Acta Metallurgica Sinica (English Letters) >
Abnormal relationship between rust particles size and rust layer compactness of weathering steels
Received date: 2009-08-12
Revised date: 2009-12-02
Online published: 2010-02-09
In order to reveal evolution of the rust layer during atmospheric corrosion, commercial weathering steel (WS) 09CuPCrNi and a recently developed bainite WS were subjected to a salt fog test. The protection and compactness of the rust layer were evaluated by electrochemical analysis, absorption-desorption test, etc. The experimental results indicate that more compact rust layer could be derived from the rust particles with larger size. The well-established notion that the rust particle growth can induce the decrement of corrosion resistance of WS. However, the present investigation shows that the notion might not be universally accurate. The unusual result means that the rust particles might grow anisotropically during corrosion.
Key words： Weathering steel; Corrosion; Rust particle; Coarsening
ZHANG Meng , YANG Shan-Wu , ZHENG Hua , CHI Li-Li , HE Shen-Lai . Abnormal relationship between rust particles size and rust layer compactness of weathering steels[J]. Acta Metallurgica Sinica (English Letters), 2010 , 23(1) : 57 -62 . DOI: 10.11890/1006-7191-101-57
[1] Z.F. Wang, P.H. Li, Y. Guan, Q.F. Chen and S.K. Pu, Corros Sci 51(5) (2009) 954.
[2] M. Kimura, H. Kihira, N. Ohta and M. Hashimoto, Corros Sci 47(10) (2005) 2499.
[3] B.R. de Meybaum and S. Ayllon, Corrosion 7 (1980) 345.
[4] J.T. Keiser and C.W. Brown, Corros Sci 23(3) (1983) 251.
[5] A. Raman, Atmospheric Corrosion Problems with Weathering Steels in Louisia a Bridges (ASTM, New York, USA,1987) p.16.
[6] M. Yamashita, H. Miyuki, Y. Matsuda, H. Nagano and T.Misawa, Corros Sci 36(2) (1994) 283.
[7] H. Tamura, Corros Sci 50(7) (2008) 1872.
[8] T. Mizoguchi, Y. Ishii, T. Okada, M. Kimura and H.Kihira, Corros Sci 47(10) (2005) 2477.
[9] T. Ishikawa, M. Kumagai and M. Yasukawa, Corrosion 57(4) (2001) 346.
[10] J. Guo, S. Yang, C. Shang, Y. Wang and X. He, Corros Sci 51(2) (2008) 242.
[11] T. Ishikawa, T. Yoshida, K. Kandori, T. Nakayama and S.Hara, Corros Sci 49(3) (2007) 1468.
[12] Y.Y. Chen, H.J. Tzeng, L.I. Wei, L.H. Wang, J.C. Oung and H.C. Shih, Corros Sci 47(4) (2005) 1001.
[13] B.A. Granville, Proceedings Welding of HSLA (Microalloyed) Structural Steels (ASM, Rome, 1978) p.85.
/
| 〈 |
|
〉 |
WeChat