Hot deformation of Fe-3%Si alloy within the temperature range of 1073--1473 K and strain rate range of 0.01--5 s-1 was carried out by compression test. Optical microscopy (OM), electron backscattered diffraction (EBSD) and transmission electron microscopy (TEM) were used to characterize the deformation microstructure on various scales. Dynamic recovery is the dominant softening mechanism under all experimental conditions. A dynamic recovery region and partial dynamic recrystallization region can be distinguished according to Zener-Hollomon parameter (Z) based on OM observation. Furthermore, the quantitative description of subgrain size and boundary misorientation has been set up as a function of Zener-Hollomon parameter.
AN Feng-Hui
. Effect of Zener-Hollomon parameter on deformation microstructure in Fe-3%Si alloy[J]. Acta Metallurgica Sinica (English Letters), 2011
, 24(1)
: 1
-8
.
DOI: 10.11890/1006-7191-111-1
[1] T. Takamiya, T. Obara, M. Muraki and M.Komatsubara, Tetsu-to-Hagane 89 (2003) 22.
[2] M. Muraki, Y. Ozaki, T. Obara and T. Kan, JMEPEG 5 (1996) 323.
[3] S.V.S. Narayana Murty, S. Torizuka and K. Nagai, Mater Sci Eng A410-411 (2005) 319.
[4] S.V.S. Narayana Murty, S. Torizuka, K. Nagai, N. Koseki and Y. Kogo, Scr Mater 52 (2005) 713.
[5] S.V.S. Narayana Murty, S. Torizuka, K. Nagai, T. Kitai and Y. Kogo, Scr Mater 53 (2005) 763.
[6] S.V.S. Narayana Murty, S. Torizuka, K. Nagai, T. Kitai and Y. Kogo, Mater Sci Eng A457 (2007) 162.
[7] G. Glover and C.M. Sellars, Metall Trans 4 (1973) 765.
[8] E. Inoue and T. Sakai, J Jpn Inst Met 55 (1991) 286.
[9] T. Obara, H. Takeuchi, T. Takamiya and T. Kan, JMEPEG 2 (1992) 205.
[10] A. Orlova and I. Podstranska, Mater Sci Eng A248 (1998) 56.
[11] J.J. Urcola and C.M. Sellars, Acta Metall 35 (1987) 2649.
[12] W.M. Mao, Z.G. An and Y. Li, Mater Sci China 2 (2008) 233.
[13] C.M. Sellars and W.J. McTegart, Acta Metall 14 (1966) 1136.
[14] S. Akta, G.J. Richardson and C.M. Sellars, ISIJ Int 45 (2005) 1666.
[15] A. Ohmorl, S. Torizuka, K. Nagai, K. Yamada and Y. Kogo, Tetsu-to-Hagane 88 (2002) 857.
WeChat