Optimizing Mechanical Properties of AlCoCrFeNiTix High-Entropy Alloys by Tailoring Microstructures
Received date: 2012-10-15
Revised date: 2012-12-28
Online published: 2013-05-06
Supported by
National Natural Science Foundation of China (No. 51101110), the Youth Science Foundation of Shanxi Province, China (No.~2012021018-1), Research Project Supported by Shanxi Scholarship Council of China (No. 2012-032) and State Key Lab of Advanced Metals and Materials (Grant No. 2011-Z06).
The effects of Ti additions and the heat treatment on the mechanical properties of AlCoCrFeNiTix (x = 0, 0.2, 0.3, 0.4 and 0.5) high-entropy alloys (HEAs) were studied. The results show that the dendrite phase with a body-centered-cubic (bcc) structure transforms into the interdendrite phase with a new bcc structure. With the increase of the Ti contents and heat-treatment temperature, the average hardness and yield strengths are greatly improved, and the highest hardness and yielding strength are 583 HV and 2.07 GPa, respectively in the investigated HEA system. The as-cast and annealed HEAs exhibit excellent mechanical properties, combining with high yielding strength and plasticity. The solid solution strengthening mechanism of Ti additions is responsible for the strengthening effect of AlCoCrFeNiTix HEAs.
Key words： High-entropy alloy; Microstructure; Compressive property; Hardness; Heat treatment
Yinfeng WANG , Shengguo MA , Xiaohua CHEN , Juyan SHI , Yong ZHANG , Junwei QIAO . Optimizing Mechanical Properties of AlCoCrFeNiTix High-Entropy Alloys by Tailoring Microstructures[J]. Acta Metallurgica Sinica (English Letters), 2013 , 26(3) : 277 -284 . DOI: 10.1007/s40195-012-0174-5
[1] J.W. Yeh, S.K. Chen, S.J. Lin, J.Y. Gan, T.S. Chin, T.T. Shun, C.H. Tsau and S.Y. Chang, Adv. Eng. Mater. 6 (2004)299.
[2] J.M. Zhu, H.F. Zhang, H.M. Fu, A.M. Wang, H. Li and Z.Q. Hu, J. Alloys Compd. 497 (2010) 52.
[3] K.B. Zhang, Z.Y. Fu, J.Y. Zhang, W.M. Wang, H. Wang, Y.C. Wang, Q.J. Zhang and J. Shi, Mater. Sci. Eng. A 508 (2009)214.
[4] Y. Zhang, S.G. Ma and J.W. Qiao, Metall. Mater. Trans. A 43 (2012) 2625.
[5] Y.J. Zhou, Y. Zhang, Y.L. Wang and G.L. Chen, Mater. Sci.Eng. A 454-455 (2007) 260.
[6] Y.P. Wang, B.S. Li, M.X. Ren, C. Yang and H.Z. Fu, Mater.Sci. Eng. A 491 (2008) 154.
[7] T.T. Shun and Y.C. Du, J. Alloys Compd. 479 (2009) 157.
[8] J.M. Zhu, H.M. Fu, H.F. Zhang, A.M. Wang, H. Li and Z.Q. Hu, Mater. Sci. Eng. A 527 (2010) 7210.
[9] J.W. Qiao, S.G. Ma, E.W. Huang, C.P. Chuang, P.K. Liaw and Y. Zhang, Mater. Sci. Forum. 688 (2011) 419.
[10] Y.J. Zhou, Y. Zhang, Y.L. Wang and G.L. Chen, Appl. Phys.Lett. 90 (2007) 181904.
[11] C.M. Lin, H.L. Tsai and H.Y. Bor, Intermetallics 18(2010) 1244.
[12] S. Ranganathan, Curr. Sci. 8 (2003) 1404.
[13] C.J. Tong, Y.L. Chen, S.K. Chen, J.W. Yeh, T.T. Shun, C.H. Tsau, S.J. Lin and S.Y. Chang, Metall. Mater. Trans. A 36(2005) 881.
[14] A. Takeuchi and A. Inoue, Mater. Trans. 46 (2005) 2817.
[15] F.R. Doer, R. Boom, W.C.M. Mattens, A.R. Miedema and A.K.Niessen, Cohesion in Metals, 2nd ed., North-Holland Physics Publishing, Netherlands, 1988.
[16] C.M. Lin and H.L. Tsai, Intermetallics 19 (2011) 288.
[17] W.R. Wang, W.L. Wang, S.C. Wang, Y.C. Tsai, C.H. Lai and J.W. Yeh, Intermetallics 26 (2012) 44.
[18] Y. Zhang, Y.J. Zhou, J.P. Lin, G.L. Chen and P.K. Liaw,Adv. Eng. Mater. 10 (2008) 534.
[19] S.S. Fang, X.S. Xiao, L. Xia, W.H. Li and Y.D. Dong, J.Non-Cryst. Solids 321 (2003) 120.
[20] C. Kittel, Int. to Solid State Phys. 6th ed, John Wiley & Songs. Inc, New York, 1980, p.26.
[21] O.E. Sebaie, A.M. Samuel, F.H. Samuel and H.W. Doty,Mater. Sci. Eng. A 486 (2008) 241.
[22] C. Ng, S. Guo, J.H. Luan, S.Q. Shi and C.T. Liu,Intermetallics, 31(2012) 165.
[23] J. Rosler, H. Harders and M. Baker, Mechanical Behaviour of Engineering Materials, Springer Berlin Heidelberg, New York, 2007.
[24] A. Inoue, Mater. Sci. Eng. A 304--306 (2001) 1.
[25] J.W. Qiao, S. Wang, Y. Zhang, P.K. Liaw and G.L. Chen,Appl. Phys. Lett. 94 (2009) 151905.
[26] Y. Zhang, X. Yang and P.K. Liaw, JOM 64 (2012)830.
[27] C.Y. Hsu, C.C. Juan, W.R. Wang, T.S. Sheu, J.W. Yeh and S.K. Chen, Mater. Sci. Eng. A 528 (2011) 3581.
[28] J.W. Qiao, Y. Zhang and P.K. Liaw, Adv. Eng. Mater. 10(2008) 1039.
/
| 〈 |
|
〉 |
WeChat