NEWLY-DEVELOPED AND CHEAP NANOCRYSTALLINE Fe-Cu-Nb-Mo-Si-B ALLOYS FOR SWITCHING MODE POWER SUPPLY

Acta Metallurgica Sinica (English Letters) ›› 1997, Vol. 10 ›› Issue (6): 489-494.

• Research paper • Previous Articles Next Articles

NEWLY-DEVELOPED AND CHEAP NANOCRYSTALLINE Fe-Cu-Nb-Mo-Si-B ALLOYS FOR SWITCHING MODE POWER SUPPLY

Y.Z. Zhang(Shanghai Iron and Steel Research Institute, Shanghai 200940, China)

Received:1997-12-25 Revised:1997-12-25 Online:1997-12-25 Published:2009-10-10

Abstract

Abstract: The synthetical soft magnetic properties are reported for newly-developed nanocrystalline Fe73.5 Cu1 Nb0.9Mo2.1 Si13.5 B9 and Fe73.5 Cu1 Nb0.5Mo2.5Si13.5B9 alloys. The levels of high-frequency losses of the new alloys are P3/100k=612 and 670 kWm-3,P2/200k=880 and 973 kWm-3, P2/500k=4300 and 4600 kWm-3, P0.5/1000k=860 and 920 kWm-3, respectively. They are significantly lower than those of the superior power Mn-Zn ferrite H7c.4.The dependences of core loss on frequency and amplitude flux density have been analysed. The practical applications of the new alloys to switching mode power supplies with the output power of 1 and 2 kW are reported.

Key words: nanocrystalline alloy, relative effective permeability, highfrequency core loss, switching mode power supply

Y.Z. Zhang(Shanghai Iron and Steel Research Institute, Shanghai 200940, China). NEWLY-DEVELOPED AND CHEAP NANOCRYSTALLINE Fe-Cu-Nb-Mo-Si-B ALLOYS FOR SWITCHING MODE POWER SUPPLY[J]. Acta Metallurgica Sinica (English Letters), 1997, 10(6): 489-494.

[1]	Shushen Guo, Yanhui Li, Yibing Zhang, Lu Yang, Wei Zhang. Reduction of High-Frequency Core Loss of a Fe_77.2Si₁₁B_8.5Cu_0.8Nb_2.5 Soft Magnetic Nanocrystalline Alloy by Minor Alloying [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(11): 1984-1992.
[2]	Li-Cheng Wu, Yan-Hui Li, Xing-Jie Jia, Ai-Na He, Wei Zhang. Effects of Ribbon Thickness on Structure and Soft Magnetic Properties of a High-Cu-Content FeBCuNb Nanocrystalline Alloy [J]. Acta Metallurgica Sinica (English Letters), 2022, 35(2): 235-242.
[3]	Chongfeng Sun, Shengqi Xi, Xiaofeng Dang, Jianping Li, Yongchun Guo, Zhong Yang, Yaping Bai. Formation of Fe-19 wt%Cr-9 wt%Ni Nanocrystalline Alloy with Excellent Corrosion Resistance: Phase Transition and Microstructure [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(6): 825-833.
[4]	Yao-Xiang Geng, Hong-Yu Ding, Dong-Peng Wang, Zhi-Jie Zhang, Hong-Bo Ju, Li-Hua Yu, Jun-Hua Xu. Formation and Structural Evolution of Fe_72.5B_15.6Si_7.8Nb_1.7Zr_1.7Cu_0.7 Nanocrystalline Alloy [J]. Acta Metallurgica Sinica (English Letters), 2020, 33(2): 313-318.
[5]	Y.J. Zhang, X.H. Li, S. Wang, K.Y. He. Temperature Dependence of Permeability of Co66Fe4Mo2Si16B12 Alloy [J]. Acta Metallurgica Sinica (English Letters), 2007, 20(4): 284-286 .
[6]	Y.J.Zhang. TEMPERATURE DEPENDENCE OF EFFECTIVE MAGNETIC ANISOTROPY OF Fe-Nb-B ALLOY [J]. Acta Metallurgica Sinica (English Letters), 2001, 14(4): 267-270 .
[7]	TONG Huayu,DING Bingzhe,JIANG Honggang,LI Shuling,LI Gusong,WANG Jingtang State Key Laboratory of RSA,Institute of Metal Research.Academia Sinica.Shenyang,China. THERMAL PROPERTIES OF NANOCRYSTALLINE Fe_78B_13Si_9 ALLOY [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(12): 496-501.

NEWLY-DEVELOPED AND CHEAP NANOCRYSTALLINE Fe-Cu-Nb-Mo-Si-B ALLOYS FOR SWITCHING MODE POWER SUPPLY

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 7

Recommended Articles

Metrics

Comments