MICROSTRUCTURE AND EXTENDED SOLID SOLUBILITY OF Tb IN RAPIDLY SOLIDIFIED Ag-Tb ALLOY

Abstract

Abstract: The 0,05—0.08 mm thick splat foils of Ag-Tb alloy,containing Tb up to 10 at.-%,were made by the hammer-anvil technique.The cooling rate was in order of 10~6 K/s.The metastable extension of solid solubility of Tb in the alloy was measured to be up to 5 at.-% by lattice parameter method.The secondary phase in metastable eutectic structure was identi- fied as Ag_3Tb from diffraction pattern.The microstructure and micro-defect in as-quenched Ag-Tb splat foil were also observed.

Key words: rapid solidification, Ag-Tb alloy, solid solubility

NING Yuantao ZHO U Xinming LI Yongnian Kunming Institute of Precious Metals,Kunming,China. MICROSTRUCTURE AND EXTENDED SOLID SOLUBILITY OF Tb IN RAPIDLY SOLIDIFIED Ag-Tb ALLOY[J]. Acta Metallurgica Sinica (English Letters), 1991, 4(8): 143-146.

[1]	Zhenyu Feng, Hong Zhong, Bin Yang, Xin Li, Shuangming Li. Improved Hydrogen Storage Properties of Ti₂₃V₄₀Mn₃₇ Alloy Doped with Zr₇Ni₁₀ by Rapid Solidification [J]. Acta Metallurgica Sinica (English Letters), 2023, 36(7): 1211-1219.
[2]	Fangsheng Mei, Tiechui Yuan, Ruidi Li, Jingwei Huang. A Comparative Study on the Microstructure and Properties of ITO Targets and Thin Films Prepared from Two Different Powders [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(5): 675-693.
[3]	Mohamad Ebrahimnia, Yujiang Xie, Changtai Chi. Effect of laser power and deposition environment on the microstructure and properties of direct laser metal-deposited 12CrNi2 steel [J]. Acta Metallurgica Sinica (English Letters), 2020, 33(4): 528-538.
[4]	Z. D. Fan, D. Wang, C. Liu, G. Zhang, J. Shen, L. H. Lou, J. Zhang. Low-Cycle Fatigue Properties of Nickel-Based Superalloys Processed by High-Gradient Directional Solidification [J]. Acta Metallurgica Sinica (English Letters), 2017, 30(9): 878-886.
[5]	Ren-Guo Guan, Di Tie. A Review on Grain Refinement of Aluminum Alloys: Progresses, Challenges and Prospects [J]. Acta Metallurgica Sinica (English Letters), 2017, 30(5): 409-432.
[6]	Hui-Jun Kang, Zhong-Lue Hu, Xiao-Xia Gao, Zong-Ning Chen, Yi-Ping Lu, Jin-Chuan Jie, Jing-Jie Guo. 3D Morphology and Formation Process of the Icosahedral Quasicrystalline Phase in Rapidly Solidified Al-Mn Alloy [J]. Acta Metallurgica Sinica (English Letters), 2016, 29(1): 28-31.
[7]	Jie Chen, Chong-Gao Bao, Yong Wang, Jin-Ling Liu, Challapalli Suryanarayana. Microstructure and Lattice Parameters of AlN Particle-Reinforced Magnesium Matrix Composites Fabricated by Powder Metallurgy [J]. Acta Metallurgica Sinica (English Letters), 2015, 28(11): 1354-1363.
[8]	Wenjing YAO, Xiuling NIU, Long ZHOU, Nan WANG, Jehyun LEE. Competition Growth of α and β Phases in Ti-50 at.%Al Peritectic Alloy during the Rapid Solidification by Laser Melting Technique [J]. Acta Metallurgica Sinica (English Letters), 2013, 26(5): 523-532.
[9]	Z.M. Zhang, C.J. Xu, X.F. Guo. Microstructre of Mg-6.4Zn-1.1Y Alloy Fabricatec by Rapid Solidification and Reciprocating Extrusion [J]. Acta Metallurgica Sinica (English Letters), 2008, 21(1): 30-36 .
[10]	Y.P. Lu. MICROSTRUCTURAL EVOLUTION OF HIGHLY UNDERCOOLED EUTECTIC Ni78.6Si21.4 ALLOY [J]. Acta Metallurgica Sinica (English Letters), 2006, 19(1): 43-50 .
[11]	Y.D.Xiao, W.X.Li, D.Jacovkis, M.T.Clavaguera-Mora, J.Rodriguez-Viejo, N.Clavaguera. STUDIES ON PRIMARY CRYSTALLIZATION OF RAPIDLY QUENCHED Al-Ni-Cu-Nd METALLIC GLASS BY USING HIGH RESOLUTION TRASMISSION ELECTRON MICROSCOPY [J]. Acta Metallurgica Sinica (English Letters), 2003, 16(5): 407-415 .
[12]	H. Pang, Z.H. Jin. NUCLEATION BEHAVIOR OF Al8Fe4Nd PHASE IN RAPIDLY SOLIDIFIED AI-Fe-V-Si-Nd ALLOY [J]. Acta Metallurgica Sinica (English Letters), 2002, 15(5): 453-459 .
[13]	N. Wang and B. Wei (Laboratory of Materials Science in Space, Northwestern Polytechnical University, Xi'an 710072, China)(Laboratory of Materials Science in Space, Northwestern Polytechnical University, Xi'an 710072, China). RAPID SOLIDIFICATION OF HYPEREUTECTIC SILVER-COPPER ALLOY IN DROP TUBE [J]. Acta Metallurgica Sinica (English Letters), 1999, 12(3): 251-258.
[14]	Liu; B.X. Kang; X.G. Cao; J.L. Huang; B. Yinand H.C. Gu (Institute of Materials Science and Engineering,Xi'an Jiaotong University, Xi'an 710049,China)(Institute of Materials Science and Engineering,Xi'an Jiaotong University, Xi'an 710049,China)( Department of Materials Engineering, Luoyang Institute of Technology, Luoyang 471049, China)( Department of Materials Engineering, Luoyang Institute of Technology, Luoyang 471049, China)( Department of Materials Engineering, Luoyang Institute of Technology, Luoyang 471049, China)( Department of Materials Engineering, Luoyang Institute of Technology, Luoyang 471049, China). INTERACTION OF PRECIPITATION AND RECRYSTALLIZATION IN RAPIDLY SOLIDIFIED Cu-Cr-Zr-Mg ALLOY [J]. Acta Metallurgica Sinica (English Letters), 1999, 12(3): 273-277.
[15]	Y.T.Ning (Institute of Precious Metals, Kunming 650221, China). METASTABLE PHASES IN RAPIDLY-SOLIDIFIED ALUMINIUMRICH Al-Sm ALLOYS [J]. Acta Metallurgica Sinica (English Letters), 1998, 11(4): 301-306.

MICROSTRUCTURE AND EXTENDED SOLID SOLUBILITY OF Tb IN RAPIDLY SOLIDIFIED Ag-Tb ALLOY

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments