A composite coating was fabricated on pure magnesium by hydrothermal treatment in order to reduce its degradation in body environment. The coating was characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The XRD pattern showed that the main composition of the coating was a mixture of CaSiO3, MgSiO3 and Mg(OH)2. Electrochemical test showed that the corrosion current density Icorr of the coated magnesium was decreased by about two orders of magnitude compared with that of the bare magnesium, and the EIS measurement also showed that the corrosion resistant performance of the coated magnesium was significantly enhanced. Meanwhile, weight loss test showed that the weight loss of the coated magnesium was lower than that of the bare magnesium. Hence, the present study indicated that the composite coating could greatly slow down the degradation of pure magnesium.
Yanjin LU, Lili TAN, Hongliang XIANG, Bingchun ZHANG, Ke YANG
. Study on corrosion resistance of pure magnesium with CaSiO3 contained coating in NaCl solution[J]. Acta Metallurgica Sinica (English Letters), 2012
, 25(4)
: 287
-294
.
DOI: 10.11890/1006-7191-124-287
[1] T. Kraus, S.F. Fischerauer, A.C. Hanzi, P.J. Uggowitzer, J.F. Loffler and A.M. Weinberg, Acta Biomater 8 (2012) 1230
[2] N.T. Kirkland, N. Birbilis and M.P. Staiger, Acta Biomater 8 (2012) 925
[3] R.Willumeit, J. Fischer, F. Feyerabend, N. Hort, U. Bismayer, S.Heidrich and B. Mihailova, Acta Biomater 7 (2011) 2704
[4] M.B. Kannan and R.K.S. Raman, Biomater 29 (2008) 2306
[5] X. Gu, Biomater 30 (2009) 484
[6] L. Xu, F. Pan, G. Yu, L. Yang, E. Zhang and K. Yang, Biomater 30 (2009) 1512
[7] L. Choudhary and R. Singh Raman, Acta Biomater 2 (2012) 916
[8] S. Shadanbaz and G.J. Dias, Acta Biomater 8 (2012) 20
[9] H.S. Brar, J. Wong and M.V. Manuel, J Mech Behav Biomed Mater 7 (2012) 87
[10] X.N. Gu, N. Li, W.R.Zhou, Y.F. Zheng, X. Zhao, Q.Z. Cai and L. Ruan, Acta Biomater 7 (2011) 1880
[11] H. Wang, C. Zhao, Y. Chen, J. Li and X. Zhang, Mater Lett 68 (2012) 435
[12] F.Geng, L.L. Tan, X.X. Jin, J.Y. Yang and K. Yang, Mater Sci: Mater Med 20 (2009) 1149
[13] M. Tomozawa and S.Hiromoto, Acta Mater 59 (2011) 355
[14] E.M.Carlisle, Calcif Tissue Int 33 (1981) 27
[15] S.Cheng, D. Wei, Y. Zhou and H. Guo, Ceram Int 37 (2011)1761
[16] S. Ni, J. Chang and L. Chou, J Biomed Mater Res Part A 76 (2006) 196
[17] K. Lin, W. Zhai, S. Ni, J.Chang, Y. Zeng and W. Qian, Ceram Int 31 (2005) 323
[18] M. Tomozawa and S. Hiromoto, Appl Surf Sci 19 (2011) 8253
[19] Y. Zhu, G. Wu, Y.H. Zhang and Q. Zhao, Appl Surf Sci 257 (2011) 6129
[20] A. Yamamoto and S. Hiromoto, Mater Sci Eng C 29 (2009) 1559
[21] Y. Zong, G. Yuan, X. Zhang, L. Mao, J. Niu and W. Ding, Mater Sci Eng B 177 (2012) 395
[22] S.Y. Zhang, Q. Li, X.K. Yang, H.X. Zhang, S.Y. Wang and F. Liu, Mater Corros 62 (2011) 841
[23] M.C. Turhan, Q. Li, H. Jha, R.F.Singer and S. Virtanen, Electrochim Acta 56 (2011)7141
[24] Y. Liu, Z.L. Wei, F.W. Yang and Z. Zhang, J Alloy Compd 509 (2011) 6440
[25] H. Inoue, K. Sugahara, A.Yamamoto and H. Tsubakino, Corros Sci 44 (2002) 603
WeChat