Strengthening and toughening forming of Al/Al2O3 composite in pseudo-semi-solid state
Received date: 2009-03-06
Revised date: 2009-07-26
Online published: 2010-02-09
A new technology—thixo-die-forging of the composite in pseudo-semi-solid state was proposed based on the powder metallurgy technology combing with semi-solid metal process, and the cup shells with Al/Al2O3 composite was prepared successfully. The metallographic analysis and performance test show that the microstructure of parts is dense and mechanical properties are excellent with the volume fraction of Al is 37 %. The bend strength and fracture toughness of the composite are about 570-690 MPa and 8.5-16.8 MPa m1/2, respectively. Comparing with reaction in situ and high temperature oxidation technologies the bending strength and fracture toughness are improved greatly. At the same time, it shows that the technology parameters have great influences on the properties. So it is feasible to prepare metal/ceramics composites by the proposed technology.
CHENG Yuan-Qing . Strengthening and toughening forming of Al/Al2O3 composite in pseudo-semi-solid state[J]. Acta Metallurgica Sinica (English Letters), 2010 , 23(1) : 21 -26 . DOI: 10.11890/1006-7191-101-21
[1] C.C. Jia, Introduction of Composites (Metallurgical Industry Press, Beijing, 2002) (in Chinese).
[2] B. Flinn, M. Ruhle and A.G. Evans, Acta Metall 37(4) (2004) 3001.
[3] T.J. Chen, Y. Hao and J. Sun, Trans Nonferrous Met Soc Chin 13(5) (2003) 1164.
[4] S. Ji and Z. Fan, Metall Mater Trans A 33(11) (2002) 3511.
[5] A. Das and Z. Fan, Mater Sci Technol 19(5) (2003) 573.
[6] T.Y. Liu, H.V. Atkinson and P. Kapranos, Metall Trans A (34) (2003) 1545.
[7] P.J. Uggowitzer and H. Kaufmann, Steel Res Int 75(8/9) (2004) 525.
[8] Q. Bai, H. Yang and M. Zhan, Trans Nonferrous Met Soc Chin 18(4) (2008) 6.
[9] G. Fan, Casting Technology (3) (2001) 26 (in Chinese).
[10] S.J. Luo, Y.S. Cheng and P.X. Wang, Trans Nonferrous Met Soc Chin 16(4) (2006) 772.
[11] Z.M. Du, Y.S. Cheng and S.J. Luo, Solid State Phenomena 116-117 (2006) 725.
[12] M.A. Schiavon, E. Radovanovic and I.V.P. Yoshida, Powder Technol 123(15) (2002) 232.
[13] Y.N. Barabanenkov, V.V. Ivanov, S.N. Ivanov, A.V.Taranov and E.N. Khazanov, Phys B 317(12) (2002) 269.
[14] R.H. Wagoner and M. Lib, Int J Plast 23(12) (2007) 345.
[15] A. Das and Z. Fan, Mater Sci Technol 19(5) (2003) 573.
[16] R.H. Wagoner and M. Lib, Int J Plast 23(9) (2007) 345.
/
| 〈 |
|
〉 |
WeChat