The radiation damage of 1Cr18Ni9Ti stainless steel and the Zr-Ti-Al alloy by 200 keV Xe+ ions bombardment at the fluence ranging from 1×1014 to 8×1015 ions/cm2 has been investigated by conventional transmission electron microscope, X-ray diffraction line profile analysis (XRDLPA) and nanoindentation. XRDLPA shows that the order of magnitude of dislocation density in both materials remains almost unchanged up to the highest irradiation dose. Selected-area electron diffraction combined with bright and dark field image indicates that 1Cr18Ni9Ti is more easily damaged than the Zr-Ti-Al alloy. With increasing the ions fluence, the radiation damage became more severe in 1Cr18Ni9Ti, accompanied with phase transition and partial amorphization. The nano-hardness was found to increase rapidly with increasing ion fluence till the dose of 1×1015 ions/cm2, and then gradually saturate with dose. The enhancement of hardness in irradiated materials is due to irradiation-induced defects acting as barriers to dislocation motion.
CI Mao-Sheng
,
LAI Wen-Sheng
,
LI Zheng-Cao
,
FENG Wei
. Radiation damage of 1Cr18Ni9Ti and Zr-Ti-Al alloys due to energetic particle irradiation[J]. Acta Metallurgica Sinica (English Letters), 2012
, 25(1)
: 29
-39
.
DOI: 10.11890/1006-7191-121-29
[1] D.N. Baker, Science 297(5586) (2002) 1486
[2] S. Parthiban, E. Elangovan, K. Ramamurthi, D. Kanjilal, K.Asokan, R. Martins and E. Fortunato, J Phys D Appl Phys 44(8) (2011) 0805404-1
[3] J.F. Ziegler, J.P. Biersack and U. Littmark, The Stopping and Range of Ions in Solids (Pergamon Press, New York,1985)
[4] R.A. Lula, Stainless Steel (American Society for Metals, Metals Park, OH, 1986) p.1
[5] K.H. Lo, C.H. Shek and J.K.L. Lai, Mater Sci Eng R 65(4-6) (2009) 39
[6] M. Oberndorfer, K. Thayer and M. Kastenbauer, Mater Corros 55(3) (2004) 174
[7] L. Vehovar and M. Tandler, Nucl Eng Des 206(1) (2001) 21
[8] S. Sahin and M. Ubeyli, J Fusion Energ 27(4) (2008) 271
[9] N. Hashimoto, T.S. Byun and K. Farrell, J Nucl Mater 351(1-3) (2006) 295
[10] T.S. Byun, N. Hashimoto, K. Farrell and E.H. Lee, J Nucl Mater 349(3) (2006) 251
[11] C. Pokor, Y. Brechet, P. Dubuisson, J.P. Massoud and A.Barbu, J Nucl Mater 326(1) (2004) 19
[12] D.Q. Peng, X.D. Bai and F. Pan, J Univ Sci Technol B 15(3) (2008) 285
[13] P. Mukherjee, P. Barat, S.K. Bandyopadhyay, P. Sen, S.K.Chottopadhyay, S.K. Chatterjee and M.K. Mitra, J Nucl Mater 305(2-3) (2002) 169
[14] D. Pecheur, F. Lefebvre, A.T. Motta, C. Lemaignan and D.Charquet, J Nucl Mater 205 (1993) 445
[15] Jade 5.0, XRD Pattern Processing, Materials Data Inc., 1999
[16] E.H. Lee, Nucl Instrum Meth B 151(1-4) (1999)29
[17] A. Meldrum, L.A. Boatner, W.J. Weber and R.C. Ewing, Geochim Cosmochim Ac 62(14) (1998) 2509
[18] N. Mottu, M. Vayer and R. Erre, Surf Coat Technol 183(2-3) (2004) 165
[19] I. Sakamoto, N. Hayashi and H. Tanoue, Surf Coat Technol 65(1-3) (1994) 133
[20] E. Johnson, A. Johansen, L. Sarholtkristensen, L.Graabaek, N. Hayashi and I. Sakamoto, Nucl Instrum Meth B 19-20 (1987) 171
[21] S. Fayeulle and D. Treheux, Nucl Instrum Meth B 19-20 (1987) 216
[22] O. Meyer and A. Azzam, Phys Rev Lett 52(18) (1984) 1629
[23] K.T.Y. Kung and R. Reif, J Appl Phys 59(7) (1986) 2422
[24] B. Rauschenbach and K. Helming, Nucl Instrum Meth B 42(2) (1989) 216
[25] B. Rauschenbach and K. Helming, Mater Sci Eng A 151(1) (1992) L9
[26] G.K. Williamson and R.E. Smallman, Philos Mag 1(1) (1956) 34
[27] P. Mukherjee, A. Sarkar, P. Barat, B. Raj and U.K. Mudali, Metall Mater Trans A 36A(9) (2005) 2351
[28] P. Mukherjee, P.M.G. Nambissan, P. Barat, P.T. Sen, S.K.Bandyopadhyay, J.K. Chakravartty, S.L. Wadekar, S. Banerjee, S.K.Chattopadhyay, S.K. Chatterjee and M.K. Mitra, J Nucl Mater 297(3) (2001) 341
[29] R.E. Stoller, J Nucl Mater 276(1-3) (2000) 22
[30] E.H. Lee, J.D. Hunn, T.S. Byun and L.K. Mansur, J Nucl Mater 280(1) (2000) 18
[31] A. Etienne, M. Hernandez-Mayoral, C. Genevois, B. Radiguet and P. Pareige, J Nucl Mater 400(1) (2010) 56
[32] M.V. Thompson, Defects and Radiation Damage in Metals, Ch. 4 and 5 (Cambridge Universeity Press, Cambridge, England,1969) p.89
[33] K.R.C. Mok, F. Benistant, M. Jaraiz, J.E. Rubio, P.Castrillo and R. Pincacho, J Appl Phys 103(1) (2008)014911-1
[34] B. Cox, J Nucl Mater 170(1) (1990) 1
[35] S.S. Kim, S.C. Kwon and Y.S. Kim, J Nucl Mater 273(1) (1999) 52
[36] B. Qin and W.S. Lai, J Mater Res 26(04) (2011)547
[37] L.E. Samuels and T.O. Mulhearn, J Mech Phys Solids 5(2) (1957) 125
WeChat