Phase field modeling of dendrite growth
Received date: 2008-10-17
Revised date: 2009-02-15
Online published: 2009-10-10
Single dendrite and multi-dendrite growth for Al-2 mol pct Si alloy during isothermal solidification are simulated by phase field method. In the case of single equiaxed dendrite growth, the secondary and the necking phenomenon can be observed. For multi-dendrite growth, there exists the competitive growth among the dendrites during solidification. As solidification proceeds, growing and coarsening of the primary arms occurs, together with the branching and coarsening of the secondary arms. When the diffusion fields of dendrite tips come into contact with those of the branches growing from the neighboring dendrites, the dendrites stop growing and being to ripen and thicken.
Yutuo ZHANG , Chengzhi WANG , Dianzhong LI , Yiyi LI . Phase field modeling of dendrite growth[J]. Acta Metallurgica Sinica (English Letters), 2009 , 22(3) : 197 -201 . DOI: 10.1016/S1006-7191(08)60089-7
[1] J. Rosam, P.K. Jimack and A.M. Mullis, Acta Mater 56(2008)4559.
[2] B. Bottger, J. Eiken and I. Steinbach, Acta Mater 54(2006)2697.
[3] W. Miller, I. Rasin and F. Pimentel, J Cryst Growth 266(2004)283.
[4] P.R. Cha, D.H. Yeonb and J.K. Yoon, J Cryst Growth 274(2005)281.
[5] J.C. Wang and G.C. Yang, Acta Mater 56(2008)4585.
[6] Y.J. Chen, C.L. Chen, W.X. Qiu and S. Jiang, Spec Cast Nonferrous Alloy 28(2008)513.
[7] Z.P. Wang, K.W. Shi, C.S. Zhu, L. Feng and R.Z. Xiao, Hot Work Technol 37(2008)4.
[8] W.Y. Long, C. Xia, B.W. Xiong and L.G. Fang, Chin Phys 17(2008)1078.
[9] Y.E. Niu, W. Yan, X.M. Feng, J. Chen and X.H. Fan, Foundry Technol 29(2008)244.
[10] M.E. Li, G.C. Yang and Y.H. Zhou, Acta Phys Sin 54 (2005) 454.
[11] T. Suzuki, M. Ode, S.G. Kim and W.T. Kim, J Cryst Growth 237-239(2002)125.
[12] S.G. Kim, W.T. Kim and T. Suzuki, Phys Rev E 60 (1999) 7186.
[13] W. Kurz and D.J. Fisher, Fundamentals of Solidification, 4th Edition, Trans Technol Publications Ltd.,Switzerland, 1998.
/
| 〈 |
|
〉 |
WeChat