Acta Metallurgica Sinica (English Letters) ›› 2003, Vol. 16 ›› Issue (6): 473-477 .

• Research Articles • Previous Articles Next Articles

F.M.Yang, X.F.Sun, H.R.Guan, Z.Q.Hu

InstituteofMetalResearch,TheChineseAcademyofSciences,Shenyang110016,China

Received:2002-11-29 Revised:1900-01-01 Online:2003-12-25 Published:2009-10-10
Contact: F.M.Yang

Abstract

Abstract: The dynamic strain aging behavior during tensile tests of K40S alloy has been investigated in the temperature range of 25-1100℃ with the strain rate range from 10^-4 to 10^-3s^-1. The results show that four different types of serration, identified as A,B, C and E type serration were observed in the temperature range of 300-500℃. The strain exponents for onset of the serrated flow were calculated as 1.21, 2. 79 and 1.61,and the activation energies as 121, 40 and 67kJ/mol for E, B and C type serration respectively. The main mechanism for dynamic strain aging discussed in light of the strain exponent and the activation energy.

Key words: dynamic strain aging, serrated flow, strain exponent,

F.M.Yang, X.F.Sun, H.R.Guan, Z.Q.Hu. [J]. Acta Metallurgica Sinica (English Letters), 2003, 16(6): 473-477 .

References

1 S. Venkadesan, C. Phaniraj, P.V. Sivaprasad and V. Rodriguez, Acta Metall. Mater. 40(3) (1992) 569．
2 F.R.N. Nabarro, Theory of Crystal Dislocations (Oxford University Press, Oxford, 1967) p.458．
3 J.M. Robinson and M.P. Shaw, Inter. Mater. Rev. 39(3) (1994) 113．
4 E. Pink and A. Grinberg, Acta Metall. Mater. 30(1982) 2153．
5 K. Bhanu Sankara Rao, M.G. Castelli and J.R. Ellis, Scripta Metall. Mater. 33(6) (1995) 1005．
6 Y. Nakada and A.S. Keh, Acta Metall. 18(4) (1970) 437．
7 A.H. Cottrell, Philos. Mag. 44 (1953) 829．
8 J. Friedel, Dislocations (Oxford Pergamon Press, London, 1964) p.102．
9 A. Vanden Beukel, Acta Metall. Mater. 28(1980) 965．
10 A. Vanden Beukel and U.F. Kocks, Acta Metall. Mater. 30(1982) 1027．
11 U.F. Kocks, A.S. Argon and M.F. Ashby, Prog. Mater. Sci. 19(1975) 1．
12 F.M. Yang, S.F. Sun, W. Zhang, Y.P. Kang, H.R. Guan and Z.Q. Hu, Mater. Lett. 49(2001) 160．
13 B.J. Brindley and A.S. Keh, Metall. Rev. 145 (1970) 101．
14 P. Rodriguez, Bull. Mater. Sci. 6(1984) 653．
15 P. McCormick, Acta Metall. 20(1972) 350．
16 I.S. Kim and M.C. Chaturvedi, Trans. JIM 28 (1987) 205．
17 U.F. Kocks, R.E. Cook and R.A. Mulford, Acta Metall. Mater. 33(4) (1985) 623．
18 J.D. Baird, Inhomogeneities of Plastic Deformation (ASM, Metals Park, OH, 1973) p.191．
19 P.G. McCormick, Acta Metall. 21(1973) 873．
20 Soon H. Hong, Hee Y. Kim, Jin S. Jang and H. Kuk, in Proc. Conf. 'Superalloys 1996', eds. R.D Kissinger, D.J. Deye, D.L. Anton and T.M. Pollock(TMS, US, 1996) p.401．
21 Th. Hehenkamp, Acta Metall. 14(7) (1966) 887．
22 A.H. Cottrell, Dislocations and Plastic Flow in Crystals(Clarendon Press, Oxford, 1953) p.1．
23 A.W. Sleeswyk, Acta Metall. 6(1958) 598．
24 L. Rémy and A. Pineau, Mater. Sci. Eng. 36(1978) 47．
25 T. Ericsson, Acta Metall. 14 (1966) 1073．
26 L. Kaufman and N.Z. Neson, Z. Metallkd. 64 (1973) 249．S

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 0

Recommended Articles

Metrics

Comments