A mathematic model of the solid fraction during rheo-casting by the cooling sloping plate process was established, and the effects of the process parameters on the solid fraction were analyzed. The calculation results show that the experimental result is approximately agreed with the calculation value. The effect of the casting temperature on the change rate of the solid fraction is not obvious. But the beginning solidification length is greatly influenced by the casting temperature. The beginning solidification length increases with the increment of the casting temperature. The effect of the sloping angle on the solid fraction becomes obvious with the increment of the sloping plate length. The solid fraction increases sharply with the decrease of the initial thickness of the melt. The melt initial thickness between 15 and 20 mm is suggested.
GUAN Ren-Guo
,
DIAO Tie-Yong
,
HUANG Hong-Qian
,
ZHANG Qiu-Sheng
,
DAI Chun-Guang
,
LIU Chun-Meng
. Mathematic model of solid fraction during rheo-casting by the cooling sloping plate process[J]. Acta Metallurgica Sinica (English Letters), 2012
, 25(1)
: 81
-88
.
DOI: 10.11890/1006-7191-121-81
[1] M.C. Flemings,Metall Trans A22 (1991) 957
[2] Z. Liu, Y.M. Hu and X.M. Liu,Acta Metall Sin (EnglLett)23(4)(2010) 277
[3] D. Brabazon, D.J. Browne and A.J. Carr,Mater Sci Eng A326(2002) 370
[4] M.A. Jaworski, T.K. Gray, M. Antonelli, J.J. Kim, C.Y.Lau, M.B. Lee, M.J. Neumann, W. Xu and D.N. Ruzic,Phys Rev Lett 104(094503)(2010) 1
[5] R. Haghayeghia, E.J. Zoquib, N.R. Greenc and H. Bahaia, J Alloy Compd502(2010) 382
[6] Z. Liu, W.M. Mao and X.M. Liu,Trans Nonferrous Met Soc China20(Suppl 3)(2010) 805
[7] Y. Zou, X.P. Dong, J. Zhang, Z.T. Fan and A.H. Wang, Foundry57(3)(2008) 215 (in Chinese)
[8] Q.F. Zhu, Z.H. Zhao, J.Z. Cui, X.J. Wang and K. Qin, Acta Metall Sin (Engl Lett)24(5)(2011) 399
[9] T. Motegi,Int J Mater Prod Technol2(2001)468
[10] Z. Wang, F.R. Cao, R.G. Guan, W.W. Wang and Z.Y. Zhao, Foundry60(5)(2011) 437 (in Chinese)
[11] T. Haga, K. Tkahashi, M. Ikawaand and H. Watari,J Mater Process Technol153-154(2004) 42
[12] P. Kapranos, D.H. Kirkwood, H.V. Atkinson, J.T.Rheinlander, J.J. Bentzen, P.T. Toft, C.P. Debel, G. Laslazc, L.Maenner, S. Blais, J.M. Rodriguez-Ibabe, L. Lasa, P. Giordano, G.Chiarmetta and A. Giese,J Mater Process Technol135(2-3) (2003) 271
[13] T. Grimmig, A. Ovcharov, C. Afrath, M. Bunck and A.Buhrig-Polaczek,Diffus Def Data Pt B116-117(2006) 484
[14] A.G. Dai, S.M. Xing and Y.F. He,Foundry55(3) (2006) 239 (in Chinese)
[15] W.H. Cai, X.J. Yang, H.M. Guo, R.J. Wei, Y. Zhang and H.C. He,J Nanchang Univ (Eng Technol Ed)25(3)(2003) 13 (in Chinese)
[16] F.G. Xie, R.G. Guan, C. Wang and X.H. Liu,Chin J Mater Res22(6)(2008) 639
[17] F.G. Xie, E.J. Zhao, R.G. Guan and X.H. Liu,Spec Cast Nonferrous Alloy(Suppl 1)(2008) 368 (in Chinese)
[18] S.M. Yang and W.Q. Tao,Heat Transfer(Higher Education Press, Beijing, 2006) p.140 (in Chinese)
[19] Q.Z. Le and J.Z. Cui,The Basic Principles of Transmission(Metallurgical Industry Press, Beijing, 2005) p.47(in Chinese)
[20] S.M. Yang,Fundamentals of Heat Transfer(Higher Education Press, Beijing, 2003) p.140 (in Chinese)
[21] E. Seheil,Z Metallkd34(1942) 70
WeChat