Growth behavior of ultrafine austenite grains in microalloyed steel
Received date: 2008-03-06
Revised date: 2008-06-12
Online published: 2009-10-10
Ultrafine austenite grains (UFAGs) with size of 1-5 μm were prepared through repetitive treatment, four times, of rapid heating and quenching, and the growth behaviors of these UFAGs during both the reheating and cooling stages were investigated. The results indicated that UFAGs without pinning particles appeared with significant coarsening when the reheating temperature reached 1000℃. Although coarsening still occurred in the cooling stage, the growth was obscured during the isothermal holding process at temperatures between 900 ℃ and Ar3
Shengjie YAO , Shengjie YAO , Xianghua LIU , Guodong WANG . Growth behavior of ultrafine austenite grains in microalloyed steel[J]. Acta Metallurgica Sinica (English Letters), 2009 , 22(1) : 7 -12 . DOI: 10.1016/S1006-7191(08)60064-2
[1] J. Huang and Z. Xu, Mater Lett 60(2006)1854.
[2] V.V. Sagaradze, Nanostruct Mater 9(1997)201.
[3] Y. Kimura, S. Takagi and S. Terasaki, Proc of 4th Workshop on HIPERS-21 (Korea Institute of Metals and Materials Press, Pohang, Korea, 2002).
[4] G.X. Liu, Principle of Metals (Metallurgical Industry Press, Beijing,1983) p.308 (in Chinese).
[5] J. Moon, J. Lee and C. Lee, Mater Sci Eng A459(2007)40.
[6] S. Renata, A. Henryk and A. Anna, Mater Charact 56(2006)340.
[7] C.G.Xu and Y.G. Tian, Spec Steel 16(1995)19 (in Chinese).
[8] L.X. Du, M.X. Xiong, S.J. Yao, X.H. Liu and G.D. Wang, Acta Metall Sin 43(2007)59 (in Chinese).
[9] S. Uhm, J. Moon, C. Lee, J. Yoon and B. Lee, ISIJ Int 44(2004)1230.
[10] R.A. Vandermeer and H. Hu, Acta Metall Mater 42(1994)3071.
[11] C.S. Smith, Trans AIME 175(1949)15.
[12] J.J. Qi, Y.H. Huang and Y. Zhang, Microalloyed Steel (Metallurgical Industry Press, Beijing, 2006)p.33 (in Chinese).
[13] Z. Li, PhD Dissertation (Northeastern University, Shenyang, 2000).
/
| 〈 |
|
〉 |
WeChat