Relationship between powder characteristic and internal oxidation of Al in Cu-Al pre-alloyed powders
Received date: 2008-04-04
Revised date: 2008-08-19
Online published: 2009-10-10
Since Cu-Al powder characteristics have important effects on the preparation of Cu/Al2O3 composite, the apparent activation energy of Al internal oxidation reaction in Cu-Al pre-alloyed powders with different characteristics was calculated in the present investigation. The microstructure and properties of the synthesized Cu/Al2O3 were studied. The results show that high-energy milling can obviously promote internal oxidation of Al in Cu-Al powders in the same solid solubility. At the same milling conditions and internal oxidation parameters, the solid solution of Al in Cu either in low or high amount will result in the poor microstructure and properties of the Cu/Al2O3 composite. Subsequently, when high-energy milling and internal oxidation are synchronously used to prepare the Cu/Al2O3 composite, there should be an appropriate solubility and milling effect for the pre-alloyed powders.
Shuhua LIANG , Xianhui WANG , Liang FANG , Zhikang FAN . Relationship between powder characteristic and internal oxidation of Al in Cu-Al pre-alloyed powders[J]. Acta Metallurgica Sinica (English Letters), 2009 , 22(1) : 71 -80 . DOI: 10.1016/S1006-7191(08)60073-3
[1] J. Kiang, Y. Ni and W.T. Wu, Intermetallics 15(2007)635.
[2] M.X. Guo, M.P. Wang, L.F. Cao and R.S. Lei, Mater Characterization 58(2007)928.
[3] B.H. Tian, P. Liu, K.X. Song, Y. Li, Y. Liu,F.Z. Ren and J.H. Su, Mater Sci Eng A 435-436(2006)705.
[4] M.T. Marques, J.B. Correia, J.M. Criado, M.J.Dianez and P. Matteazzi, Key Eng Mater 230-232(2002)652.
[5] S.H. Kim and D.N. Lee, Mater Sci Eng A 313(2001)24.
[6] S.H. Kim and D.N. Lee, Mater Sci Eng A 319-321(2001)471.
[7] K. Kucharová, S.J.Zhu and J. Cadek, Mater Sci Eng A 348(2003)170.
[8] K. Kucharová , S.J. Zhu and J. Cadek, Mater Sci Eng A 355(2003)267.
[9] R.K. Islamgaliev, W.Buchgraber, Y.R. Kolobov, N.M. Amirkhanov, A.V. Sergueeva, K.V.Ivanov and G.P. Grabovetskaya Mater Sci Eng A 319-321(2001)872.
[10] S.T. Oh, J.S. Lee and T. Sekino, Scr Mater 44(2001)2117.
[11] M.S. Motta, P.K. Jena, E.A. Brocchi and I.G. Solózano, Mater Sci Eng C 15 (2001) 175.
[12] P.K. Jena, E.A. Brocchi and M.S. Motta, Mater Sci Eng A 313(2001)180.
[13] D.W. Lee, G.H. Ha and B.K. Kim, Scr Mater 44(2001)2137.
[14] J.Hwang Seung, D. Wexler and A. Calka, J Mater Sci 39(2004)4659.
[15] J.F. Perez and D.G. Morris, Scr Metall 31(1994)231.
[16] K.X. Song, J.D. Xing, Q.M. Dong, P. Liu, B.H. Tian and X.J. Cao, Mater Design 26(2005)337.
[17] T. Venugopal, K. Prasad Rao and B.S. Murty, Mater Sci Eng A 393(2005)382.
[18] S.H. Liang, Z.K.Fan and L. Fang, J Compos Mater 38(2004)1495.
[19] S.H. Liang, Z.K. Fan, L. Xu and L. Fang, Composites A 35(2004)1441.
[20] S.H. Liang, PhD Dissertation Internal Prepared Cu/Al2O3(Cr2O3) Composites and their Preparation Mechanism (Xi'an Jiaotong University,2004). [21] X.W. Chen, Physical Chemistry in Iron and Steel Metallurgy (Metallurgical Industry Press, Beijing, 1990) p.182.
[22] D. Feng, Metallic Physics (Science Press, Beijing, 1987) p.200.
/
| 〈 |
|
〉 |
WeChat