Mechanical and Electrical Properties of the Ternary Ag–Sb–Zn System
Received date: 2013-05-08
Revised date: 2013-07-25
Online published: 2014-03-11
This paper presents comparative review of experimental and thermodynamic assessment of ternary Ag–Sb–Zn system. Isothermal section of the Ag–Sb–Zn system at 300 °C has been calculated by CALPHAD method using thermodynamic parameters from literature. Microstructural analysis of a number of alloys was carried out by scanning electron microscopy and optical microscopy, whereas chemical composition of observed phases was analyzed using energy-dispersive X-ray spectroscopy. Hardness of selected alloys from four vertical sections was determined using Brinell hardness test and additionally by micro Vickers hardness test. Electrical conductivity of a number of alloys in the ternary Ag–Sb–Zn system was experimentally determined. Good overall agreement between experimental and calculated values was obtained.
M. Premović , D. Minić , D. Manasijević , Vladan Ćosović , D. Živković , I. Dervišević , N. Talijan . Mechanical and Electrical Properties of the Ternary Ag–Sb–Zn System[J]. Acta Metallurgica Sinica (English Letters), 2014 , 27(1) : 47 -54 . DOI: 10.1007/s40195-013-0016-0
| [1] | V. Buchtovà, D. ?ivkovi?, J. Vre?tàl, D. Manasijevi?, A. Kroupa, Monatsh. Chem. 136, 1939(2005)10.1007/s00706-005-0383-y |
| [2] | I. Krastev, A. Zielonka, J. Appl. Electrochem. 32(10), 1141(2002)10.1023/A%3A1021284719851 |
| [3] | C. Xu, D. Yi, C. Wu, H. Liu, W. Li, Mater. Sci. Eng., A 538, 202(2012)10.1016/j.msea.2012.01.031 |
| [4] | H.-J. Wu, S.-W. Chen, Acta Mater. 59, 6463(2011)10.1016/j.actamat.2011.07.010 |
| [5] | D. Jendrzejczyk-Handzlik, D. ?ivkovi?, W. Gierlotka, D. Manasijevi?, K. Fitzner, D. Mini?, J. Min. Metall. B 43(2), 161(2007)10.2298/JMMB0702161J |
| [6] | Z.H. Long, S.X. Zhou, H.S. Liu, Z.P. Jin, Thermochim. Acta 498(1–2), 22(2010)10.1016/j.tca.2009.09.006 |
| [7] | J. Liu, C. Guo, C. Li, Z. Du, Thermochim. Acta 539, 44(2012)10.1016/j.tca.2012.03.026 |
| [8] | D. ?ivkovi?, D. Mini?, D. Manasijevi?, J. ?estak,?. ?ivkovi?, J. Min. Metall. B 47(1), 23(2011)10.2298/JMMB1101023Z |
| [9] | V. ?osovi?, N. Talijan, D. ?ivkovi?, D. Mini?,?. ?ivkovi?, J. Min. Metall. B 48(1), 131(2012)10.2298/JMMB111101013C |
| [10] | M. Peng, Z. Qiao, A. Mlkula, CALPHAD 20(1), 69(1996)10.1016/0364-5916(96)00013-2 |
| [11] | R. Schmid Fetzer,Ternary Alloys, vol. 2(VCH-Verlagsgesellschaft, Weinheim, 1988), pp. 556–557 |
| [12] | A. Mikula, Metall. Trans. B 23, 601(1992)10.1007/BF02649720 |
| [13] | F. Kohler, Monatsh. Chem. 91, 738(1960)10.1007/BF00899814 |
| [14] | C. Colinet,Dissertation, University of Grenoble, France, 1967 |
| [15] | M. Hillert, CALPHAD 4(1), 1(1980)10.1016/0364-5916(80)90016-4 |
| [16] | G.W. Toop, Trans. Met. Soc. AIME 233, 850(1965) |
| [17] | N. Saunders, A.P. Miodownik,CALPHAD,(A Comprehensive Guide), 1998) |
| [18] | H.L. Lukas, S.G. Fries, B. Sundman,Computational Thermodynamics: CALPHAD Method (Cambridge University Press, Cambridge, 2007)10.1017/CBO9780511804137 |
| 19 | A.T. Dinsdale, A. Kroupa, J. Vizdal, J. Vrestal, A. Watson, A. Zemanova (eds.),COST 531 Database for Lead-Free Solders, vol. 1 (COST Office, Belgium, 2008) |
| [20] | A.T. Dinsdale,SGTE Unary Database, Version 4.4.(2002), . Accessed 12 March 2013 |
/
| 〈 |
|
〉 |
WeChat