Corrosion Behavior and Biocompatibility of Hydroxyapatite Coating on H2SO4 Passivated 316L SS for Human Body Implant
Received date: 2012-11-12
Revised date: 2013-04-12
Online published: 2013-07-11
The aim of this studies at simultaneous improvement of the corrosion behavior and biocompatibility of metallic implant and bone Osseointegration simultaneously. Stainless steel 316L (SS) was used as metallic substrate and after surface treatment with 15 vol.% sulfuric acid, it was coated with hydroxyapatite coating employing plasma-spraying process. Structure characterization techniques including XRD, SEM and EDX were also utilized to investigate the microstructure, morphology, and crystallinity of the coating. Electrochemical potentiodynamic tests were performed in two types of physiological solutions in order to determine and compare the corrosion resistance behavior of the coated and uncoated specimens as an indication of biocompatibility.
The results indicate that the surface treatment and hydroxyapatite coating improve the corrosion resistance behavior of SS. The corrosion current density of the surface treated and the hydroxyapatite coated SS also decrease. These also show that surface treated and hydroxyapatite coated SS can be used as human body implants with the goals of corrosion resistance improvement (biocompatibility) and bone osseointegration.
Ali Parsapour , Saied Nouri Khorasani , Mohammad Hossein Fathi . Corrosion Behavior and Biocompatibility of Hydroxyapatite Coating on H2SO4 Passivated 316L SS for Human Body Implant[J]. Acta Metallurgica Sinica (English Letters), 2013 , 26(4) : 409 -415 . DOI: 10.1007/s40195-012-0212-3
[1]S. Nagarajan and N. Rajendran, Appl. Surf. Sci.255(2009) 3927
[2]D. Sharan, The Problem of Corrosion in Orthopedic Implant Materials, Orthopedic Update, India, 1999, Vol. 9, pp.1-5.
[3]H. Takao, Mater. Sci. Eng. 267(1999)260.
[4]R. Venugopalan and J. Gaydon, A Review of Corrosion Behavior of Surgical Implant Alloys, Department of Biomedical Engineering, University of Alabama at Birmingham.
[5]D.F. Williams, Definitions in Biomaterials, Proceeding of a Consensus Conference of the European Society for Biomaterials,England, 1986, p.4.
[6]R.Venugopalan and C. Trepanier, Min. Invas. Ther. & Allied Technol.9(2000)67.
[7]Y. Okazaki and E. Gotoh, Biomaterials 26(2005)11.
[8]E. Leitao, R.A. Silva and M.A. Barbosa, Mater. Sci.8(1997)365.
[9]S.R. Sousa and M.A. Barbosa, Mater. Sci.2(1991)19.
[10]M.H. Fathi, S.B. Moosavi and V. Mortazavi, Dent. Res.J.1(2003)36.
[11]T. Urs, I. Uggowitzer and J. Peter, Wear239 (2000) 48.
[12]K.H.W. Seah and X. Chen, J. Mater. Sci.8(1993) 1841.
[13]S. Kannan, A. Balamurugan and S. Rajeswari,Electrochem. Acta49(2004) 2395.
[14]S. Herts, Passivation Stainless Steel by Anselm Kuhn Metal Finishing Information Services Ltd., U.K. Metal Finishing,1998, pp.100-105.
[15]C. Shih, C.M. Shi, Y. Su, M.S. Chang and S.J. Lin,Corros. Sci.46(2004) 427.
[16] L.P. Ward, K.N. Strafford, T.P. Wilks and C.Subramanian, J. Mater. Process. Technol.56(1996) 364.
[17]ASTM F86: Standard Recommended Practice for surface preparation and marking of Metallic Surgical Implant In: Medical Device and Services, PA: American Society for Testing and Materials, 1998, 13.01, pp.7-9.
[18]M.H. Fathi, V. Mortazavi and S.B. Moosavi, Designing, Preparing and Evaluation of Novel HA/Ti Composite Coating for Endodontic Dental Implant, J. Dentistry. Tehran University of Medical Science, 2002, 15.
[19]J.M. Bastidas, C.L. Torres, E. Cano and J.L. Polo,Corros. Sci.44(2002) 625.
[20]S. Nagarajan, V. Raman and N. Rajendran, Mater. Chem.Phys.119(2010) 363.
[21]F.S. Shieu, M.J. Deng and S.H. Lin, Corros. Sci.40(1998) 1267.
[22]S. Kannan, A. Balamurugan and S. Rajeswari,Electrochem. Acta49(2004) 2395.
[23]M.A. Baker and J.E. Castle, Corros. Sci.35(1993) 667.
[24]P. Marcus, Corros. Sci.36(1994) 2155.
[25]ASTM G5: Standard Reference Test Method for making Potentiostaic and Potentiodynamic Anodic Polarization Measurements In; metals, Test Methods and Analytical procedures, Philadelphia, PA: American Society for Testing and Materials, 1995, 03.02, pp.48-58.
[26]L.L. Hench and J. Wilson, An Introduction to Bioceramics, World Scientific, London, 1993, pp.23-59.
[27]C. Guzman Vazquez, C. Pina Barba and N. Munguia, Revista Mexicana Fisica51(2005) 284.
[28]W. Suchanek and M. Yoshimura, J. Mater. Res.13 (1989) 94.
[29]U. Bismayer, J. Shi, A. Klocke, S. Gierlotka and B.Palosz, Key Eng. Mater.288-289(2005) 561.
[30] K. Bordji, J.Y. Jouzeau, D. Mainard, E. Payan and P.Netter, Biomaterials17(1996) 491.
[31] E. Park, R.A. Condrate, D. Lee, K. Kociba and P.K.Gallagher, J. Mater. Sci: Med13(2002) 211.
[32]K.T. Oh and Y.S. Park, Surf. Coat. Technol.110(1998) 4.
[33] M.C.P. Ereira, M.L. Pereira and J.P. Sousa, Biomaterials 20(1999) 2193.
[34] M.H. Fathi, M. Salehi, A. Saatchi, V. Mortazavi and S.B.Moosavi, Dent. Mater.19(2003)188.
/
| 〈 |
|
〉 |
WeChat