Abstract: The microstructure characteristics with super fine ferrite grain size less than 5mm,appropriate retained austenite fraction around 5.0and or removable abundant dislocations have been obtained by controlled rolling and cooling, which leads to well balance comprehensive properties with high tensile strength of 510 and 615MPa, high elongation of 40and 27, low ratio of yield strength to tensile strength 0.83 and 0.80, as well as low ductilebrittle transition temperature less than -80 and -70℃ for advanced aluminum hot-rolled TRIP steel and silicon hot-rolled TRIP steel respectively.

Key words: super fine ferrite grain, removable dislocation, retained austenite