ROUGHNESS-INDUCED SHEAR RESISTANCE OF MODE Ⅱ CRACK GROWTH

Abstract

Abstract: It is obtained in this paper that the fatigue threshold value of mode H was 1.9 times of that of mode Ⅰ in dual-phase steel(DPS),and the normal stress intensity factor range oJ mode Ⅱ branch crack tip was 2.2 times of that of mode Ⅰ.Above results illustrate that the resistance of mode Ⅱ crack growth was higher than that of mode Ⅰ,the former resulting from roughness-induced shear resistance,the latter,crack closure. The mode Ⅱ component can play two important roles in near-threshold fatigue crack growth:(1)increasing crack tip plasticity which accelerates the crack growth and(2)intro- ducing crack surface contact and rubbing to reduce the crack propagation rate.By means of crack closure,the quantity of shear resistance was easily solved in this paper.The friction shear stress strength factor range of mode Ⅱ,K_,is still much higher than the closure stress strength factor range of mode Ⅰ,K_(Ⅰ,cl).This illustrated that the roughness enlarged the second role and played a role of shielding crack tip from mode Ⅱ crack.

Key words: mixed-mode(Ⅰ/Ⅱ)fatigue crack growth threshold, crack closure, toughness, shear resistance, steel 16 Mn

ZHENG Yesha WANG Zhongguang AI Suhua State Key Laboratory of Fatigue and Fracture for Materials,Institute of Metal Research,Academia Sinica,Shenyang,China postdoctor,Shanghai Institute of Ceramics,Academia Sinica,Shanghai 200050,China. ROUGHNESS-INDUCED SHEAR RESISTANCE OF MODE Ⅱ CRACK GROWTH[J]. Acta Metallurgica Sinica (English Letters), 1993, 6(6): 397-404.

[1]	Hong Chen, Ruitao Qu, Haotian Ma, Kexing Song, Feng Liu. Simultaneously Enhanced Strength and Fracture Resistance in HfNbTaTiZr Refractory High-Entropy Alloy at Higher Strain Rate [J]. Acta Metallurgica Sinica (English Letters), 2025, 38(4): 529-541.
[2]	Chao Xia, Kexin Zhao, Xin Zhou, Yuqi He, Panpan Gao, Hengxin Zhang, Guangrui Gao, Fengying Zhang, Hua Tan. Effect of Microstructural Characteristics on Fracture Toughness in Direct Energy Deposited Novel Ti-6Al-4V-1Mo Alloy [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(1): 119-131.
[3]	Xueli Wang, Xin Ji, Bin He, Dongpo Wang, Chengning Li, Yongchang Liu, Wei Guan, Lei Cui. Prediction of M-A Constituents and Impact Toughness in Stir Zone of X80 Pipeline Steel Friction Stir Welds [J]. Acta Metallurgica Sinica (English Letters), 2023, 36(4): 573-585.
[4]	Bing Wang, Hong-Lin Zhang, Bin Xu, Hai-Yang Jiang, Ming-Yue Sun, Dian-Zhong Li. Sensitivity of the Impact Toughness and Microstructure of 15CrNi3MoV Steel Under Different Quenching Rates [J]. Acta Metallurgica Sinica (English Letters), 2023, 36(10): 1735-1748.
[5]	Wen-Ting Zhu, Jun-Jun Cui, Zhen-Ye Chen, Yang Zhao, Li-Qing Chen. Correlation of Microstructure Feature with Impact Fracture Behavior in a TMCP Processed High Strength Low Alloy Construction Steel [J]. Acta Metallurgica Sinica (English Letters), 2022, 35(4): 527-536.
[6]	Xin-Tong Lian, Long Chen, Zeng-Wei Fan, Teng-Shi Liu, De-Xiang Xu, Han Dong. Effects of Modified Inclusions and Precipitates Alloyed by Rare Earth Element on Corrosion and Impact Properties in Low Alloy Steel [J]. Acta Metallurgica Sinica (English Letters), 2022, 35(10): 1719-1730.
[7]	Yi-Shuang Yu, Zhi-Quan Wang, Bin-Bin Wu, Jing-Xiao Zhao, Xue-Lin Wang, Hui Guo, Cheng-Jia Shang. Tailoring Variant Pairing to Enhance Impact Toughness in High-Strength Low-Alloy Steels via Trace Carbon Addition [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(6): 755-764.
[8]	Ling-Yang Yuan, Pan-Wen Han, Ghulam Asghar, Bao-Liang Liu, Jin-Ping Li, Bin Hu, Peng-Huai Fu, Li-Ming Peng. Development of High Strength and Toughness Non-Heated Al-Mg-Si Alloys for High-Pressure Die-Casting [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(6): 845-860.
[9]	Xiaohui Xi, Jinliang Wang, Liqing Chen, Zhaodong Wang. On the Microstructural Strengthening and Toughening of Heat-Affected Zone in a Low-Carbon High-Strength Cu-Bearing Steel [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(5): 617-627.
[10]	He Duan, Yi-Yin Shan, Ke Yang, Xian-Bo Shi, Wei Yan, Yi Ren. Effect of Rare Earth and Cooling Process on Microstructure and Mechanical Properties of an Ultra-Cleaned X80 Pipeline Steel [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(5): 639-648.
[11]	Hua-Ping Tang, Qu-Dong Wang, Colin Luo, Chuan Lei, Tian-Wen Liu, Zhong-Yang Li, Kui Wang, Hai-Yan Jiang, Wen-Jiang Ding. Effects of Solution Treatment on the Microstructure, Tensile Properties, and Impact Toughness of an Al-5.0Mg-3.0Zn-1.0Cu Cast Alloy [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(1): 98-110.
[12]	Yongkui Li, Jianxin Lou, Hongtao Ju, Li Lin. Impact Toughness of Heat-Affected Zones of 11Cr Heat-Resistant Steels [J]. Acta Metallurgica Sinica (English Letters), 2020, 33(6): 821-827.
[13]	Jian Han, Zhixiong Zhu, Gang Wei, Xingxu Jiang, Qian Wang, Yangchuan Cai, Zhengyi Jiang. Microstructure and Mechanical Properties of Nb- and Nb + Ti-Stabilised 18Cr-2Mo Ferritic Stainless Steels [J]. Acta Metallurgica Sinica (English Letters), 2020, 33(5): 716-730.
[14]	Xian-Kai Fan, Fu-Quan Li, Lei Liu, Hai-Chao Cui, Feng-Gui Lu, Xin-Hua Tang. Evolution of γ′ Particles in Ni-Based Superalloy Weld Joint and Its Effect on Impact Toughness During Long-Term Thermal Exposure [J]. Acta Metallurgica Sinica (English Letters), 2020, 33(4): 561-572.
[15]	Wen-Chao Dong, Ming-Yue Wen, Hui-Yong Pang, Shan-Ping Lu. Effect of Post-weld Tempering on the Microstructure and Mechanical Properties in the Simulated HAZs of a High-Strength-High-Toughness Combination Marine Engineering Steel [J]. Acta Metallurgica Sinica (English Letters), 2020, 33(3): 391-402.

ROUGHNESS-INDUCED SHEAR RESISTANCE OF MODE Ⅱ CRACK GROWTH

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments