304 stainless steel coatings had been deposited on carbon-steel substrate by cold spray technique, vacuum annealing treatment was applied to the coatings with different temperatures, and the influence of annealing treatment on the microstructure and electrochemical behavior of the coatings in 3.5% NaCl were analyzed. The results indicated that, the cold sprayed coating was constituted by the flattened particles, and the interfaces were clearly observed between the deposited particles. It was also found that annealing treatment led to the recovery and recrystallization of the elongated grains in the as-sprayed coatings with the increase of annealing temperature. When the annealing temperature achieved to 950℃, the interface of particles was disappeared and the coating's structure was made of new recrystallization austenite grains. Annealing treatment increased the potential volts, and reduced the corrosion rate with the increase of annealing temperature. The electrical corrosion morphology indicated that, the corrosion was firstly at the distortion area and the crevice corrosion mechanism played an important part. Based on these results, processes active during annealing treatment are kinetically dependent and strongly influenced by the annealing treatment temperature.
DIAO Jie
. Influence of annealing treatment on microstructure and properties of cold sprayed stainless steel coatings[J]. Acta Metallurgica Sinica (English Letters), 2011
, 24(2)
: 92
-100
.
DOI: 10.11890/1006-7191-112-92
[1] C. Borchers, F. Gartner, T. Stoltenhoff, H.Assadi and H. Kreye, J Appl Phys 93 (2003) 10064.
[2] H. Assadi, F. Gartner, T. Stoltenhoff and H. Kreye, Acta Mater 51 (2003) 4379.
[3] T. Schmidt, F. Gartner, H. Assadi and H. Kreye, Acta Mater 54 (2006) 729.
[4] G. Bae, Y. Xiong, S. Kumar, K. Kang and C. Lee, Acta Mater 56 (2008) 4858.
[5] H. Na, G. Bae, S. Shin, S. Kumar, H-J.Kim and C. Lee, Compd Sci Technol 69 (2009) 463.
[6] H.J. Kim, C.H. Lee and S.Y. Hwang, Surf Coat Technol 191 (2005) 335.
[7] T. Stoltenhoff, H. Kreye and H.J. Richter, J Therm Spray Technol 11 (2002) 542.
[8] H.J. Kim, C.H. Lee and S.Y. Hwang, Mater Sci Eng A 391 (2005) 243.
[9] L. Ajdelsztajn, B. Jodoin and J.M. Schoenung, Surf Coat Technol 201 (2006) 1166.
[10] A. Ferriere, C. Sanchez Bautista, G.P. Rodriguez and A.J.Vazquez, Solar Energy 80 (2006) 1338.
[11] G. Jin, B.S. Xu, H.D. Wang, Q.F. Li, S.C. Wei, Surf Coat Technol 201 (2007) 5261.
[12] Z.S. Zeng, N. Sakoda, T. Tajiri and S.J. Kuroda, Surf Coat Technol 203 (2008) 284.
[13] Z.S. Zeng, N. Sakoda and T. Tajiri, J Therm Spray Technol 15 (2006) 431.
[14] K.M. EI-Khatib, M.O. Abou Helal, A.A. EI-Moneim and H.Tawfik, Anti-Corros Methods Mater 51 (2004) 136.
[15] Y.H. Yoo, S.H. Lee, J.G. Kim, J.S. Kim and C. Lee, J Alloy Compd 461 (2008) 304.
[16] K. Balani, T. Laha, A. Agarwal, J. Karthikeyan, N.Munroe, Surf Coat Technol 195 (2005) 272.
[17] K. Spencer, D. M. Fabijanic and M.X. Zhang, Surf Coat Technol 204 (2009) 336.
[18] W.Y. Li, H. Liao, G. Douchy and C. Coddet, Mater Des 28 (2007) 2129.
[19] T. Schmidt, F. Gartner, H. Assadi and H. Kreye, Acta Mater 54 (2006) 729.
[20] W.Y. Li, C.J. Li, H.L. Liao, J Therm Spray Technol 15 (2006) 206.
[21] C. Borchers, F. Gartner, T. Stoltenhoff and H.Kreye, Acta Mater 53 (2005) 2991.
[22] E. Calla, D.G. McCartney and P.H. Shipway, J Therm Spray Technol 15 (2006) 255.
[23] M.T. Simnad and U.R. Evans, Trans Faraday Soc 46 (1950) 175.
[24] N.D. Green and G.A. Saltzman, Corrosion 20 (1964) 27.
[25] C. Garcia, F. Martin, P. De Tiedra, J.A Heredero and M.L. Aparicio, Corros Sci 43 (2001) 1519.
WeChat