Acta Metallurgica Sinica (English Letters) >
Research of warm compaction technology on nylon bonded Nd-Fe-B magnets
Received date: 2008-06-25
Revised date: 2008-08-25
Online published: 2009-10-10
Warm compaction and room temperature compaction were applied to prepare bonded Nd-Fe-B magnets. Warm compaction was proved to be a good way to improve the density, magnetic and mechanical properties of bonded magnets. The results indicated that the density of magnet was determined by the compaction pressure and warm compaction temperature, while the thermosetting temperature could hardly affect the density of magnet. The mechanical properties of magnets were the best when the thermosetting temperature was 200℃. The Br, Hcb and (BH)max of warm compaction magnet were higher than that of room compaction. When the warm compaction temperature and thermosetting temperature were invariable, the density of magnet increased with the increase of compaction pressure, which resulted in the increase of Br, Hcb and (BH)max of magnet and the decrease of Hcj of magnet. When the warm compaction temperature and compaction pressure were invariable, the magnetic properties of magnets decreased with the increase of thermosetting temperature. The magnetic properties of warm compaction molding magnets were better than that of injection molding magnets.
Xiuhai ZHANG , Weihao XIONG , Dameng YE , Jun QU , Zhenhua YAO . Research of warm compaction technology on nylon bonded Nd-Fe-B magnets[J]. Acta Metallurgica Sinica (English Letters), 2009 , 22(3) : 174 -180 . DOI: 10.1016/S1006-7191(08)60086-1
[1] D. Brown, B.M. Ma and Z.M. Chen, J Magn Magn Mater 248(2002)432.
[2] B.M. Ma, J.W. Herchenroeder, B. Smith, M. Suda, D.N.Brown and Z. Chen, J Magn Magn Mater 239(2002)418.
[3] J.M.D. Coey, J Alloy Compd 326(2001)2.
[4] W. Chen, R.W. Gao, M.G. Zhu, W. Pan and W. Li, J Magn Magn Mater 262(2003)222.
[5] J.M.D. Coey, J Appl Phys 81(1997)4810.
[6] M.G. Garrell, A.J. Shih, B.M. Ma, E.L. Curzio and R.O.Scattergood, J Magn Magn Mater 257(2003)32.
[7] C.F. Wu and W.J. Xu, Polymer 47(2006)6004.
[8] D. Plusa, M. Dospial, B. Slusarek and U. Kotlarczyk, J Magn Magn Mater 306(2006)302.
[9] J.K. Kuo and C.K. Chen, J Powder Sources 162(2006)207.
[10] Y.D. Peng, J.H. Yi, T.M. Ye, L.Y. Li, Q.L. Xia and H.Z.Wang, Mater Sci Eng Powder Metall 11(2006)133 (in Chinese).
[11] A.K. Ariffin, M.M. Rahman, N. Muhamad and J. Sahari, J Mater Process Technol 116(2001)67.
[12] H. Shokrollahi and K. Janghorban, J Magn Magn Mater 313(2007)182.
[13] C.B. Rong, V. Nandwana, N. Poudyal and J.P. Liu, J Appl Phys 102(2007)1.
[14] X. Yang, S.J. Guo and F. Akluar, Materials 13(2006)528.
[15] M. Yue, Y.P. Wu, Y.F. Xiao and J.X. Zhang, Mater Sci Technol 15(2007)541.
[16] L. Lu, S.X. Bai, H. Zhang and J. Funct, Mater Devices 9(2003)337 (in Chinese).
[17] J. Xiao, J.U. Otaigbe and D.C. Jiles, J Magn Magn Mater 218(2000)60.
[18] J. Li, Y. Liu, S.J. Gao, M. Li, Y.Q. Wang and M.J. Tu, J Magn Magn Mater 299(2006)195.
[19] Y.K. Chen and J.W. Ye, Powder Metall Technol 24(2006)263 (in Chinese).
[20] Z.H. Hua, S.D. Li and Z.D. Han, J Rare Earths 25(2007)336 (in Chinese).
[21] J. Zhu, J Rare Earths 22 (2001) 60 (in Chinese).
[22] B.H. Duan, X.H. Qu and Y.P. Li, J Magn Mater Devices 34(2003)36 (in Chinese).
[23] J.W. Ye, Y. Liu, L.X. Lian, J. Li and S.J. Gao, Electron Compon Mater 24(2005)14 (in Chinese).
/
| 〈 |
|
〉 |
WeChat