Phase and Microstructure Selection During Directional Solidification of Peritectic Alloy Under Convection Condition

  • Lingshui Wang ,
  • Jun Shen ,
  • Yilong Xiong ,
  • Yujun Du ,
  • Hengzhi Fu
Expand
  • State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an, 710072, China

Received date: 2013-09-16

  Revised date: 2013-12-25

  Online published: 2014-10-16

Abstract

A phase and microstructure selection map used for peritectic alloy directionally solidified under convection condition was presented, which is based on the nucleation, constitutional undercooling criterion (NCU criterion), and the highest interface temperature criterion. This selection map shows the relationships between the phase/microstructure, the G/V ratio (G is the temperature gradient, V is the growth velocity), and the alloy composition under different convection intensities and nucleation undercoolings. Comparing with the results from directional solidification experiments of Sn–Cd peritectic alloys, this selection map was generally in agreement with the experimental results.

Cite this article

Lingshui Wang , Jun Shen , Yilong Xiong , Yujun Du , Hengzhi Fu . Phase and Microstructure Selection During Directional Solidification of Peritectic Alloy Under Convection Condition[J]. Acta Metallurgica Sinica (English Letters), 2014 , 27(4) : 585 -592 . DOI: 10.1007/s40195-014-0096-5

References

[1] W.J. Boettinger, Metall. Mater. Trans. B 9, 2023(1974)10.1007/BF02644495
[2] W.Z. Luo, J. Shen, Z.X. Min, H.Z. Fu, Mater. Lett. 63, 1419(2009)10.1016/j.matlet.2009.03.037
[3] K. Tokieda, H. Yasuda, I. Ohnaka, Mater. Sci. Eng. A 262, 238(1999)10.1016/S0921-5093(98)01005-3
[4] D.M. Liu, X.Z. Li, Y.Q. Su, L.S. Luo, B. Zhang, J.J. Guo, H.Z. Fu, Mater. Lett. 65, 1628(2011)10.1016/j.matlet.2011.03.034
[5] J.S. Park, R. Trivedi, J. Cryst. Growth 187, 511(1998)10.1016/S0022-0248(97)00884-1
[6] L.S. Luo, Y.Q. Su, J.J. Guo, X.Z. Li, H.M. Yang, H.Z. Fu, Appl. Phys. Lett. 92, 061903(2008)10.1063/1.2841639
[7] R. Trivedi, Metall. Mater. Trans. A 26, 1583(1995)10.1007/BF02647608
[8] O. Hunziker, M. Vandyoussefi, W. Kurz, Acta Mater. 46, 6325(1998)10.1016/S1359-6454(98)00336-X
[9] X.Z. Li, J.J. Guo, Y.Q. Su, S.P. Wu, H.Z. Fu, Acta Metall. Sin. 41, 593(2005). (in Chinese)
[10] J.J. Guo, X.Z. Li, Y.Q. Su, S.P. Wu, H.Z. Fu, Acta Metall. Sin. 41, 599(2005). (in Chinese)
[11] A. Karma, W.J. Rappel, B.C. Fuh, R. Trivedi, Metall. Mater. Trans. A 29, 1457(1998)10.1007/s11661-998-0361-1
[12] P. Mazumder, R. Trivedi, Phys. Rev. Lett. 88, 235507(2002)10.1103/PhysRevLett.88.235507
[13] S. Liu, R. Trivedi, Metall. Mater. Trans. A 37, 3293(2006)10.1007/BF02586164
[14] L.S. Wang, J. Shen, Z. Shang, L. Wang, H.Z. Fu, Acta Metall. Sin. 49, 822(2013). (in Chinese)
[15] H.Q. Hu, The Principle of Melt Solidification(China Machine Press, Beijing, 2000), PP. 111–118. (in Chinese)
[16] H. Yasuda, N. Notake, K. Tokieda, I. Ohnaka, J. Cryst. Growth 210, 637(2000)10.1016/S0022-0248(99)00760-5
[17] R. Trivedi, J.S. Park, J. Cryst. Growth 235, 572(2002)10.1016/S0022-0248(01)01803-6
[18] D. Ma, Y. Li, S.C. Ng, J. Cryst. Growth 219, 300(2000)10.1016/S0022-0248(00)00622-9
[19] J. Dutkiewicz, L. Zabdyr, Z. Moser, J. Salawa, J. Phase. Equil. 10, 223(1989)
[20] L. Wang, J. Shen, L. Qin, Z.R. Feng, L.S. Wang, H.Z. Fu, J. Cryst. Growth 356, 26(2012)10.1016/j.jcrysgro.2012.07.014
[21] M. Hillert, Solidification and Casting of Metals(The Metals Society, London, 1979), p. 242
[22] L.S. Wang, J. Shen, Z.R. Feng, H.Z. Fu, Appl. Phys. A 113, 177(2013)10.1007/s00339-012-7510-5
[23] F. Kohler, L. Germond, J.D. Wagnière, M. Rappaz, Acta Mater. 57, 56(2009)10.1016/j.actamat.2008.08.058
[24] M. Rappaz, F. Kohler, J. Valloton, A.B. Phillion, M. Stampanoni, Metall. Mater. Trans. A 41, 563(2010)10.1007/s11661-009-0118-5
[25] R. Trivedi, Scr. Mater. 53, 47(2005)10.1016/j.scriptamat.2005.03.019
Options
Outlines

/