Crystal Structure Evolution of the Cu-rich Nano Precipitates from bcc to 9R in Reactor Pressure Vessel Model Steel
Received date: 2013-03-26
Revised date: 2013-07-01
Online published: 2014-02-28
Supported by
National Basic Research Program of China (No. 2011CB610503), the National Natural Science Foundation of China (No.50931003) and Ministry of Major Subject of Shanghai (No.S30107)
The crystal structure evolution of the Cu-rich nano precipitates from bcc to 9R during thermal aging was studied in nuclear reactor pressure vessel (RPV) model steels. The specimens, contained higher copper and nickel contents than commercially available one, were heated at 890℃ for 0.5 h and then water quenched followed by tempering at 660℃ for 10 h and aging at 400℃ for 1000 h. It was observed that bcc and 9R orthogonal structure, as well as 9R orthogonal and 9R monoclinic structure, coexist in a single Cu-rich nano precipitate. Further analyses pointed out that Cu-rich nano precipitates of bcc structure were not stable, it may preferentially transform to 9R orthogonal structure and then to 9R monoclinic structure. This results showed that the crystal structure evolution of the Cu-rich nano precipitates was complex.
Liu FENG , Bangxin ZHOU , Jianchao PENG , Junan WANG . Crystal Structure Evolution of the Cu-rich Nano Precipitates from bcc to 9R in Reactor Pressure Vessel Model Steel[J]. Acta Metallurgica Sinica (English Letters), 2013 , 26(6) : 707 -712 . DOI: 10.1007/s40195-013-0170-4
[1]P.D. Styman, J.M. Hyde, K. Wilford and A. Morley, Prog.Nucl. Energy 57 (2012) 86.
[2]T. Toyama, Y. Nagai, Z. Tang and M. Hasegawa, Acta Mater. 55 (2007) 6852.
[3]M.K. Miller, R.K. Nanstad, M.A. Sokolov and K.F.Russell, J. Nucl. Mater. 351 (2006) 216.
[4]R.P. Kolli, R.M. Wojes, S. Zaucha and D.N. Seidman,Int. J. Mater. Res. 99(2008) 513.
[5]R.P. Kolli and D.N. Seidman, Acta Mater. 56 (2008) 2073.
[6] C. Zhang, M. Enomoto, T. Yamashita and N. Sano, Metall.Mater. Trans. A 35(2004) 1263.
[7]E. Hornbogen and R.C. Glen, Trans. Metall. Soc. AIME. 218(1960) 1061.
[8]D. Molnar, R. Mukherjee, A. Choudhury and A. Mora, Acta Mater. 60(2012) 6961.
[9]P. Grammatikopoulos, D.J. Bacon and Y.N. Osetsky, Model.Simul. Mater. Sci. Eng. 19(2011) 1.
[10]J.B. Yang, T. Yamashita, N. Sano and M. Enomoto,Mater. Sci. Eng. A. 487 (2008) 128.
[11]A. Deschamps, M. Militzer and W.J. Poole, ISIJ Int. 41(2001) 196.
[12]Y. Kamada, S. Takahashi, H. Kikuchi and S. Kobayashi,J. Mater. Sci. 44(2009) 949.
[13]A. Ghosh, B. Mishra, S. Das and S. Chatterjee, Metall.Mater. Trans. A 36(2005) 703.
[14]A. Ghosh and S. Chatterjee, Mater. Charct. 55(2005) 298.
[15]H. Nakamichi, K. Yamada and K. Sato, J. Microsc. 242(2011) 55.
[16]V.N. Urtseva, D.A. Mirzaevb, I.L. Yakovlevac and N.A.Tereshchenkoc, Phys. Met. Metall. 110(2010) 346.
[17]J.J. Blackstock and G.J. Ackland, Philos. Mag. A 81(2001) 2127.
[18] S.L. Perez, M.L. Jenkins and J.M. Titchmarsh, Philos.Mag. Lett. 86(2006) 367.
[19]W. Wang, B.X. Zhou, G. Xu and D.F. Chu, Mater. Charact.62(2011) 438.
[20]Y.U. Heo, Y.K. Kimb, J.S. Kim and J.K. Kim, Acta Mater. 61(2013) 519.
[21]G. Xu, D.F. Chu, L.L. Cai, B.X. Zhou and W. Wang, Acta Metall. Sin. 47 (2011) 905. (in Chinese)
[22]P.J. Othen, M.L. Jenkins, G.D.W. Smith and W.J.Phythian, Philos. Mag. Lett. 64 (1991) 383.
[23]T.H. Lee, Y.O. Kim and S.J. Kim, Philos. Mag. A87(2007) 209.
[24]Y.L. Bouar, Acta Mater. 49 (2001) 2661.
[25]H.R. Habibi-bajguir and M.L. Jenkins, Philos. Mag. Lett. 73(1996) 155.
[26]P.J. Othen, M.L. Jenkins and G.D.W. Smith, Philos. Mag.A70(1994) 1.
[27]R. Monzen, M.L. Jenkins and A.P. Sutton, Philos. Mag.A80(2000) 711.
/
| 〈 |
|
〉 |
WeChat