Abstract: The effect of W on mechanical properties of 12% Cr-W-V-Nb heat resistant steel at high temperatures and room temperature is reported.The experimental results indicated that if the W content was about 2.2—3.0 wt-%,there was no obviously change of R.T.tensile strength, but impact toughness decreased with the rise of W content.On the other hand,the increase of W content enhanced the short time stress rupture strength,but did not for the long time one. The increase of W have two effects on the precipitation behavior,promoting Laves formation of type Fe_2W,increasing the precipitated phase amount and speeding up the coarsening pro- cess of precipitated phase at high temperatures.The effect of W on the mechanical properties is closely associated with precipitation behaviors.When the rupture life is short,there has no enough time to coarsen the precipitated phases,so the increase of precipitated phases results in strengthening effect,i.e.the W increases the high temperature strength.After prolonged expo- sure,the evident coarsening took plaee,that decreased the effect of precipitation.

Key words: 12%Cr-W-V-Nb steel, martensitic heat-resistant steel, Laves phase, precipitation behavior