THE INFLUENCES OF SOLUTION PH AND CURRENT DENSITY ON COERCIVITY OF ELECTROPLATING CoNdNiMnP PERMANENT MAGNETIC ALLOY FTLM ARRAYS

Acta Metallurgica Sinica (English Letters) ›› 2004, Vol. 17 ›› Issue (5): 677-681 .

• Research Articles • Previous Articles Next Articles

THE INFLUENCES OF SOLUTION PH AND CURRENT DENSITY ON COERCIVITY OF ELECTROPLATING CoNdNiMnP PERMANENT MAGNETIC ALLOY FTLM ARRAYS

H.C.Jiang, W.L.Zhang, J.P.Zhang, W.X.Zhang, B.Peng, S.Q.Yang

School of Microelectronics and Solid Electronics,University of Electronic Science and Technology of China,Ghengdu610054,Ghina

Received:1900-01-01 Revised:1900-01-01 Online:2004-10-25 Published:2009-10-10
Contact: H.C.Jiang

Abstract

Abstract: The influences of plating bath solution PH and current density on coercivity of electroplating CoNdNiMnP permanent magnetic film arrays were studied. The experiment results show that both for solution PH and current density there were the best depositing parameters. Too high and too low plating bath solution PH or current density both result in decreasing of the film array coercivity. When solution PH is 3.5 and current density is 5mA/cm^2, the prepared film array coercivity can reach the maximum.

Key words: solution PH, current density, electroplating

H.C.Jiang, W.L.Zhang, J.P.Zhang, W.X.Zhang, B.Peng, S.Q.Yang. THE INFLUENCES OF SOLUTION PH AND CURRENT DENSITY ON COERCIVITY OF ELECTROPLATING CoNdNiMnP PERMANENT MAGNETIC ALLOY FTLM ARRAYS[J]. Acta Metallurgica Sinica (English Letters), 2004, 17(5): 677-681 .

[1]	Mengcheng Zhou, Yaxiong Dai, Changhao Liu, Shengli Ding, Xinfang Zhang. Migration Behavior of Impurity Iron in Silicon Melt Under Pulsed Electric Current [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(5): 889-903.
[2]	Enobong Felix Daniel, Junhua Dong, Xiaofang Li, Ini-Ibehe Nabuk Etim, Inime Ime Udoh, Rongyao Ma, Lei Chen, Changgang Wang. Corrosion Behaviour of Carbon Steel Fasteners in Neutral Chloride Solution [J]. Acta Metallurgica Sinica (English Letters), 2022, 35(4): 563-576.
[3]	Jiancheng Li, Haobo Liu, Ying Li, Chuanbing Cai, Shixue Dou, Wenxian Li. Research Progress of Electromagnetic Properties of MgB₂ Induced by Carbon-Containing Materials Addition and Process Techniques [J]. Acta Metallurgica Sinica (English Letters), 2020, 33(4): 471-489.
[4]	Farid Habelhames, Zerguine Wided, Leila Lamiri, Belkacem Nessark,Hassina Derbal-Habak. Morphology and Photoelectrochemical Characterization of MEH-PPV/PCBM Composite Film Doped with TiO₂ Nanoparticles [J]. Acta Metallurgica Sinica (English Letters), 2013, 26(4): 373-377.
[5]	Zhaoxia PING, Guoan CHENG,Yedong HE. Ni-P-SiC composite coatings electroplated on carbon steel assisted by mechanical attrition [J]. Acta Metallurgica Sinica (English Letters), 2010, 23(2): 137-146.
[6]	Buming CHEN,Zhongcheng GUO,Hui HUANG,Xianwan YANG,Yuandong CAO. Effect of the current density on electrodepositing alpha-lead dioxide coating on aluminum substrate [J]. Acta Metallurgica Sinica (English Letters), 2009, 22(5): 373-382.
[7]	Z. Zhang, W.H. Leng , J.Q. Zhang. STUDY OF THE INFLUENCE OF pH ON THE ELECTROCRYSTALLIZATION OF ZINC [J]. Acta Metallurgica Sinica (English Letters), 2005, 18(4): 497-504 .
[8]	Z.M.Zou, X.M.Cao, C.Tian, J.S.Zhang. PREPARATION OF LEAD-ACID BATTERY USING ELECTROPLATED RETICULATED SiC AS THE POSITIVE CURRENT COLLECTOR [J]. Acta Metallurgica Sinica (English Letters), 2005, 18(2): 107-112 .
[9]	Z.Zhang. ELECTROCHEMICAL NOISE ANALYSIS OF THE INFLUENCE OF THE Zn^2＋ IONS CONCENTRATION ON ZINC ELECTROPLATING [J]. Acta Metallurgica Sinica (English Letters), 2005, 18(2): 137-144 .
[10]	H.C.Jiang, W.L.Zhang, J.P.Zhang, W.X.Zhang, B.Peng, S.Q.Yang. INFLUENCES OF NEODYMIUM ON MAGNETIC CHARACTERISTICS OF ELECTROPLATING CoNdNiMnP FILMS [J]. Acta Metallurgica Sinica (English Letters), 2005, 18(2): 149-152 .
[11]	Z.Zhang. STUDY THE INFLUENCE OF H3BO3 ON THE ZINC ELECTROPLATING USING ELECTROCHEMICAL NOISE TECHNIQUE [J]. Acta Metallurgica Sinica (English Letters), 2004, 17(5): 661-666 .
[12]	C.H.Jiang, J.M.Yoo, J.W.Ko, G.W.Qiao. THE INFLUENCE OF PRECURSOR VARIABLES ON THE PHASE FORMATION,MICROSTRUCTURE AND TRANSPORT PROPERTY OF Bi—2223／Ag TAPES [J]. Acta Metallurgica Sinica (English Letters), 2003, 16(2): 84-89 .
[13]	B.W. Zhang, Z.M. Ren, Y.B. Zhong. THEORETICAL INVESTIGATION ON BY-ONLY-CURRENT ELECTROMAGNETIC SEPARATION OF INCLUSION FROM MOLTEN METALS [J]. Acta Metallurgica Sinica (English Letters), 2002, 15(5): 416-424 .
[14]	Y.S. Dong and P.H. Lin (Department of Mechanical Engineering, Southeast University, Nanjing 210096, China) J. Shen and Q.C. Li (School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China). THE PREPARATION AND APPLICATION OF ELECTROPLATED SHEET CONTAINING RS ALUMINUM ALLOY POWDERS [J]. Acta Metallurgica Sinica (English Letters), 2000, 13(5): 1047-1052.
[15]	S.Y.Hu Collge of Mechanical Engineering, China Agriculture University (East Campus), Beijing 100083, China. STUDY ON THE REAR CAPACITY OF DEPOSITS USING ELECTROLESS NICKEL DEPOSITION AND ELECTROPLATE CHROMIUM [J]. Acta Metallurgica Sinica (English Letters), 1999, 12(5): 777-781.

THE INFLUENCES OF SOLUTION PH AND CURRENT DENSITY ON COERCIVITY OF ELECTROPLATING CoNdNiMnP PERMANENT MAGNETIC ALLOY FTLM ARRAYS

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments