Effect of silicon and prior deformation of austenite on isothermal transformation in low carbon steels

  • Minghui CAI ,
  • Hua DING ,
  • Jiansu ZHANG ,
  • Long LI
Expand
  • 1) School of Materials and Metallurgy,Northeastern University, Shenyang 110004, China
    2) Technology Center, Baoshan Iron and Steel Co., Ltd., Shanghai 201900, China
    3) National Institute for Materials Science, Tsukuba 305-0047, Japan

Received date: 2008-08-25

  Revised date: 2008-11-21

  Online published: 2009-10-10

Abstract

Isothermal transformation (TTT) behavior of the low carbon steels with two Si contents (0.50 wt pct and 1.3 wt pct) was investigated with and without the prior deformation. The results show that Si and the prior deformation of the austenite have significant effects on the transformation of the ferrite and bainite. The addition of Si refines the ferrite grains, accelerates the polygonal ferrite transformation and the formation of M/A constituents, leading to the improvement of the strength. The ferrite grains formed under the prior deformation of the austenite become more homogeneous and refined. However, the influence of deformation on the tensile strength of both steels is dependent on the isothermal temperatures. Thermodynamic calculation indicates that Si and prior deformation reduce the incubation time of both ferrite and bainite transformation, but the effect is weakened by the decrease of the isothermal temperatures.

Cite this article

Minghui CAI , Hua DING , Jiansu ZHANG , Long LI . Effect of silicon and prior deformation of austenite on isothermal transformation in low carbon steels[J]. Acta Metallurgica Sinica (English Letters), 2009 , 22(2) : 100 -109 . DOI: 10.1016/S1006-7191(08)60076-9

References

[1]A. Kumar, S.B. Singh and K.K. Ray,  Mater Sci Eng  474A  (2008) 270.
[2]K. Hasegawa, K. Kawamura, T. Urabe and Y. Hosoya,  ISIJ Int  44(3)  (2004) 603.
[3]R.D.K. Misra, S.W. Thompson, T.A. Hylton and A.J. Boucek, Metall Mater Trans  32A  (2001) 745.
[4]R.A. Kot and B.L. Bramfitt,  Fundamentals of Dual-Phasemsteels  (Metallurgical Society of AIME, Warrendale, PA, 1981)p.447.
[5]M. Takahashi, O. Kawano and T. Hayashida,  Nippon SteelmTech Rep  378  (2003) 7.
[6]T. Araki, I. Kozasu, H. Tankechi, K. Shibata, M. Enomoto and H. Tamehiro,  ISIJ Int  1(4)  (1992) 1.
[7]L.J. Zhu, D. Wu and X.M. Zhao,  Acta Metall Sin (Engl Lett)  21(3)  (2008) 163.
[8]I. Tsukatani, S. Hashimoto and T. Inoue,  ISIJ Int  31(9)  (1991) 992.
[9]E. Essadiqi and J.J. Jonas,  Metall Trans  19A  (1991) 417.
[10]X. Fang, Z. Fan and B. Ralph,  J Mater Sci  38  (2003) 3877.
[11]P.G. Xu, B.Z. Bai, H.S. Fang, Z.J.Wang, J.P. Wang and Y.K.Pan,  J Univ Sci Technol Beijing,  10(2)  (2003) 39 (in Chinese).
[12]R.L. Larn and J.R. Yang,  Mater Sci Eng  278A  (2000) 278.
[13]C. Capdevila, C. Garcia and F.G. Caballero,  Scripta Mater  44(1)  (2001) 129.
[14]Z.Y. Xu and L.W. Mou,  Acta Mater  23A(1)  (1987)33 (in Chinese).
[15]Z.Y. Liu, G.D. Wang and Q. Zhang and L.X. Ma,  Acta Mater  30B(6)  (1994) 277 (in Chinese).
[16]Z.Y. Liu, Y.B. Xun and G.D. Wang,  Simulation and Predication of the Evolution of Microstructure and Properties of Hot Rolled Steels  (Northeastern University Press, Shenyang, 2004) p.156 (in Chinese).
[17] M. Gomez, S.F. Medina and G. Caruana,  ISIJ Int 43(8)  (2003) 1228.

Outlines

/