The thermal fatigue behaviour of an air plasma sprayed thermal barrier coating was investigated. And also the interfacial strengths of thermal barrier coated specimens subjected to thermal fatigue, as well as a retired TBC vane were also evaluated by means of an instrumented indentation machine. The results indicated that, (1) the TGO grew at the interface during thermal fatigue cycle as a function of the exposure time at elevated temperature; (2) the microcracks were initiated in the top coating and at the interface after thermal cycle tests; (3) the interfacial strength of TBC, which was evaluated by the indentation method, increased with the thermal cycles; (4) the interfacial strength of the retired TBC vane was almost equal with that of the as-sprayed TBC specimen.
YASUHIRO
. Evaluation of interfacial strength by an instrumented indentation method and its application to an actual TBC vane[J]. Acta Metallurgica Sinica (English Letters), 2011
, 24(2)
: 109
-117
.
DOI: 10.11890/1006-7191-112-109
1 J Soc Mater Sci Jpn A. Nitta 2007 56 90
2 J Soc Mater Sci Jpn Y. Yoshioka and A. Yamashita 2009 58 649
3 A. Schmidt and A. Scholz, Surf Coat Technol Y. Yamazaki 2006 201 744
4 Renusch, H. Echsler and M. Schutze, Conf Proc in Life Time Modeling of High Temperature Corrosion Process (2001) p.324.
5 N. Roy and K.M. Godiwalla, Bull Mater Sci A.K. Ray 2001 24 203
6 Acta Mater A. Rabiei and A.G. Evans 2000 48 3963
7 H. Fukanuma and N. Ohno, J Solid Mech Mater Eng Y. Yamazaki 2010 4 196
8 T. Kinebuchi, H. Fukanuma and N. Ohno, J Soc Mater Sci Jpn Y. Yamazaki 2008 57 596
9 T. Yoshida, H. Fukanuma and N. Ohno, J Soc Mater Sci Jpn Y. Yamazaki 2009 58 168
10 H. Echsler and M. Schutze, Mater High Temp D. Renusch 2004 21 65
11 J Soc Mater Sci Jpn M. Arai 2009 58 917
12 V.M. Sglavo, L. Mattivi, L. Bertamini and S. Sturlese, J Thermal Spray Technol R.D. Maschio 1994 3 51
13 P. Demarecaux and J. Lesage, Thin Solid Film D. Chicot 1996 283 151
14 Proc R Soc Lond A M.D. Drory and J.W. Hutchinson 1996 452 2319
15 I. Mircea, J. Suffener and B. Baufeld, Key Eng Mater M. Bartsch 2005 290 183
16 Eng Fracture Mech A. Vasinonta and J.L. Beuth 2001 68 843
17 Yamazaki and T. Yoshida, Key Eng Mater 417-418 (2010) 85 .
18 Proc Int. Thermal Spray Conf and Expo Y. Yamazaki and T. Yoshida 2008 2008
19 P. Chantikul, B.R. Lawn and D.B. Marshall, J Am Ceram Soc G.R. Anstis 1981 64 533
20 A.G. Evans and D.B. Marshall, J Am Ceram Soc B.R. Lawn 1981 63 574
21 J Jpn Thermal Spray Soc Y. Yamazaki and S. Kuga 2010 47 106
22 Toyoda, T. Komatsu, K. Satoh and M. Nayama, IIW Doc. X-1161-88 (1988).
23 Yamazaki, T. Kinebuchi, H. Fukanuma, N. Ohno and K.Kaise, Key Eng Mater 353-358 (2007) 1935.
WeChat