralasian Asian Pacific Course and Conference (Minerals,Metals and Materials Society, Warrendale, 1995) p.297.
[3] J. Sengupta, S.L. Cockcroft and D. Maijer, J Light Met 2 (2002) 137.
[4] J. Grandfield, K. Goodall and P. Misic, Light Metals 1997, R. Huglen ed (TMS, Warrendale, 1997) p.1081.
[5] T.W. Clyne and G.J. Davies, Foundryman 74 (1981) 65.
[6] Y. Zuo, J. Cui and J. Dong, Mater Sci Eng A408 (2005) 176.
[7] B. Zhang, J. Cui and G. Lu, Mater Sci Eng A355 (2003) 325.
[8] P. Gillon, Mater Sci Eng A287 (2000) 146.
[9] A. Garcia, J. Quaresma and N. Cheung, Mater Sci Eng A431(15) (2006) 201.
[10] J. Shen, J. Li and L.G. Li, Trans Nonferrous Met Soc Chin 5(4) (1995) 64.
[11] D.Y. Li, D. Shi and Y. Zhang, Trans Nonferrous Met Soc Chin 15(2) (2005) 17.
/
| 〈 |
|
〉 |
WeChat