Chemical conversion coating on AZ31B magnesium alloy and its corrosion tendency
Received date: 2008-04-10
Online published: 2009-10-10
The morphology change of the magnesium matrix after pre-treatment and the morphology as well as the phase composition of chemical conversion coating formed by phosphate were studied using scanning electron microscope and X-ray diffraction. The corrosion resistance of the coating was studied by salt spray and damp test, and the corrosion tendency during salt immersion test was analyzed. The results show that the phase composition before and after pre-treatment is almost changeless, and the deep microflaw appears between α and β phases during acidic pickling. The phosphate conversion coating is mainly composed of Mg, MgO, and some amorphous phase, and it can provide a good protection for the AZ31B alloy. Results from corrosive morphology indicate that the growth and the corrosion resistance of the phosphate conversion coating are related to the forming process of the AZ31B matrix.
Hualan JIN , Xiangjie YANG , Ming WANG . Chemical conversion coating on AZ31B magnesium alloy and its corrosion tendency[J]. Acta Metallurgica Sinica (English Letters), 2009 , 22(1) : 65 -70 . DOI: 10.1016/S1006-7191(08)60072-1
[1]C.D. Gu, J.S. Lian, G.Y. Li, L.Y. Niu and Z.H.Jiang, J Chin Soc Corros Prot 25(2005)271.
[2]F.H. Froes and C.M. Ward-Close, J Mater Process Technol 48(1995)667.
[3]R. Gonz\'{a lez-Martinez, J. G\"{o ken, D. Letzig, J.Timmerberg, K. Steinhoff and K.U. Kainer, Acta Metall 20(2007)235.
[4]H.L. Jin, R.J. Wei and X.J. Yang, Mater Prot 37(2004) 27.
[5]H.L. Jin, X.J. Yang, R.J. Wei and X. Chen, Chin J Nonferrous Met 17(2007)963.
[6]D. Hawke and D.L. Albright, Met Finish 93(1995)34.
[7]B.L. Jiang, S.F. Zhang, G.J. Wu and T.Q. Lei, Chin J Nonferrous Met 12(2002)454.
[8]O. Sachiko, Oxide Corros Rev 16(1998)175.
[9]R. Subramanian, S. Srcars and J. Mazumder, J Mater Sci 26(1991)951.
[10]A.K. Sharma, M.R. Suresh and H. Bhojraj, Met Finish 96(1998)10.
[11]U. Hiroyuki, T. Matsufumi and I. Tetsuji, J Jpn Inst Light Met 48(1998)248.
[12]J. Wang and Y. Ding, Mater Prot 39(2006)38.
[13]Y. Zhang, Y. Xu, D.R. Zhou, X. Chen, Z.Y. Wu and G.F. Cui, J Harbin Inst Technol 34(2002)376.
[14]H.H. Elsentriecy, K. Azumi and H. Konno, Surf Coat Technol 202(2007)532.
[15]J.J. Yin, Y.D. Li, L.W. Liang and Y. Hao, J Gansu Univ Technol 29(2003)36.
[16]H.W. Huo, Y. Li and F.H. Wang, J Chin Soc Corros Prot 22(2002)14.
[17]M. Pourbaix, Atlas of Electrochemical Equilibrium in Aqueous Solution (National Association of Corrosion Engineers,Houston, 1974) p.141.
/
| 〈 |
|
〉 |
WeChat