Electrochemical corrosion behavior of 300M ultra high strength steel in chloride containing environment

  • XUN Min ,
  • DONG Tiao-Fang ,
  • XIAO Kui- ,
  • LI Xiao-Gang
Expand
  • Corrosion and Protection Center, School of Material and Engineering, University of Science and Technology Beijing, Beijing 100083, China

Received date: 2010-02-26

  Revised date: 2010-04-23

  Online published: 2010-08-11

Abstract

The electrochemical corrosion behavior of 300M ultra high strength steel in chloride containing environment was investigated by potentiodynamic polarization technique, electrochemical impedance spectroscopy (EIS) and scanning electron microscopy (SEM). The results show that uniform corrosion occurs on 300M steel during the electrochemical measurements because no anodic passivation phenomenon is observed on polarization curves within the measurement range. The tests also show that 300M steel is highly susceptible to chloride containing solution, which is characterized by corrosion current density increasing with the addition of chlorides, and corrosion potential shifting towards positive direction and corrosion resistance decreasing, positively suggesting that chloride ions speed up the corrosion rate of 300M steel. Meanwhile corrosion products on the 300M steel surface formed during the salt spray test are too loose and porous to effectively slow down the corrosion rate. Additionally, a schematic structure of uniform corrosion mechanism can explain that 300M steel has better property of stress corrosion cracking (SCC) resistance than stainless steels.

Cite this article

XUN Min , DONG Tiao-Fang , XIAO Kui- , LI Xiao-Gang . Electrochemical corrosion behavior of 300M ultra high strength steel in chloride containing environment[J]. Acta Metallurgica Sinica (English Letters), 2010 , 23(4) : 301 -311 . DOI: 10.11890/1006-7191-104-301

References

[1] M.L.A. Graca, C.Y. Hoo and O.M. Silva, Eng Fail Anal  16(1)  (2009) 182.
[2] R.O. Ritchie and R.M. Horn,  Metal Mater Trans A 9(3)  (1978) 331.
[3] Y. Tomita and T. Okawa,  Mater Sci Eng A  172(1-2) (1993) 145.
[4] C.F.G. aballero, M.J. Santofimia, C. Garcia-Mateo,S. Kaliappan, H. Shaikh, and P.V. Sivaprasad,  Mater Design 30(6)  (2009) 2077.
[5] H. Garbacz, M. Lewandowska, W. Pachla and K.J.Kurzydlowski,  J Microsc-Oxf   223(3)  (2006) 272.
[6] P.J. Antony, S. Chongdar, P. Kumar and R. Raman, Electrochim Acta  52(12)  (2007) 3985.
[7] A. Igual Munoz, J. Garcia Anton, J.L Guinon and V. Perez Herranz,  Corros Sci  49(8) (2007) 3200.
[8] H. Altun and S. Sen,  Mater Design  25(7) (2004) 637.
[9] L.C. Chang and H.K.D.H. Bhadeshia,  Mater Sci Eng A 184(1)  (1994) L17.
[10] R.W. Revie and H.H. Uhlig,  Corrosion and Corrosion Control, An Introduction to Corrosion Science and Engineering, 4th ed. (A John Wiley & Sons, Inc., Hoboken New Jersey, 2007)p.350.
[11] B. Diaz, L. Freire, X.R. Novoa and M.C.Perez,  Electrochim Acta  54  (2009) 5190.
[12] J. Sanchez, J. Fullea, C. Andrade, J.J. Gaitero and A. Porro,  Corros Sci  50  (2008) 1820.
[13] B. Jegdic, D.M. Drazic and J.P. Popic,  Corros Sci 50(5)  (2008) 1235.
[14] W.R. Osorio, L.C. Peixoto, L.R. Garcia and A.Garcia,  Mater Corros  60(10)  (2009) 804.
[15] C.O.A. Olsson and D. Landolt,  Electrochim Acta 48(9)  (2003) 1093.
[16] Y.F. Cheng,  Bull Electrochem  21(11)  (2005)503.
[17] X.L. Zhang, Z.H. Jiang, Z.P. Yao, Y. Songa and Z.D. Wub, Corros Sci  51(3)  (2009) 581.
[18] M. Pisarek, P. Kedzierzawski, M. Janik-Czachor and K.J.Kurzydlowski,  J Solid State Electrochem  13(2)  (2009)283.
[19] T.P. Hoar and W.R. Jacob,  Corros Sci  66(7) (1967) 341.
[20] P.C. Pistorius and G.T. Burstein,  Corros Sci 33(12)  (1992) 1885.
[21] K.V.S. Ramana, T. Anita, S. Mandal, S. Kaliappan, H.Shaikh and P.V. Sivaprasad,  Mater Design  30(9)  (2009)3770.
[22] S.D. Cramer,  ASM Handbook: Corrosion  (ASM International, United States of America, 1987) p.302.

Outlines

/