Applying the Protective Mn-Co-La2O3 Coating on Crofer 22 APU Ferritic Stainless Steel Used as Solid Oxide Fuel Cell Interconnects

doi:10.1007/s40195-024-01660-w

Abstract

Abstract:

This research studies the effect of Mn-Co-La₂O₃ coating synthesized by the electrodeposition method on the oxidation resistance and electrical conductivity of the Crofer 22 APU stainless steel interconnect plates in solid oxide fuel cells. The test samples were characterized by a field emission scanning electron microscope (FESEM) equipped with energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). The oxidation kinetics of the coated and uncoated samples were studied by tracking their weight changes over time at 800 °C, showing that the oxidation mechanism for all samples follows the parabolic law. Lower oxidation rate constant (k_p) values of the coated sample compared with that of the uncoated one indicated a reduction in the oxidation rate of the steel substrate in the presence of the Mn-Co-La₂O₃ coating. The examination of the cross-section of different samples after the isothermal oxidation for 500 h at 800 °C exhibited that applying the composite coating leads to a decrease in the thickness of the chromia layer formed on the steel surface. Furthermore, under these conditions, the area-specific resistance (ASR) of the coated sample (13.11 mΩ cm²) is significantly lower than that of the uncoated one (41.45 mΩ cm²).

Key words: Area specific resistance, Oxidation, Fuel cell, Composite coating

Farhad Mohsenifar, Hadi Ebrahimifar, Ahmad Irannejad. Applying the Protective Mn-Co-La₂O₃ Coating on Crofer 22 APU Ferritic Stainless Steel Used as Solid Oxide Fuel Cell Interconnects[J]. Acta Metallurgica Sinica (English Letters), 2024, 37(5): 872-888.

Figures/Tables 16

Table 1 Chemical composition of Crofer 22 APU steel

C	Cr	Mn	Si	Ni	Al	Ti	La	Fe
0.01	22.7	0.38	0.02	0.02	0.02	0.07	0.06	Bal

Table 2 Chemical compositions and operating conditions for Mn-Co-La2O3 electrodeposition

Manganese sulfate, monohydrate (MnSO₄∙H₂O)	84.5 g L⁻¹ (0.5 M)
Cobalt sulphate, heptahydrate (CoSO₄∙7H₂O)	28.11 g L⁻¹ (0.1 M)
Sodium gluconate (NaC₆H₁₁O₇)	152.7 g L⁻¹ (0.7 M)
Lanthanum oxide (La₂O₃)	20 g L⁻¹
Boric acid (H₃BO₃)	61.84 g L⁻¹ (1 M)
Ammonium sulfate (NH₄)₂SO₄	13.2 g L⁻¹ (0.1 M)
Current density	250 mA cm⁻²
Temperature	25 °C
pH	2
Time	45 min

Fig. 1 Experimental setup used for measuring the ASR

Fig. 2 a, b FESEM micrographs; c EDX analysis; d EDX mappings of the Mn-Co-La2O3 coating

Table 3 Quantitative results of EDX analysis of Mn-Co-La2O3 coating

Element	Line	Int	Error	K	Kr	W%	A%	ZAF^*	Peak/background
O	Ka	100.8	5.0219	0.0973	0.0900	13.58	37.23	0.6624	7.84
Mn	Ka	71.8	0.5800	0.0995	0.0920	8.22	6.56	1.1203	7.30
Co	Ka	366.4	0.5800	0.7597	0.7028	73.57	54.75	0.9553	35.25
La	La	18.9	0.5800	0.0435	0.0402	4.63	1.46	0.8689	3.10
				1.0000	0.9250	100.00	100.00

Fig. 3 X-ray diffraction patterns of Mn-Co-La2O3 coating

Fig. 4 High-resolution spectra and fitted curve of a Mn 2p; b Co 2p; c La 3d; d O 1s of Mn-Co-La2O3 coating

Fig. 5 a FESEM cross-section micrograph; b EDS line scan of the Mn-Co-La2O3-coated steel

Fig. 6 Oxidation kinetics of bare and Mn-Co-La2O3-coated steel in air for 500 h at 800 °C expressed as: a weight gain; b squared weight gain as a function of time during isothermal oxidation

Fig. 7 a, b FESEM surface morphology; c, d EDS analysis of uncoated Crofer 22 APU stainless steel at point 1 (c), point 2 (d) after 500 h of isothermal oxidation at 800 °C

Fig. 8 a, b FESEM surface morphology; c, d EDS analysis of Mn-Co-La2O3-coated Crofer 22 APU stainless steel at point 1 (c), point 2 (d) after 500 h of isothermal oxidation at 800 °C

Fig. 9 XRD pattern of: a uncoated; b Mn-Co-La2O3-coated specimens after 500 h of isothermal oxidation at 800 °C

Fig. 10 FESEM cross-section image and EDS line scan of: a, b uncoated; c, d Mn-Co-La2O3-coated specimens after 500 h of isothermal oxidation at 800 °C

Fig. 11 SEM images of: a, b uncoated; c, d Mn-Co-La2O3-coated samples after cyclic oxidation at 800 °C, and as well as e specific weight gain as a function of cycle number during cyclic oxidation

Table 4 Thermal expansion coefficients of the phases formed on samples specimens after 500 h of isothermal oxidation at 800 °C

Material	α (× 10⁻⁶ °C⁻¹)
Crofer 22 APU [53]	11.5
Cr₂O₃ [54]	9.6
MnCr₂O₄ [55]	7.2
FeCr₂O₄ [56]	8.5
Co₃O₄ [20]	9.3
MnCo₂O₄ [20]	9.7
La₂O₃ [57]	9.1

Fig. 12 ASR values of the uncoated and Mn-Co-La2O3-coated samples against the oxidation time: a at 800 °C; b against the temperature

References 96

[1]	A.G. Olabi, M.A. Abdelkareem, Renew. Sust. Energ. Rev. 158, 112111 (2022)
[2]	S.Z. Golkhatmi, M.I. Asghar, P.D. Lund, Renew. Sust. Energ. Rev. 161, 112339 (2022)
[3]	A. Ndubuisi, S. Abouali, K. Singh, V. Thangadurai, J. Mater. Chem. A 10, 2196 ( 2022)
[4]	J.C. Mah, A. Muchtar, M.R. Somalu, M.J. Ghazali, Int. J. Hydrog.Energy 42, 9219 (2017)
[5]	J. Peng, D. Zhao, Y. Xu, X. Wu, X. Li,Energies 16, 788 (2023)
[6]	L. Zhou, J.H. Mason, W. Li, X. Liu, Renew. Sust. Energ. Rev. 134, 110320 (2020)
[7]	V. Bongiorno, R. Spotorno, D. Paravidino, P. Piccardo,Metals 11, 405 (2021)
[8]	C.M. Harrison, P.R. Slater, R. Steinberger-Wilckens, Solid State Ion. 354, 115410 (2020)
[9]	J. Zhou, Q. Chen, J. Sang, R. Wu, Z. Li, W. Guan, Acta Metall. Sin. -Engl. Lett. 34, 668 (2021)
[10]	Z. Yang, M. Guo, N. Wang, C. Ma, J. Wang, M. Han, Int. J. Hydrog.Energy 42, 24948 (2017)
[11]	J.C. De Vero, K. Develos-Bagarinao, H. Kishimoto, T. Ishiyama, K. Yamaji, T. Horita, H. Yokokawa, J. Power.Sources 377, 128 (2018)
[12]	S. Molin, A.G. Sabato, M. Bindi, P. Leone, G. Cempura, M. Salvo, S.C. Polo, A. Boccaccini, F. Smeacetto, J. Eur. Ceram. Soc. 37, 4781 (2017)
[13]	X. Li, J. Shu, L. Chen, H. Bi, Acta Metall. Sin. -Engl. Lett. 27, 501 (2014)
[14]	N. Shaigan, W. Qu, D.G. Ivey, W. Chen, J. Power.Sources 195, 1529 (2010)
[15]	S. Sabzalian, M. Soltanieh, S. Rastegari, Int. J.Hydrogen Energy 48, 16406 (2023)
[16]	K.H. Tan, H.A. Rahman, M.S. Azami, U.A. Yusop, N.A. Baharuddin, M.I. Nor Ma’arof, Ceram. Int. 48, 34258 (2022)
[17]	S. Frangini, L. Della Seta, C. Paoletti,Energies 15, 632 (2022)
[18]	M. Li, J. Xie, W. Gao, Z. Zhan, Z. Li, Surf. Coat. Technol. 444, 128655 (2022)
[19]	F. Li, P. Zhang, Y. Zhao, D. Yang, J. Sun, Int. J. Hydrog.Energy 48, 16048 (2023)
[20]	M.R. Ardigo-besnard, I. Popa, S. Chevalier, Corros. Sci. 148, 251 (2019) DOI
[21]	A. Petric, H. Ling, J. Am. Ceram. Soc. 90, 1515 (2007)
[22]	B. Talic, S. Molin, K. Wiik, P.V. Hendriksen, H.L. Lein, J. Power.Sources 372, 145 (2017)
[23]	J. Mao, E. Wang, H. Wang, M. Ouyang, H. Hu, L. Lu, D. Ren, Y. Liu,Coatings 13, 1144 (2023)
[24]	Y. Zhang, S. Wu, L. Chen, J. Liu, L. Jia, D. Yan, L. Jian, J. Electrochemic. Soc. 170, 024509 (2023)
[25]	Z. Shen, J. Rong, X. Yu, Ceram. Int. 46, 5821 (2020)
[26]	M.H. Shirani Bidabadi, T. Siripongsakul, T. Thublaor, P. Wiman, S. Chandra-ambhorn, Surf. Coat. Technol. 434, 128176 (2022)
[27]	T. Thublaor, S. Chandra-ambhorn, Corros. Sci. 174, 108802 (2020)
[28]	H. Ebrahimifar, M. Zandrahimi, Oxid. Met. 84, 129 (2015)
[29]	S. Chandra-ambhorn, W. Homjabok, W. Chandra-ambhorn, T. Thublaor, T. Siripongsakul, Corros. Sci. 187, 109506 (2021)
[30]	Y.Z. Hu, Y.T. Su, C.X. Li, C.J. Li, G.J. Yang, Appl. Surf. Sci. 499, 143726 (2020)
[31]	C. Jia, Y. Yang, S. Molin, Y. Zhang, M. Chen, M. Han, J. Alloys Compd. 787, 1327 (2019)
[32]	E. Dogdibegovic, S. Ibanez, A. Wallace, D. Kopechek, G. Arkenberg, S. Swartz, J.M. Funk, M. Reisert, M.A. Rahman, A. Aphale, P. Singh, H. Ding, W. Tang, M.V. Glazoff, D. Ding, T.L. Skafte, M.C. Tucker, Int. J. Hydrog.Energy 47, 24279 (2022)
[33]	T. Brylewski, S. Molin, M. Marczyński, L. Mazur, K. Domaradzki, O. Kryshtal, A. Gil, Int. J. Hydrog.Energy 46, 6775 (2021)
[34]	F. Saeidpour, R. Khaleghian-Moghadam, Oxid. Met. 97, 493 (2022)
[35]	C. Goebel, R. Berger, C. Bernuy-Lopez, J. Westlinder, J.E. Svensson, J. Froitzheim, J. Power.Sources 449, 227480 (2020)
[36]	Z.B. Ma, M.H. Wang, Y.S. Zhang, K. Li, M.G. Zhang, W. Yang,Vacuum 204, 111352 (2022)
[37]	N. Hosseini, F. Karimzadeh, M. Abbasi, G. Choi, J. Alloys Compd. 673, 249 (2016)
[38]	H.P. Tseng, T.Y. Yung, C.K. Liu, Y.N. Cheng, R.Y. Lee, Int. J. Hydrog.Energy 45, 12555 (2020)
[39]	H. Zhu, S. Geng, J. Zhang, M. Chen, F. Wang,Ionics 28, 5525 (2022)
[40]	J. Li, M. Zou, W. Chen, X. Hu, J. Zhou, X. Jiang,Thin Solid Films 768, 139692 (2023)
[41]	J. Gong, G. Zangari, J. Electrochem. Soc.149, C209 (2002)
[42]	W. Wei, W. Chen, D.G. Ivey, J. Power.Sources 186, 428 (2009)
[43]	N. Guglielmi, J. Electrochem. Soc. 119, 1009 (1972)
[44]	E. Lee, J. Choi, Surf. Coat. Technol. 148, 234 (2001)
[45]	B.J. Hwang, C.S. Hwang, J. Electrochem. Soc. 140, 979 (1993)
[46]	P. Vereecken, I. Shao, P. Searson, J. Electrochem. Soc. 147, 2572 (2000)
[47]	M. Fernández-Barcia, V. Hoffmann, S. Oswald, L. Giebeler, U. Wolff, M. Uhlemann, A. Gebert, Surf. Coat. Technol. 334, 261 (2018)
[48]	M.M. Kerrigan, J.P. Klesko, C.H. Winter, Chem. Mater. 29, 7458 (2017)
[49]	W. Zhao, J. Jiang, Y. Luo, J. Li, Y. Ding,Coatings 13, 870 (2023)
[50]	V. Barhate, K. Agrawal, V. Patil, S. Patil, A. Mahajan, Int. J. Mod. Phys.B 32, 1840074 (2018)
[51]	P. Zhang, J. Guo, P. Zhao, B. Zhu, W. Huang, S. Zhang, RSC Adv. 5, 11989 (2015)
[52]	F. Alahmadi, I.S. Khan, D. Poloneeva, G. Shterk, L.C. Garzon-Tovar, R. Schucker, A. Bavykina, J. Gascon, Ind. Eng. Chem. Res. 61, 15195 (2022)
[53]	S. Becker, M. Baerns, J. Catal. 128, 512 (1991)
[54]	M. Li, Y. Gao, K. Zhao, H. Li, F. He, P. Lv, Z. Huang, Fuel Process. Technol. 216, 106771 (2021)
[55]	Y.F. He, M.L. Li, S.J. Liu, H.Y. Wei, H.Y. Ye, Y.M. Song, P. Qiu, Y.L. An, M.Z. Peng, X.H. Zheng, Acta Metall. Sin. -Engl. Lett. 34, 668 (2021)
[56]	V. Bongiorno, P. Piccardo, S. Anelli, R. Spotorno, Acta Metall. Sin. -Engl. Lett. 32, 1530 (2019)
[57]	S. Geng, Q. Zhao, Y. Li, J. Mu, G. Chen, F. Wang, S. Zhu, Int. J. Hydrog.Energy 42, 10298 (2017)
[58]	S. Geng, S. Qi, D. Xiang, S. Zhu, F. Wang, J. Power.Sources 215, 274 (2012)
[59]	H. Shahbaznejad, H. Ebrahimifar, J. Mater. Sci. Mater. Electron. 32, 7550 (2021)
[60]	D. Koszelow, M. Makowska, F. Marone, J. Karczewski, P. Jasiński, S. Molin, Corros. Sci. 189, 109589 (2021)
[61]	K. Przybylski, T. Brylewski, E. Durda, R. Gawel, A. Kruk, J. Therm. Anal. Calorim. 116, 825 (2014)
[62]	Z. Sun, S. Gopalan, U.B. Pal, S.N. Basu, Surf. Coat. Technol. 323, 49 (2017)
[63]	S. Molin, Int. J. Appl. Ceram. Technol. 15, 349 (2018)
[64]	F. Saeidpour, M. Zandrahimi, H. Ebrahimifar, Int. J. Hydrog.Energy 44, 3157 (2019)
[65]	F.H. Stott, F.I. Wei, C.A. Enahoro, Mater. Corros. 40, 198 (1989)
[66]	T. Brylewski, J. Dabek, K. Przybylski, J. Therm. Anal. Calorim. 77, 207 (2004)
[67]	T. Brylewski, M. Nanko, T. Maruyama, K. Przybylski, Solid State Ion. 143, 131 (2001)
[68]	M. Cox, B. McEnaney, V. Scott, Philos. Mag. 26, 839 (1972)
[69]	A. Sabioni, A. Huntz, L. Borges, F. Jomard, Philos. Mag. 87, 1921 ( 2007)
[70]	J. Gilewicz-Wolter, J. Dudała, Z. Żurek, M. Homa, J. Lis, M. Wolter, J. Phase Equilibria Diffus. 26, 561 (2005)
[71]	H.T. Michels, Metall. Mater. Trans. A 7, 379 (1976)
[72]	B. Pint, Oxid. Met. 45, 1 (1996)
[73]	J.H. Zhu, M.J. Lewis, S.W. Du, Y.T. Li,Thin Solid Films 596, 179 (2015)
[74]	S. Fontana, S. Chevalier, G. Caboche, Oxid. Met. 78, 307 (2012)
[75]	B.K. Kim, D.I. Kim, K.W. Yi, Corros. Sci. 130, 45 (2018)
[76]	W.M. Fr, D.H. Yoon, K. Raju, S. Kim, K.S. Song, J.H. Yu, Met. Mater. Int. 24, 157 (2018)
[77]	G.V. Samsonov, The oxide handbook, 2nd edn. (Springer, New York, 2013), p. 126
[78]	W. Qu, L. Jian, J.M. Hill, D.G. Ivey, J. Power.Sources 153, 114 (2006)
[79]	C.W. Parmelee, A.E. Badger, G.A. Ballam, A study of a group of typical spinels University of Illinois, Urbana, 1932), p.20
[80]	J. Muthusamy, G. Venkadesan, M.S. Panithasan, Int. J. Hydrog.Energy 47, 27199 (2022)
[81]	S.N. Hosseini, F. Karimzadeh, M.H. Enayati, N.M. Sammes, Solid State Ion. 289, 95 (2016)
[82]	A.M. Dayaghi, M. Askari, H. Rashtchi, P. Gannon, Surf. Coat. Technol. 223, 110 (2013)
[83]	Y. Xu, Z. Wen, S. Wang, T. Wen, Solid State Ion. 192, 561 (2011)
[84]	Y.T. Yu, J.H. Zhu, J. Electrochem. Soc.165, F297 (2018)
[85]	F. Saeidpour, M. Zandrahimi, H. Ebrahimifar, Corros. Sci. 153, 200 (2019) DOI
[86]	F. Saeidpour, H. Ebrahimifar, Corros. Sci. 182, 109280 (2021)
[87]	F. Saeidpour, M. Zandrahimi, H. Ebrahimifar, Oxid. Met. 93, 87 (2020)
[88]	P. Paknahad, M. Askari, M. Ghorbanzadeh, J. Power.Sources 266, 79 (2014)
[89]	V.I. Gorokhovsky, P. Gannon, M. Deibert, R.J. Smith, A. Kayani, M. Kopczyk, D. VanVorous, Z. Yang, J.W. Stevenson, S. Visco, J. Electrochem. Soc.153, A1886 (2006)
[90]	B. Gillot, F. Jemmali, Mater. Chem. Phys. 18, 139 (1987)
[91]	C. Quan, S. Deng, Y. Jiang, C. Jiang, M. Shuai, J. Alloys Compd. 793, 170 (2019)
[92]	N. Gavrilov, V. Ivanov, A. Kamenetskikh, A. Nikonov, Surf. Coat. Technol. 206, 1252 (2011)
[93]	Y. Zhou, H. Hu, H. Zhang,Vacuum 86, 210 (2011)
[94]	A. Strawbridge, P. Hou, Mater. High Temp. 12, 177 (1994)
[95]	E. Lang, The role of active elements in the oxidation behaviour of high temperature metals and alloys (Elsevier, New York, 2012), pp. 14-15
[96]	Y. Zhou, J. Sun, S. Wang, H. Zhang, Corros. Sci. 63, 351 (2012)

Applying the Protective Mn-Co-La₂O₃ Coating on Crofer 22 APU Ferritic Stainless Steel Used as Solid Oxide Fuel Cell Interconnects

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 16

References 96

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	Xuhui Liu, Zijin Xiao, Yang Yuan, Qihong Huang, Kaiwei Tang, Yilong Dai, Dechuang Zhang, Jia She, Feng Peng, Fugang Qi, Xiaoping Ouyang. Corrosion-resistant and bioactive FeMn-CaP-Col@CS coating on magnesium alloy for orthopedic implants: Fabrication and characterization [J]. Metals Advances, 2026, 39(1): 1-12.
[2]	Zhenzhen Tian, Rongqian Wu, Fubing Yu, Yan Zhou, Wenhui Yao, Yuan Yuan, Zhihui Xie, Yanlong Ma, Atrens Andrej, Liang Wu. Preparation and Corrosion Resistance Mechanism of Magnesium-Lithium Alloy Micro-arc Oxidation/Quaternary LDHs@GO Self-healing Composite Film [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(9): 1545-1558.
[3]	Hongliang Liu, Jingpei Nie, Liwei Bai, Yujing Fu, Xiaoguang Yang, Zhen Chang, Xue Zhang, Ying Li. Preparation and Anti-Oxidation Mechanism of an Inventive Preprocessing Method for Press-Hardened Steels [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(9): 1604-1612.
[4]	Yicheng Wang, Rongcheng Li, Bowen Jin, Chenghao Xie, Xinfeng Tang, Gangjian Tan. Revealing the True Thermoelectric Properties of SnTe through Removing SnO₂ Contamination [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(5): 754-762.
[5]	Yang Feng, Shuai Wang, Yang Zhao, Li-Qing Chen. Achieving High-Temperature Oxidation and Corrosion Resistance in Fe-Mn-Cr-Al-Cu-C TWIP Steel via Annealing Control [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(4): 642-656.
[6]	Yifei Gao, Peng Zhang, Pan Ren, Yingfei Yang, Guofeng Han, Wenbo Du, Wei Li, Qiwei Wang. Effect of CeO₂ on the H₂O/NaCl-Induced Corrosion Behavior of Ni-Co Coating at 650 °C [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(4): 672-690.
[7]	Hang Ding, Juanjuan Liang, Xin Luo, Song Tang, Yun Xie, Xiao Peng. Unveiling the Selective Oxidation Mechanism of a Low Cr Alloy with Surface Spraying Oxide Nanoparticles of hcp Structure [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(12): 2125-2133.
[8]	Shuaiwu Peng, Zejun Chen, Runhua Yao, Sen Pei, Ruiqiang Hang, Yonghua Sun, Xiaohong Yao, Ying Lu. Corrosion Behavior, Antioxidation Property, Antibacterial Ability, and Osteogenic Activity of Zn / Chitosan-Catechol Coating Prepared on NiTi Alloy [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(11): 1909-1925.
[9]	Yonghua Chen, Zhenzhen Tian, Fubing Yu, Mingyi Wu, Wenhui Yao, Yuantai He, Yuan Yuan, Zhihui Xie, Guozhi Wu, Jiahao Wu, Fusheng Pan, Liang Wu. Evaluation of Corrosion Resistance for ZIF-67@Co-M (M = Fe, Al, Ni) LDHs Composite Coatings Based on AZ31 Magnesium Alloy [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(11): 2001-2023.
[10]	Jin-Xiu Li, Jun-Xiu Chen, M. A. Siddiqui, S. K. Kolawole, Yang Yang, Ying Shen, Jian-Ping Yang, Jian-Hua Wang, Xu-Ping Su. Enhancing Corrosion Resistance and Antibacterial Properties of ZK60 Magnesium Alloy Using Micro-Arc Oxidation Coating Containing Nano-Zinc Oxide [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(1): 45-58.
[11]	Xiaoxue Wang, Jingjing Guo, Zihao Zeng, Peng Zhou, Rongqiao Wang, Xiuchun Liu, Kai Gao, Jingli Sun, Yong Yuan, Fuhui Wang. A Semi-Mechanistic Model for Predicting the Service Life of Composite Coatings on VW63Z Magnesium Alloy [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(7): 1161-1176.
[12]	Weidong Zhang, Yu Cui, Li Liu, Wenquan Wang, Wenzheng Chen, Rui Li, Fuhui Wang. Corrosion Behavior of Pre-oxidized GH4169 Alloy with Solid NaCl Deposited in a Wet Oxygen Flow at 600 °C [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(7): 1249-1264.
[13]	Chuan Rong, Jieren Yang, Xiaoliang Zhao, Ke Huang, Ying Liu, Xiaohong Wang, Dongdong Zhu, Ruirun Chen. Microstructure Recrystallization and Mechanical Properties of a Cold-Rolled TiNbZrTaHf Refractory High-Entropy Alloy [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(4): 633-647.
[14]	Wenting Wang, Jingjun Xu, Jun Zuo, Ke Ma, Yang Li, Guangqi He, Meishuan Li. Oxidation Resistance of In Situ Reaction/Hot Pressing Synthesized Ti₂AlC-20% TiB₂ Composite at 600-900 °C in Air [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(4): 739-748.
[15]	Ying Shen, Xianfeng Shan, Iniobong P. Etim, Muhammad Ali Siddiqui, Yang Yang, Zewen Shi, Xuping Su, Junxiu Chen. Comparative Study of the Effects of Nano ZnO and CuO on the Biodegradation, Biocompatibility, and Antibacterial Properties of Micro-arc Oxidation Coating of Magnesium Alloy [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(2): 242-254.