Hot compression test was carried out at 1000 ℃ to investigate the dynamic recrystallization nucleation mechanism of a nickel-base superalloy. It was found that the bulging of original grain boundaries was inhibited by carbides and deformation twins at the boundaries. Recrystallized nuclei evolved from the subgrains of dislocation reconfiguration along original grain boundaries, and the growth of the potential nuclei was carried out by the coalescence of subgrains. The necklace structure of recrystallized grains along original grain boundaries was attributed to the strain gradient from grain boundary to grain interior.
YU Shuai
,
YU Lei
,
LIU Yang
. Nucleation mechanism of a nickel-base superalloy during dynamic recrystallization[J]. Acta Metallurgica Sinica (English Letters), 2011
, 24(4)
: 295
-300
.
DOI: 10.11890/1006-7191-114-295
[1] L.Y. Jiao, J.F. Huang and G.P. Zhao, J Iron Steel Res 15 (2003) 48.
[2] Y. Liu, L. Wang, S. Wang and T. Cui, J Mater Metall 5 (2006) 288.
[3] S.S. Xie, Z.X. Wang, H.C. Yang and G.P. Zhao, Chin J Nonferrous Met 8 (1998) 167.
[4] J.X. Dong, A. Li and M.C. Zhang, J Mater Eng 9 (2003) 7.
[5] S.S. Xie, H.C. Yang, Z.X. Wang and Z.Y. Huang, J Northeastern Univ (Nat Sci) 19 (1998) 577.
[6] F.J. Humphreys, J Mater Sci 36 (2001) 3833.
[7] Y. Wang, W.Z. Shao, L. Zhen, L. Yang and X.M. Zhang, Mater Sci Eng A497 (2008) 479.
[8] C.G. Roberts, S.L. Semiatin and A.D. Rollett, Scr Mater 56 (2007) 899.
[9] F.J. Humphreys and M. Hatherly, Recrystallization and Related Annealing Phenomena, 2nd ed. (Elsevier, Oxford,2004) p.415.
[10] W. Xu, M. Ferry, J.M. Cairney and F.J. Humphreys, Acta Mater 55 (2007) 5157.
[11] R.D. Doherty, D.A. Hughes, F.J. Humphreys, J.J. Jonas,D.J. Jensen, M.E. Kassner, W.E. King, T.R. McNelley, H.J. McQueen and A.D. Rollett, Mater Sci Eng A238 (1997) 219.
[12] B.J. Zhang, G.P. Zhao, L.Y. Jiao, G.H. Xu, H.Y. Qin and D. Feng, Acta Metall Sin 41 (2005) 351 (in Chinese).
[13] Y. Wang, W.Z. Shao, L. Zhen and X.M. Zhang, Mater Sci Eng A486 (2008) 321.
[14] B.H. Tian, C. Lind, E. Schafier and O. Paris, Mater Sci Eng A367 (2004) 198.
[15] E. Brunger, X. Wang and G. Gottstein, Scr Mater 38 (1998) 1843.
[16] J.S. Zhang, High Temperature Deformation and Fracture of Materials (Science Press, Beijing, 2007) p.105 (in Chinese).
[17] J.P. Thomas, E. Bauchet, C. Dumont and F. Montheillet, Superalloys 2004 (Pennsylvania, America, 2004).
[18] F. Liu, Master Thesis (Northeastern University,Shenyang, 2005).
[19] M.A. Meyers and K.K. Chawla, Mechanical Behavior of Materials (Cambridge University Press, New York, 2009) p.338.
[20] L.M. Dougherty, I.M. Robertson and J.S. Vetrano, Acta Mater 51 (2003) 4367.
[21] R. Sandstrom, B. Lehtinen, E. Hedman, I. Groza and S.Karlsson, J Mater Sci 13 (1978) 1229.
WeChat