IMPROVEMENT ON SUSCEPTIBILITY OF ULTAR-HIGH STRENGTH STEEL TO STRESS CORROSION CRACKING BY HIGH TEMPERATURE QUENCHING

Abstract

Abstract: The effect of quenching temperature on the stress corrosion cracking of 30Cr3SiNiMoV ultra-high strength steel in 3.5% NaCl aqueous solution has been studied.The threshold K_(ISCC) may continuously increase with the quenching temperature raised from 870 to 1200℃ . All of the fractures are intergranular.The analyses of the segregation along prior austenitic grain boundaries,grain size and other microstructural factors reveal that the inerease of K_(ISCC) is mainly due to the coarsening of prior austenitic grains.

Key words: ultra-high strength steel, stress corrosion cracking, grain boundary segregation

LI Guangfu WU Rengen Harbin Institute of Technology,Harbin,China LI Guangfu Division of Metallography,Harbin Institute of Technology,Harbin 150006,China. IMPROVEMENT ON SUSCEPTIBILITY OF ULTAR-HIGH STRENGTH STEEL TO STRESS CORROSION CRACKING BY HIGH TEMPERATURE QUENCHING[J]. Acta Metallurgica Sinica (English Letters), 1990, 3(3): 213-217.

[1]	Xiaoqing Liu, Xiaoguang Qiao, Xiaoye Qiu, Xianke Zhang, Chubin Yang, Dongdong Zhang, Xiurong Zhu, Mingyi Zheng. Role of Grain Boundary Segregation and Nanoprecipitation on the Tensile Properties and Thermal Stability of Dilute Mg-0.7Al-0.3Ca (wt%) Alloy [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(12): 2165-2178.
[2]	Yongfeng Zheng, Xiaofeng Hu, Haichang Jiang, Lijian Rong. New Insights into the Aging Embrittlement Mechanism of 30Cr2Ni4MoV Steel Containing Si and Mn [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(12): 2163-2169.
[3]	Wen Wang, Shan-Yong Chen, Ke Qiao, Pai Peng, Peng Han, Bing Wu, Chen-Xi Wang, Jia Wang, Yu-Hao Wang, Kuai-She Wang. Microstructure, Mechanical Properties, and Corrosion Behavior of Mg-Al-Ca Alloy Prepared by Friction Stir Processing [J]. Acta Metallurgica Sinica (English Letters), 2022, 35(5): 703-713.
[4]	F. Shi, L. Yan, J. Hu, L. F. Wang, T. Z. Li, W. Li, X. J. Guan, C. M. Liu, X. W. Li. Improving Intergranular Stress Corrosion Cracking Resistance in a Fe-18Cr-17Mn-2Mo-0.85N Austenitic Stainless Steel Through Grain Boundary Character Distribution Optimization [J]. Acta Metallurgica Sinica (English Letters), 2022, 35(11): 1849-1861.
[5]	Hongchi Ma, Baijie Zhao, Yi Fan, Kui Xiao, Jinbin Zhao, Xuequn Cheng, Xiaogang Li. Simultaneously Improving Mechanical Properties and Stress Corrosion Cracking Resistance of High-Strength Low-Alloy Steel via Finish Rolling within Non-recrystallization Temperature [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(4): 565-578.
[6]	Ji-Jin Xu, Shuai Wang, Ze Chai, Chun Yu, Jun-Mei Chen, Hao Lu. Comparison of the Stress Corrosion Cracking Behaviour of AISI 304 Pipes Welded by TIG and LBW [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(4): 579-589.
[7]	Zhixiong Zhu, Xingxu Jiang, Gang Wei, Xiaogang Fang, Zhihong Zhong, Kuijing Song, Jian Han, Zhengyi Jiang. Influence of Zn Content on Microstructures, Mechanical Properties and Stress Corrosion Behavior of AA5083 Aluminum Alloy [J]. Acta Metallurgica Sinica (English Letters), 2020, 33(10): 1369-1378.
[8]	Jin-Jin Zhao, Xian-Bin Liu, Shuai Hu, En-Hou Han. Effect of Cl^- Concentration on the SCC Behavior of 13Cr Stainless Steel in High-Pressure CO₂ Environment [J]. Acta Metallurgica Sinica (English Letters), 2019, 32(12): 1459-1469.
[9]	Hong-Liang Ming,Zhi-Ming Zhang,Peng-Yuan Xiu,Jian-Qiu Wang,En-Hou Han,Wei Ke,Ming-Xing Su. Microstructure, Residual Strain and Stress Corrosion Cracking Behavior in 316L Heat-Affected Zone [J]. Acta Metallurgica Sinica (English Letters), 2016, 29(9): 848-858.
[10]	Jian Chen, Jian-Qiu Wang, En-Hou Han, Wei Ke, D. W. Shoesmith. Effect of Hydrogen on Corrosion and Stress Corrosion Cracking of AZ91 Alloy in Aqueous Solutions [J]. Acta Metallurgica Sinica (English Letters), 2016, 29(1): 1-7.
[11]	Qiang Guo, Jian-Hua Liu, Mei Yu, Song-Mei Li. Influence of Rust Layers on the Corrosion Behavior of Ultra-High Strength Steel 300M Subjected to Wet-Dry cyclic Environment with Chloride and Low Humidity [J]. Acta Metallurgica Sinica (English Letters), 2015, 28(2): 139-146.
[12]	Changsheng Li, Biao Ma, Tao Li, Tao Zhu. Microstructure and Mechanical Properties of 1,000 MPa Ultra-High Strength Hot-Rolled Plate Steel for Coal Mine Refuge Chamber [J]. Acta Metallurgica Sinica (English Letters), 2014, 27(3): 422-429.
[13]	Zhiyong LIU, Cuiwei DU, Xin ZHANG, Fuming WANG,Xiaogang LI. Effect of pH Value on Stress Corrosion Cracking of X70 Pipeline Steel in Acidic Soil Environment [J]. Acta Metallurgica Sinica (English Letters), 2013, 26(4): 489-496.
[14]	J.X. Pan, K.Y. Kim. THE EFFECT OF W ON THE REPASSIVATION BEHAVIOR OF Ni-ADDED STAINLESS STEELS [J]. Acta Metallurgica Sinica (English Letters), 2005, 18(4): 489-496 .
[15]	S.Q. Li; J.I. Dickson and J.P. Bailon (Central Iron and Steel Research Institute (CISRI), Beijing 100081, China)(Ecole Polytecnique de Montreal, Montreal H3C 3A7, Canada). STUDY ON FRACTOGRAPHY OF TRANSGRANULAR SCC OF 70Cu-3OZn IN AN AMMONIACAL SOLUTION [J]. Acta Metallurgica Sinica (English Letters), 1998, 11(5): 347-357.

IMPROVEMENT ON SUSCEPTIBILITY OF ULTAR-HIGH STRENGTH STEEL TO STRESS CORROSION CRACKING BY HIGH TEMPERATURE QUENCHING

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments