Pitting Corrosion of 13Cr Steel in Oxygen-free Completion Fluids of Organic Salt
Received date: 2012-12-31
Revised date: 2013-03-04
Online published: 2013-05-06
Supported by
National Science & Technology Pillar Program(No. 2012BAK13B04)
Corrosion behavior of 13Cr steel in oxygen-free completion fluids of the organic salt at 180℃ was studied. Cross-sectional morphologies of the corrosion products were observed by scanning electron microscopy. Energy dispersive spectrum (EDS) was used to study the element distribution of the corrosion product inside and outside the pits. The results show that the organic salt causes severe pitting corrosion of 13Cr steel. The width and depth of the pits increase simultaneously when the test duration prolongs, and potassium enriches inside the pits.
Key words： 13Cr steel; Pitting corrosion; Organic salt; Completion fluids
Lining XU , Yao MENG , Yunguang SHI , Yan LIU . Pitting Corrosion of 13Cr Steel in Oxygen-free Completion Fluids of Organic Salt[J]. Acta Metallurgica Sinica (English Letters), 2013 , 26(3) : 271 -276 . DOI: 10.1007/s40195-012-0283-1
[1] M.A. Simpson, S. Al-Reda, D. Foreman, J. Guzman and S.Aramco, in: the 40th Offshore Technology Conference,Houston, Texas, U. S., 4-7 May, 2009.
[2] J.D. Downs, in: the 17th Middle East Oil & Gas Show and Conference, Manama, Bahrain, 14-16 March, 2011.
[3] Z.Z. Yang, W. Tian and Q.R. Ma, Acta Metall. Sin. (Engl.Lett.) 21 (2008) 85.
[4] M.S. Ramsey, D.A. Texas, J.A. Shipp and B.J. Lang, in: SPE Annual Technology Conference, Denver, Colorado, 6-9 October, 1996.
[5] P. Guo, W. A. Gilchrist, J. Geoff Page, P. Wills and B.Atlas, in: the 43rd Annual Logging Symposium, Oiso, Japan,4-7 June, 2002.
[6] D. Bungert, S. Maikranz, R. Sundermann, J. Downs, W. Benton and M.A. Dick, in: IADC/SPE Drilling Conference, New Orleans, Louisiana, U. S., 2-4 February, 2000.
[7] M. Brangetto, C. Pasturel and M. Gregoire, Drill. Contractor 63(3) (2007) 108.
[8]M. Ueda and H. Takabe, in: NACE Corrosion Conference, Houston, Texas, U.S., 17-18 January, 1998.
[9] S. Hashizume, Y. Minami and Y. Ishizawa, in: NACE Corrosion Conference, Houston, Texas, U.S., 7-10 August , 1995.
[10]M.B. Kermani, G. Weighhill, T. Pendlington and G. Elliot, in: NACE Corrosion Conference, Houston, Texas, U.S., 7-10 August, 1995.
[11] R. Ebara, Mater. Sci. Eng. A 468-470 (2007) 109.
[12] R. Ebara, Proc. Eng. 2 (2010) 1297.
[13] S.I. Rokhlin, J.Y. Kim, H. Nagy and B. Zoofan, Eng. Fract. Mech. 62 (1999) 425.
[14] R.M. Schroeder and I.L. Muller, Mater. Corros. 60(2009) 365.
[15] Z.F. Yin, X.Z. Wang, L. Liu, J.Q. Wu, and Y.Q. Zhang, J.Mater. Eng. Perform. 20 (2011) 1330.
[16] O. Yevtushenko, R. Babler and A. Pfennig, Mater.Corros. 63 (2010) 517.
[17] G.X. Zhao, M. Zheng, X.H. Lu, X.H. Dong and H.L. Li,Met. Mater. Int. 11 (2005) 135.
[18] R.C. Newman, Corrosion 57 (2001) 1030.
[19] G.S. Frankel, Electrochem. Soc. 145 (1998) 2186.
/
| 〈 |
|
〉 |
WeChat