Effect of Direct Quenching on Microstructure and Mechanical Properties of a Wear-resistant Steel
Received date: 2012-10-21
Revised date: 2013-03-24
Online published: 2013-07-11
Supported by
National Natural Science Foundation of China (Nos. 51074052 and 51004035).
A wear-resistant steel was hot rolled at the same finish temperature, and subsequently treated with conventional reheat quenching and tempering process (RQ&T) and direct quenching and tempering process (DQ&T), respectively. The effect of direct quenching on the microstructure and mechanical properties was investigated in detail by using optical microscope, transmission electron microscope and scanning electron microscope equipped with electron backscattered diffraction. The results showed that the microstructures of both the RQ and DQ specimens were complex constituents of lath martensite and lower bainite. Compared with the RQ specimen, the lower bainite content in DQ specimen was much higher. Furthermore, the bainite in the DQ specimen extended into and segmented the prior austenite grains, which can decrease martensite packet size. The proportion of high-angle boundary in the DQ specimen was higher than that in the RQ specimen, which may improve the impact toughness. The carbides in DQ&T specimen were much finer and distributed even dispersively because direct quenching can retain substantive defects which may provide more nucleation sites for carbide precipitation in the tempering process. Besides, the mechanical properties of DQ and DQ&T specimens were superior than those subjected to RQ and RQ&T processes, respectively.
Key words： Direct quenching; Temper; Lower bainite; Martensite packet; Mechanical properties
Hongyu SONG , Shunhu ZHANG , Liangyun LAN , Canming LI , Haitao LIU , Dewen ZHAO , Guodong WANG . Effect of Direct Quenching on Microstructure and Mechanical Properties of a Wear-resistant Steel[J]. Acta Metallurgica Sinica (English Letters), 2013 , 26(4) : 390 -398 . DOI: 10.1007/s40195-012-0183-4
[1]K.S. Luo and B.Z. Bai, Mater. Des. 31 (2010)2510.
[2]Z.Q. Jiang, J.M. Du and X.L. Feng, J. Iron Steel Res.Int. 13(1) (2006) 57.
[3]M.X. Wei, S.Q. Wang, L. Wang and K. Chen, J. Iron Steel Res. Int.18(10) (2011) 47.
[4]S.K. Dhua and S.K. Sen, Mater. Sci. Eng. A 528 (2011) 6356.
[5]F.B. Pickering, Proc. Int. Conf. on HSLA Steels Technology & Applications, Philadelphia, Pennsylvania, 3-6 Oct.,1983.
[6]T. Tanaka, Proc. of Int. Conf. on High Strength Low Alloy Steels, Wollongon, Australia, 1984.
[7]N. Shikanai and M. Suga, Proc. Symp. on Physical Metallurgy of Direct-Quenched Steels, Chicago, Illinois, 2-4 Nov,1992.
[8]S.K. Dhua, D. Mukerjee and D.S. Sarma, Metall. Mater.Trans. A 34 (2003) 241.
[9]Y.L. Zhao, J. Shi, W.Q. Cao, M.Q. Wang and G. Xie, J.Zhejiang Univ. Sci. A (Appl. Phys. Eng.) 11 (2010) 776.
[10]R.K. Weiss and S.W. Thompson, Proceedings of the Symposium on Physical Metallurgy of Direct-quenched Steels,Warrendale, USA, 1992.
[11]T. Abe, M. Kurihara, H. Tagawa and K. Tsukada, Trans.Iron. Steel. Inst. Jpn. 27 (1987) 478.
[12]M. Fujioka, A.Yoshie, Y. Onoe and K. Okamoto, Speich.Symp. Proc., Montreal, Quebec, Canada, 25-28 Oct, 1992.
[13]Y.J. Song, J.T. Lu, J.H. Liu, L. Shen, Q.C. Rao and H.J.Zhou, Trans. Met. Heat Treatment 3(1) (1982) 11. (in Chinese)
[14]Z. Guo, C.S. Lee and J.W. Morris, Acta Mater. 52(2004) 5511.
[15]Reza, A. Lara and R. Reed-Hill, Physical Metallurgy Principles, CENGAGE Learning, Stamford, 2009, p.700.
[16]J. Qiu, X. Ju, Y. Xin, S. Liu, Y.L. Wang, H.B. Wu and D. Tang, J. Nucl. Mater. 407 (2010) 189.
[17]Y.J. Guo and J.F. Huang, Trans. Met. Heat Treatment 12(1) (1991) 8. (in Chinese)
[18]C. Ouchi, ISIJ 41(5) (2001) 42.
[19]L.L. Yun, CH.L. Qiu, P. Zhou, D.W. Zhao, C.M. Li, X.H.Gao and L.X. Du, Acta Metall. Sin. (Engl. Lett.) 24 (2011)473.
[20]A.M. Guo, R.D.K. Misra, J.B. Liu, L. Chen, X.L. He and S.J. Jansto, Mater. Sci. Eng. A 527 (2010) 6440.
[21]M. Diaz-Fuentes, A. Iza-Mendia and I. Gutierrez, Metall.Mater. Trans. A 34 (2003) 2505.
[22]G. Miyamoto, N. Iwata, N. Takayama and T. Furuhara, Acta Mater. 58 (2010) 6393.
[23]S. Morito, I. Kishida and T. Maki. J. Phys. IV France 112 (2003) 453.
[24] G. Krauss, Mater. Sci. Eng. A 273-275 (1999)40.
[25]L.G. Hu and X.W. Xie, Heat Treatment of Steels, Northwestern Polytechnical Press, Xi'an, 2004, p.169 (in Chinese).
[26]R.H. Aborn, Trans. ASM 48 (1956) 51.
[27]T. Swarr and G. Krauss, Metall. Mater. Trans. A 7 (1976) 41.
[28]S.K. Das and G. Thomas, Metall. Mater. Trans. B 1 (1970) 325.
[29]G.R. Speich and W.C. LesLie, Metall. Mater. Trans. B3 (1972) 1043.
[30]E. Rabinowicz, L.A. Dunn and P.G. Russel, Wear 4 (1961) 345.
[31]H. Liebowitz, Fracture, New York and London Academic Press, 1969.
[32]G.C. Hwang, S. Lee, J.Y. Yoo and W.Y. Choo, Mater. Sci.Eng. A 252 (1998) 256.
[33]B. Ouchi, Iron Steel Inst. Jpn. Int. 41 (2001)542.
[34]H.J. Zhou, Y.J. Li and J.Y. Qi, International Congress on Heat Treatment of Materials, Shanghai, China, 1983.
[35]J.Y. Qi, Y.L. Li and H.J. Zhou, J. Xi'an Jiaotong Univ.18 (1984)9.
/
| 〈 |
|
〉 |
WeChat