Acta Metallurgica Sinica (English Letters) >
Influence of Mg Contents on Aging Precipitation Behavior of Al–3.5Cu–xMg Alloy
Received date: 2013-05-20
Revised date: 2013-11-01
Online published: 2014-03-11
The influence of Mg content on the microstructures and mechanical properties at room temperatures of Al–3.5Cu–(0.71–1.81)Mg alloys was studied. Precipitation phases in the alloys were identified by TEM and HRTEM. The results show that when Mg contents increase from 0.71 to 1.81 wt%, the precipitates are transformed from S, S″, Ω, and θ′ phases to S and S″ phases, and Ω phase is first observed in Al–3.48Cu–0.71 Mg alloy with Cu/Mg mass ratio of 5 during the conventional aging heat treatment (190 °C/12 h). Regard to aging hardness effect of the tested alloys, the hardness of the alloys improves with the increase of Mg content, but the increases become slow when Mg content is greater than 1.35 wt%.
Key words： Al–Cu–Mg alloy; Mechanical property; Microstructure; Phase transition
Siyu Li , Jin Zhang , Jinlong Yang , Yunlai Deng , Xinming Zhang . Influence of Mg Contents on Aging Precipitation Behavior of Al–3.5Cu–xMg Alloy[J]. Acta Metallurgica Sinica (English Letters), 2014 , 27(1) : 107 -114 . DOI: 10.1007/s40195-014-0033-7
| [1] | T. Masumoto, Mater. Sci. Eng. A 179, 8(1994)10.1016/0921-5093(94)90155-4 |
| [2] | D.A. Lukasak, R.M. Hart, Light Met. Age 49, 11(1991) |
| [3] | S.P. Ringer, T. Sakural, I.J. Polmear, Acta Mater. 45, 3732(1997)10.1016/S1359-6454(97)00039-6 |
| [4] | S.C. Wang, M.J. Starink, Int. Mater. Rev. 50, 193(2005)10.1179/174328005X14357 |
| [5] | S.C. Wang, M.J. Starink, Mater. Sci. Eng. A 386, 156(2004)10.1016/j.msea.2004.07.006 |
| [6] | K.M. Knowles, W.M. Stobbs, Acta Cryst. B 44, 207(1988)10.1107/S0108768187012308 |
| [7] | H. Perlitz, A. Westgren, Arkiv. Kemi. Mineral. Geol. 16B, 13(1943) |
| [8] | J.M. Silcock, T.J. Heal, H.K. Hardy, J. Inst. Met. 82, 239(1953) |
| [9] | L. Kovarik, P.I. Gouma, C. Kisielowski, S.A. Court, M.J. Mills, Acta Mater. 52, 2509(2004)10.1016/j.actamat.2004.01.041 |
| [10] | A. Charai, T. Walther, C. Alfonso, A.M. Zahra, C.Y. Zahra, Acta Mater. 48, 2751(2000)10.1016/S1359-6454(99)00422-X |
| [11] | S.C. Wang, M.J. Starink, Acta Mater. 55, 933(2007)10.1016/j.actamat.2006.09.015 |
| [12] | M. Gazizov, R. Kaibyshev, J. Alloys Compd. 527, 163(2012)10.1016/j.jallcom.2012.02.144 |
| [13] | O. Novelo-Peralta, I.A. Figueroa, G. Lara-Rodríguea, G. González, Mater. Chem. Phys. 130, 431(2011)10.1016/j.matchemphys.2011.07.004 |
| [14] | K. Hono, Acta Metall. Mater. 41, 829(1993)10.1016/0956-7151(93)90016-L |
| [15] | A. Garg, Y.C. Chang, J.M. Howe, Scr. Metall. Mater. 24, 677(1990)10.1016/0956-716X(90)90222-3 |
| [16] | L.M. Wang, H.M. Flower, T.C. Lindley, Scr. Mater. 41, 391(1999)10.1016/S1359-6462(99)00150-5 |
| [17] | S.C. Wang, M.J. Starink, N. Gao, Scr. Mater. 54, 287(2006)10.1016/j.scriptamat.2005.09.010 |
| [18] | A. Garg, Y.C. Chang, J.M. Howe, Scr. Metall. 24, 677(1990)10.1016/0956-716X(90)90222-3 |
| [19] | N. ünlü, B.M. Gable, G.J. Shiflet, E.A. Starke Jr, Metall. Mater. Trans. A 34, 2757(2003)10.1007/s11661-003-0177-y |
| [20] | J.L. Cai, D.Q. Yi, H.W. Wang, B. Wang, Chin. J. Nonferr. Met. 21, 1504(2011). (in Chinese) |
/
| 〈 |
|
〉 |
WeChat