Based on thermodynamics calculation, the results of the formation temperature of MnS inclusions of non-quenched and tempered steel during heating process were discussed. It is shown that while the solid fraction is 0.9, MnS inclusions began to precipitate in the final stage of solidification. The solidification process of 49MnVS3 non-quenched and tempered steel during heating has been observed in situ using a confocal scanning laser microscope (CSLM), which agrees well with the thermodynamics calculation. MnS particles were coarsening during heating process, which would reduce the pinning effect on the austenite grain boundaries and bring about the sudden growth of some austenite grains in this stage.
LUO Yan-Zhao
. In situ observation and thermodynamic calculation of MnS in 49MnVS3 non-quenched and tempered steel[J]. Acta Metallurgica Sinica (English Letters), 2011
, 24(4)
: 326
-334
.
DOI: 10.11890/1006-7191-114-326
[1] S.R. Collins and G.M. Michal, Metall Mater Trans A 24A (1993) 2701.
[2] L.E. Iorio and W.M. Garrison, ISIJ Int 42 (2002) 545.
[3] M.E. Valdez, Y. Wang and S. Sridhar, Steel Res 76 (2005) 306.
[4] H. Takada, I. Bessho and T. Ito, Tetsu-to-Hagane 18 (1978) 564.
[5] C.E. Cicutti, J. Madias and J.C. Gonzalez, Ironmaking and Steelmaking 24 (1997) 155.
[6] M. Wintz, M. Bobadilla, J. Lehmann and H. Gaye, ISIJ Int 6 (1995) 715.
[7] T. Yamashita, S. Torizuka and K. Nagai, ISIJ Int 11 (2003) 1833.
[8] Z.B. Yang, PhD Dissertation (University of Science and Technology Beijing, Beijing, 2008).
[9] E.B. Yue, PhD Dissertation (China Iron and Steel Research Institute, 2004).
[10] E.T. Turkdogan, Fundamentals of Steelmaking (The University Press, Cambridge) p.298.
[11] H.B. Yin, K. Blazek and O. Lanzi, ISIJ Int 10 (2009) 1561.
[12] N. Yuki, H. Shibata and T. Emi, ISIJ Int 4 (1998) 317.
[13] Y. Kashiwaya, Y. Yamaguchi, H. Kinoshita and K. Ishii, ISIJ Int 2 (2007) 226.
[14] D.N. Crowther, P.S. Mitchell and W.B. Morrison, Proc 39th MWSP Conference (Indianapolis, USA, 1997).
[15] E.J. Palmiere, G.I. Garcia and A.J. DeArdo, Metall Mater Trans A 27A (1996) 951.
[16] S. Morito, H. Saito, T. Furuhara and T. Maki, ISIJ Int 45 (2005) 91.
[17] R. Priestner, Mater Sci Forum 284 (1998) 95.
[18] X.J. Shao, X.H. Wang and W.J. Wang, J Univ Sci Technol Beijing 5 (2010) 570.
[19] Z. Guo, N. Kimura, S. Tagashira, T. Furuhara and T. Maki, ISIJ Int 42 (2002) 1033.
WeChat